Heat-dissipating composition and lubricating plate
A composition and dispersion technology, applied in the directions of lubricating compositions, heat exchange materials, synthetic resin layered products, etc., can solve the problems of poor machining accuracy, difficult cutting and removal, and tool wear and tear, and achieve increased flatness. The effect of uniformity, improved precision, and good mechanical strength
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
no. 1 approach
[0051] First Embodiment: Preparation Method of Waterborne Polyurethane Resin
[0052] First, put diisocyanate, polyester diol, polyether diol (containing ethoxylated diol) and 2,2 - Dimethylolpropionic acid (GEOSecialitychemicals, IncDMPA), to carry out a synthesis reaction to obtain a prepolymer, the reaction time is 1.0 hours to 5.0 hours, in which 2,2-dimethylolpropionic acid is used as an anionic group source, containing Ethoxylated glycols are used as a source of nonionic groups. During the synthesis reaction, an organic solvent is added to the reactants to reduce the viscosity of the reactants.
[0053] It should be noted that the diisocyanate used in the above synthesis reaction is selected from 2,4- / 2,6-toluene diisocyanate (TDI, toluenediisocyanate) (BayerDesmodurTDI), 4,4'-diphenylmethane diisocyanate Isocyanate (MDI, methylenediphenyldiisocyanate) (BayerDesmodurMDI), isophorone diisocyanate (IPDI, isophoronediisocyanate) (BayerDesmodurIPDI), 4,4'-dicyclohexylmetha...
no. 2 approach
[0065] Second Embodiment: Preparation Method of Waterborne-Silicone Polyurethane Resin
[0066] Under oil bath heating conditions (50~100°C), add appropriate proportions of diisocyanate, polyester diol, polyether diol and 2,2-dimethyl alcohol propionic acid into the reaction bottle to synthesize Reaction, the reaction time is 1.0 hours to 5.0 hours. It should be understood that the types and selection conditions of the diisocyanate, polyester diol, polyether diol and organic solvent in this embodiment are the same as those in the first embodiment.
[0067] Next, an organic solvent is added to the above-mentioned reactant to reduce the viscosity of the reactant, and a polysiloxane copolymer is added to participate in the synthesis reaction, and a prepolymer is obtained after 0.5 hours to 4.0 hours. In this embodiment, the polymer The siloxane copolymer is polydimethylsiloxane copolymer or polydimethylsiloxane diamine (its general formula is R-(Si(CH 3 ) 2 -O) n -R, R=OH or ...
no. 3 approach
[0071] Third Embodiment: Preparation Method of Water-Based Silicone / Fluorinated Polyurethane Resin
[0072] Under oil bath heating conditions (50~100°C), add appropriate proportions of diisocyanate, polyester diol, polyether diol and 2,2-dimethyl alcohol propionic acid into the reaction bottle to synthesize Reaction, the reaction time is 1.0 hours to 5.0 hours. It should be understood that the types and selection conditions of the diisocyanate, polyester diol, polyether diol and organic solvent in this embodiment are the same as those in the first embodiment.
[0073] Then, an organic solvent is added to the above-mentioned reactant to reduce the viscosity of the reactant, and polysiloxane copolymer and polytetrafluorocarbon glycol (its general formula is HO-(CF 2 CF 2 ) n -OH, molecular weight 500-3000) (Shin-Etsu Chemical polytetrafluorocarbon diol) participates in the synthesis reaction, and the prepolymer is obtained after 0.5 hours to 4.0 hours. It should be understoo...
PUM
![No PUM](https://static-eureka.patsnap.com/ssr/23.2.0/_nuxt/noPUMSmall.5c5f49c7.png)
Abstract
Description
Claims
Application Information
![application no application](https://static-eureka.patsnap.com/ssr/23.2.0/_nuxt/application.06fe782c.png)
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap