a chiller

A technology of chilling agent and uniform mixing, applied in the field of chilling agent, can solve problems such as difficulty in finding eutectic temperature

Active Publication Date: 2015-09-30
南京钢铁集团盛达实业有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] During the solidification process of gray cast iron, it is difficult to find the exact eutectic temperature due to the influence of the inoculation status of the molten iron and the crystallization conditions.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • a chiller

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] Embodiment 1, the chiller includes the following components, by weight percentage, tellurium 45%, aluminum 20%, titanium 10%, iron 25%, and the above-mentioned components are made into particles of 0.5-1.5 mm and then uniformly mixed to form the chiller. refrigerant.

Embodiment 2

[0011] Embodiment 2, the chiller includes the following components, by weight percentage, tellurium 55%, aluminum 30%, titanium 10%, iron 5%, and the above-mentioned components are made into particles of 0.5-1.5 mm and then uniformly mixed to form the chiller. refrigerant.

Embodiment 3

[0012] Embodiment 3, the chiller includes the following components, by weight percentage, tellurium 50%, aluminum 30%, titanium 10%, iron 10%, the above-mentioned components are made into particles of 0.5-1.5 mm and then uniformly mixed to form the chiller. refrigerant.

[0013] Spread the chiller evenly on the bottom of the thermal analysis sample cup to measure the addition of molten iron in the thermal analysis sample cup.

[0014] Such as figure 1 As shown, after using the chiller provided in Example 3 to detect both sides of the molten iron with different components, the CE, C, Si value data and their comparison with the results of the chemical analysis of the same molten iron can be seen The accuracy of the measurement results after the invention is used is high, and the measurement stability is good.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a chilling agent which comprises the following components in percentage by weight: 45-55% of tellurium, 20-30% of aluminum, 10% of titanium and the balance of iron. After being prepared into 0.5-1.5mm particles, all the above components are uniformly mixed to form the chilling agent. The chilling agent provided by the invention can promote hypo-eutectic or hypereutectic molten iron which is inoculated or not inoculated to be solidified according to white cast, so as to display a long eutectic stopping platform on a cooling curve, and thus accurate CEL, C and Si values can be obtained.

Description

technical field [0001] The present invention relates to a chiller. Background technique [0002] Cast iron is an iron-carbon alloy with eutectic transformation. When the molten iron is poured into the thermal analysis sample cup, the molten iron with a certain composition undergoes a phase change during cooling and solidification, releasing the latent heat of crystallization, and the cooling curve changes. The eigenvalues ​​conform to certain rules, so the carbon equivalent, carbon content and silicon content of cast iron can be determined according to the eigenvalues ​​on the cooling curve. The thermal analysis sample cup uses this thermal effect to analyze the CEL, C, Si and related characteristics of cast iron by measuring the primary crystal temperature and eutectic temperature point of the cooling curve during the solidification process. [0003] During the solidification process of gray cast iron, it is difficult to find the accurate eutectic temperature due to the in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C33/08C21C1/08
Inventor 吴万奋
Owner 南京钢铁集团盛达实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com