Alkaline-free anti-crack concrete shrinkage reducing agent

A concrete shrinkage reducing agent and the technology of shrinkage reducing agent are applied in the field of alkali-free anti-cracking concrete shrinkage reducing agent, which can solve the problem of less consideration of the anti-cracking effect of concrete, and achieve easy control of production conditions, improvement of workability, and improvement of crack resistance and impermeability. Effect

Inactive Publication Date: 2015-06-17
HUNAN CONSTR ENG GRP COR +1
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These shrinkage reducing agents rarely consider the anti-cracking effect on concrete

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] The content of each component of the alkali-free anti-crack concrete shrinkage reducer is: Class I fly ash: 5.5kg, polypropylene short fiber: 1.5kg, polyethylene glycol: 0.9kg, methacrylic acid: 0.7kg, calcium formate: 0.68kg, neopentyl glycol: 0.64kg, sodium dodecylbenzenesulfonate: 0.08kg.

Embodiment 2

[0039] The content of each component of the alkali-free anti-cracking concrete shrinkage reducer is: Class I fly ash: 4.5kg, polypropylene short fiber: 1.5kg, polyethylene glycol: 1.4kg, methacrylic acid: 1.2kg, calcium formate: 0.28kg, neopentyl glycol: 1.04kg, sodium dodecylbenzenesulfonate: 0.08kg.

Embodiment 3

[0041] The content of each component of the non-alkali anti-cracking concrete shrinkage reducer is: Class I fly ash: 6.5kg, polypropylene short fiber: 1.0kg, polyethylene glycol: 0.7kg, methacrylic acid: 0.7kg, calcium formate: 0.48kg, neopentyl glycol: 0.54kg, sodium dodecylbenzenesulfonate: 0.08kg.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses an alkaline-free anti-crack concrete shrinkage reducing agent comprising the following components in percentage by weight: 35-66% of I-grade coal ash, 8-18% of polypropylene staple fiber, 2-18% of polyethylene glycol, 3-17% of methacrylic acid, 2-15% of calcium formate, 3-16% of neopentyl glycol and 0.2-0.8% of sodium dodecyl benzene sulfonate. The invention provides possibility for realizing the comprehensive improvement of an additive technology, reducing concrete shrinkage, inhibiting non-loaded cracks and improving the durability of concrete through the research on and application as a shrinkage reducing additive and creates the environment-friendly alkaline-free anti-crack concrete shrinkage reducing agent. The technology is simple in feeding way, easily-controlled in production condition, simple in process and capable of producing the alkaline-free anti-crack concrete shrinkage reducing agent which is low in alkaline content and mixing amount and capable of effectively controlling the shrinkage of concrete. The alkaline-free anti-crack concrete shrinkage reducing agent has a relatively good social benefit and a relatively high economic benefit.

Description

technical field [0001] The invention relates to an alkali-free anti-crack concrete shrinkage reducer. Background technique [0002] Concrete is the most widely used building material in contemporary construction projects. Concrete engineering technology is always advancing along with the needs of engineering construction and the development of science and technology. It has been widely used in industrial and civil construction, water conservancy, urban construction, agriculture and forestry, transportation and seaport and other projects. At the same time, many new problems will appear in the application process of concrete, especially in recent years, the durability degradation of concrete. Accidents of structural damage due to insufficient durability occur frequently, and the resulting economic losses are also incalculable. The biggest disadvantage of concrete is that it is prone to cracks. Cracks in concrete are not only an accident of engineering quality, but their...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B24/16C04B24/02
Inventor 肖燎刘玉辉谭丁黄涛杨玉宝李再德黄伟金泽乾
Owner HUNAN CONSTR ENG GRP COR
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com