Colored photosensitive composition, black photo spacer, and color filter

A photosensitive composition and photopolymerization technology, applied in optical filters, photosensitive materials for optomechanical equipment, optics, etc., can solve problems such as damage characteristics, curability of spacer layers, etc., to ensure light Effects of absorbing and maintaining voltage retention and high adhesion

Active Publication Date: 2014-10-01
MITSUBISHI RAYON CO LTD
View PDF36 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, in order to make the spacer light-shielding, it is generally considered to add a colorant containing a pigment to the photosensitive composition, but with the addition of the colorant, the curability of the spacer layer decreases due to the decrease of the transparent component. Small, and the characteristics may be damaged by the influence of impurities derived from pigments, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Colored photosensitive composition, black photo spacer, and color filter
  • Colored photosensitive composition, black photo spacer, and color filter
  • Colored photosensitive composition, black photo spacer, and color filter

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0387] [Manufacturing method of colored photosensitive composition]

[0388] The colored photosensitive composition of the present invention is prepared according to a conventional method. Hereinafter, although an example is given and it demonstrates concretely, the manufacturing method of the coloring photosensitive composition in this invention is not limited to this method.

[0389] From the viewpoint of ensuring the dispersion stability of the pigment, the coloring photosensitive composition of the present invention is preferably prepared in the following manner to prepare a pigment dispersion liquid in advance and to mix other components therein.

[0390] [1] Manufacturing method of pigment dispersion liquid

[0391] Predetermined amounts of the pigment, solvent, and dispersant, and, if necessary, a dispersion aid are weighed, and in the dispersion treatment step, the pigment is dispersed to obtain a liquid pigment dispersion. In this dispersion treatment step, a paint ...

Embodiment

[0432] Hereinafter, although an Example and a comparative example are given and this embodiment is demonstrated more concretely, this embodiment is not limited to the following example unless the summary is exceeded. In addition, below, "part" means a "weight part."

[0433] The constituent components of the colored photosensitive composition used in the following examples and comparative examples are as follows.

[0434]

[0435]"ZCR-1569H" manufactured by Nippon Kayaku Co., Ltd. (MW = 3000 to 4000, acid value = about 100 mg-KOH / g)

[0436] In addition, this binder resin-1 corresponds to "alkali-soluble resin (A)" in this invention.

[0437]

[0438] "ZCR-1642H" manufactured by Nippon Kayaku Co., Ltd. (MW = 5000 to 6500, acid value = about 100 mg-KOH / g)

[0439] In addition, this binder resin-2 corresponds to "alkali-soluble resin (A)" in this invention.

[0440]

[0441] Resin (MW=3500-4500, acid value = about 110 mg-KOH / g)

[0442] [chemical formula 21]

[0443]...

Synthetic example 1

[0445]

[0446] Add 50g of epoxy compound (epoxy equivalent 264) of above structure (11), 13.65g of acrylic acid, 60.5g of methoxybutyl acetate, 0.936g of triphenylphosphine and 0.032g of p-methoxyphenol into a thermometer equipped with , a stirrer, and a flask with a cooling tube, the reaction was carried out at 90° C. while stirring until the acid value became 5 mgKOH / g or less. The reaction required 12 hours, and an epoxy acrylate solution was obtained.

[0447] 25 parts by weight of the above-mentioned epoxy acrylate solution and 0.74 parts by weight of trimethylolpropane (TMP), 3.95 parts by weight of biphenyltetracarboxylic dianhydride (BPDA), 2.7 parts by weight of tetrahydrophthalic anhydride (THPA) It was added to the flask equipped with the thermometer, the stirrer, and the cooling tube, and it heated up slowly to 105 degreeC, stirring, and it was made to react.

[0448] When the resin solution became transparent, it was diluted with methoxybutyl acetate, and it p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
diameteraaaaaaaaaa
transmittivityaaaaaaaaaa
Login to view more

Abstract

A colored photosensitive composition containing a pigment, a binder resin, a photopolymerizable monomer, and a photopolymerization initiator, wherein the pigment contains the following: (A) one pigment selected from the group consisting of C.I. pigment orange 43, C.I. pigment orange 64, and C.I. pigment orange 72; and (B) C.I. pigment blue 60.

Description

technical field [0001] The present invention relates to a colored photosensitive composition and the like. Specifically, it relates to a colored photosensitive composition preferably used for forming a black photo-spacer in a color filter such as a liquid crystal display, and a black photo-spacer and a black photo-spacer formed using the colored photosensitive composition. Color filter containing this black photo-spacer. Background technique [0002] A liquid crystal display (LCD) utilizes the property of switching an alignment method of liquid crystal molecules by on / off of a voltage applied to the liquid crystal. On the other hand, each member constituting a cell of an LCD is often formed using a photosensitive composition typified by photolithography. The application range of the photosensitive composition also tends to be further expanded in the future because it is easy to form a fine structure and easy to handle a substrate for a large screen. [0003] However, in a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): G03F7/004C08F2/44C08F2/50G02B5/20G02B5/22
CPCG03F7/0007C08F2/50G02B5/223G03F7/105C09B67/0033
Inventor 岩田训志泽井良尚裴丽华
Owner MITSUBISHI RAYON CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap