Composition with multiple oral treatment and healthcare functions and preparation method thereof

A technology for oral treatment and health care, applied in the application field of oral treatment and health care, to achieve the effects of repairing tooth defects, eliminating dentin hypersensitivity, and inhibiting periodontal disease

Active Publication Date: 2014-11-05
BEIJING DATSING BIO TECH
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this invention can only inhibit the growth of bacteria in the oral cavity, and has no

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composition with multiple oral treatment and healthcare functions and preparation method thereof
  • Composition with multiple oral treatment and healthcare functions and preparation method thereof
  • Composition with multiple oral treatment and healthcare functions and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] Embodiment 1: Preparation has the composition of multiple oral cavity treatment and health care effect

[0052] 1. Weigh each material according to the following formula:

[0053]

[0054] The quasi-nano-scale bioactive mineral powder contains the following components by weight percentage: SiO 2 45%, CaO24.5%, Na 2 O24.5%, P 2 o 5 6%; among them, the quasi-nanometer powder with a particle size within the range of 100-900nm accounts for 7% of the total powder weight.

[0055] 2. Preparation method:

[0056] 1) Set the vacuum degree to -70kPa, emulsify and stir at a high speed, the stirring speed is 500 rpm, and the wall scraping stirring speed is 20 rpm, add humectants, protective agents, adhesives, spices according to the formula, and stir for 60 minutes ;

[0057] 2) Break the vacuum and stand until the mixture is a uniform solid-liquid mixed phase, and the standing time is 25 hours to obtain the mixture;

[0058] 3) Set the vacuum degree to -70kPa, emulsify ...

Embodiment 2

[0060] Embodiment 2: Preparation has the composition of multiple oral cavity treatment and health care effect

[0061] 1. Weigh each material according to the following formula:

[0062]

[0063] The quasi-nano-scale bioactive mineral powder contains the following components by weight percentage: SiO 2 45%, CaO24.5%, Na 2 O24.5%, P 2 o 5 6%; among them, the quasi-nanometer powder with a particle diameter within the range of 100-900nm accounts for 5% of the total powder weight.

[0064] 2. Preparation method:

[0065] 1) Set the vacuum degree to -80kPa, emulsify and stir at a high speed, the stirring speed is 1200 rpm, and the wall scraping stirring speed is 30 rpm, add humectants, protective agents, adhesives, spices according to the formula, and stir for 35 minutes ;

[0066] 2) Break the vacuum and stand until the mixture is a uniform solid-liquid mixed phase, and the standing time is 25 hours to obtain the mixture;

[0067] 3) Set the vacuum degree to -80kPa, high...

Embodiment 3

[0069] Embodiment 3: preparation has the composition of multiple oral cavity treatment and health care effect

[0070] 1. Weigh each material according to the following formula:

[0071]

[0072] The quasi-nano-scale bioactive mineral powder contains the following components by weight percentage: SiO 2 45%, CaO24.5%, Na 2 O24.5%, P 2 o 5 6%; among them, the quasi-nanometer powder with a particle size within the range of 100-900nm accounts for 20% of the total powder weight.

[0073] 2. Preparation method:

[0074] 1) Set the vacuum degree to -80kPa, emulsify and stir at a high speed, the stirring speed is 1000 rpm, and the wall scraping stirring speed is 40 rpm, add humectants, protective agents, adhesives, spices according to the formula, and stir for 50 minutes ;

[0075] 2) Break the vacuum and stand until the mixture is a uniform solid-liquid mixed phase, and the standing time is 10 hours to obtain the mixture;

[0076] 3) Set the vacuum degree to -80kPa, emulsif...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to a composition with multiple oral treatment and healthcare functions. The composition comprises the following ingredients: a quasi-nanoscale bioactive mineral powder, a protective agent, an adhesive, a moisturizer and other components. The invention relates to a preparation method of the composition. The preparation method comprises the following steps: adding the protective agent, the moisturizer and an emulsifier according to the above formula under vacuum and high-speed emulsification stirring conditions; stirring for 50-60 min; standing to obtain a mixture; adding the quasi-nanoscale bioactive mineral powder and other components according to the formula into the above mixture under vacuum and high-speed emulsification stirring conditions; stirring for 5-60 min; and standing for 5-30 min so as to obtain the composition. The invention also relates to an application of the composition in the preparation of medicines or dental products for preventing and curing hemodia, periodontal disease, dental ulcer and plaque-induced dental caries.

Description

technical field [0001] The invention relates to the field of oral cavity treatment and health care, in particular to a composition with multiple oral cavity treatment and health care functions and a preparation method thereof, and also relates to the application of the composition in oral cavity treatment and health care. Background technique [0002] Dental hypersensitivity is a common and frequently-occurring disease in clinical oral cavity. The global incidence rate is about 40%, and the domestic incidence rate reaches 30%, while the incidence rate among periodontal disease patients is as high as about 98%. There are various causes of tooth hypersensitivity, such as wedge-shaped defect, periodontal atrophy, root exposure, dental trauma, severe wear, etc., or iatrogenic tooth preparation, cavity preparation, scaling, scraping, etc. dentin exposure due to tooth discoloration, etc. However, the basic pathogenesis has formed a unified theory in the industry - "hydrodynamic t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A61K33/42A61K8/73A61K8/25A61K8/24A61P1/02A61P31/04A61Q11/00A61K33/24A61K33/08A61K33/00A61K31/722A61K31/728
CPCA61K8/19A61K8/25A61K8/34A61K8/73A61K33/00A61K33/42A61Q11/00
Inventor 翟晖李伟峰李次会李湘杰张国强石道林
Owner BEIJING DATSING BIO TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap