Universal shoe material treatment agent and preparation method thereof

A technology for treating agents and shoe materials, applied in the direction of adhesives, adhesive additives, non-polymer adhesive additives, etc., can solve the problems of increasing financial resources, occupying reserve space, etc., and achieving cost saving, strong penetration, and resource reduction. Effect

Active Publication Date: 2016-01-20
GUANGSHAN BOZHENG RESIN
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Greatly increased the financial resources, material resources and manpower of the merchants, and took up a lot of storage space at the same time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Embodiment 1: a kind of universal shoe material treatment agent, this treatment agent is made by mixing the raw materials of following weight ratio: dimethyl carbonate 2400g, ethyl acetate 90g, nylon 500g, neoprene 181g, styrene-isoprene 200g of ethylene-styrene block copolymer, 400g of hydrolyzed polymaleic anhydride, 3g of hydroquinone, 5g of benzoyl peroxide initiator, 2g of 2,6 di-tert-butyl p-cresol stabilizer, 390g of butanone, Cyclohexanone 450g, dimethylformamide 160g.

[0013] The universal shoe material treatment agent in the above-mentioned Example 1 is prepared according to the following method: First, add 500 g of dimethyl carbonate and 90 g of ethyl acetate to the reaction kettle, set the temperature at 95° C. to remove moisture, and add 500 g of nylon after 1 hour , Neoprene 181g and styrene-isoprene-styrene block copolymer 200g, set the temperature at 95°C, and disperse and dissolve within 1.5 hours (styrene-isoprene-styrene block copolymer temperature ...

Embodiment 2

[0014] Embodiment 2: a kind of universal shoe material treatment agent, this treatment agent is made by mixing the raw materials of following weight ratio: dimethyl carbonate 2600g, ethyl acetate 120g, nylon 400g, styrene-isoprene-styrene embedded Segment copolymer 300g, neoprene 220g, hydrolyzed polymaleic anhydride 600g, hydroquinone 10g, benzoyl peroxide initiator 2g, 2,6 di-tert-butyl p-cresol stabilizer 3g, butanone 350g, Cyclohexanone 550g, dimethylformamide 100g.

[0015] The universal shoe material treatment agent in the above example 2 is prepared according to the following method: First, add 500 g of dimethyl carbonate and 120 g of ethyl acetate to the reaction kettle, set the temperature at 100° C. to remove moisture, and add 400 g of nylon after 1.5 hours , 220g of neoprene and 300g of styrene-isoprene-styrene block copolymer, set the temperature at 100°C, and carry out dispersion and mutual dissolution within 2 hours, after mutual dissolution, cool down to 80°C fo...

Embodiment 3

[0016] Embodiment 3: a kind of universal shoe material treating agent, this treating agent is made by mixing the raw materials of following weight ratio: dimethyl carbonate 2500g, ethyl acetate 100g, nylon 450g, neoprene 200g, styrene-isoprene 250g of ethylene-styrene block copolymer, 500g of hydrolyzed polymaleic anhydride, 5g of hydroquinone, 3g of benzoyl peroxide initiator, 2g of 2,6 di-tert-butyl p-cresol stabilizer, 400g of butanone, Cyclohexanone 500g, dimethylformamide 140g. Raw materials in this embodiment: the nylon model is preferably No. 6, and the neoprene model is preferably A-90.

[0017] The universal shoe material treatment agent in the above-mentioned Example 3 is prepared according to the following method: First, add 500 g of dimethyl carbonate and 100 g of ethyl acetate to the reaction kettle, set the temperature at 95° C. to remove moisture, and add 650 g of nylon after 1 hour , Neoprene 200g and styrene-isoprene-styrene block copolymer 250g, set temperat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an all-purpose shoe material treating agent and a preparation method of the all-purpose shoe material treating agent. The all-purpose shoe material treating agent comprises, by weight, 2400 to 2600 grams of dimethyl carbonate, 80 to 120 grams of ethyl acetate, 400 to 500 grams of nylon, 180 to 220 grams of chloroprene rubber adhesive, 200 to 300 grams of styrene-isoprene-styrene segmented copolymer, 400 to 600 grams of hydrolytic polymaleic anhydride, three to ten grams of hydroquinone, two to five grams of benzoyl peroxide initiator, one to three grams of 2,6-butylated hydroxytoluene stabilizer, 350 to 450 grams of butanone, 450 to 550 grams of cyclohexanone and 100 to 160 grams of dimethyl formamide. The all-purpose shoe material treating agent can replace tens of treating agents. The all-purpose shoe material treating agent is formed through diversification graft polymerization and then is discomposed and diluted to be mixed with a strong solvent for synthesis. The all-purpose shoe material treating agent is high in seepage force, rapid in crystallization and super powerful. By the adoption of the all-purpose shoe material treating agent and the preparation method of the all-purpose shoe material treating agent, a very difficult problem which has not been solved by manufacturers at present is solved, the blank of shoe material treatment of the chemical industry is filled up, a traditional complicated manufacturing technology becomes easy, the manufacturing process is simplified, cost is greatly reduced, the financial resources, the material resources and the manpower resources are greatly saved, and consumption of all the resources is greatly reduced.

Description

technical field [0001] The invention relates to a treatment agent, in particular to a universal shoe material treatment agent capable of meeting the requirements of various shoe materials and a preparation method thereof. Background technique [0002] For more and more shoe materials in the market, such as rubber sole, TPR, PU, ​​PVC, PU foam, EVA [0003] Foam, PE / PP bottom fabric, nylon, oil leather, sheepskin, artificial leather, etc. The performance of these shoe materials, [0004] The requirements for aesthetics and durability are increasing day by day, and in order to save costs and improve performance, manufacturers have made many improvements to the cost process of materials. This puts higher demands on the adhesive (glue) treatment agent. Different treatment agents are customized for each material, so there are rubber treatment agents, EVA treatment agents, TPR treatment agents, nylon treatment agents, PU, ​​PVC treatment agents, etc. There are many types of tr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & AuthorityPatents(China)
IPC IPC(8): C09J4/06C09J11/06
Inventor张升喜张宇航张涛陈玉霞陈俭勇陈杰
OwnerGUANGSHAN BOZHENG RESIN