A5B19 type rare earth-yttrium-nickel system hydrogen storage alloy added with zirconium and titanium elements

A technology of hydrogen storage alloys and rare earths, which is applied to electrical components, battery electrodes, circuits, etc., can solve the problems of increased manufacturing difficulty, difficult control of alloy components, and potential safety hazards, and achieves simple, safe, and The effect of good activation properties

Active Publication Date: 2014-11-19
BAOTOU RES INST OF RARE EARTHS +2
View PDF5 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the high vapor pressure of the active metal element magnesium, the manufacturing difficulty is increased, and the alloy composition

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A5B19 type rare earth-yttrium-nickel system hydrogen storage alloy added with zirconium and titanium elements
  • A5B19 type rare earth-yttrium-nickel system hydrogen storage alloy added with zirconium and titanium elements
  • A5B19 type rare earth-yttrium-nickel system hydrogen storage alloy added with zirconium and titanium elements

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 12

[0022] The alloys described in Example 12 and Example 13 were prepared using the same ratio of raw materials. The alloy described in Example 12 is prepared by the aforementioned high-temperature smelting-quick quenching method. The process is as follows: the purity of each elemental metal or intermediate alloy raw material in the composition is >99.0%, and the ratio of the chemical molecular formula is calculated and each raw material is accurately weighed ( Raw materials that are easy to burn need to increase the ratio in an appropriate amount), put the raw materials into Al 2 o 3 The crucible is evacuated to 3.0Pa and filled with inert gas Ar to 0.055MPa. Heat up and melt, keep warm for about 6 minutes and then quickly solidify. The speed of the quick-setting copper roller is 3.4m / s. The copper roller is usually fed with cooling water, and the temperature of the cooling water is 25°C.

Embodiment 13

[0023]The alloy described in Example 13 can also be prepared by high-temperature smelting-quick quenching method, and an annealing heat treatment step is added in the process, specifically: the purity of each elemental metal or intermediate alloy raw material in the composition is >99.0%, and the ratio is calculated according to the chemical molecular formula Calculate and accurately weigh each raw material (the proportion of easy-to-burn raw materials needs to be increased in an appropriate amount), and put the raw materials into Al 2 o 3 The crucible is evacuated to 3.0Pa and filled with inert gas Ar to 0.055MPa. Heat up and smelt, keep warm for about 6 minutes and then quickly solidify. The speed of the quick-setting copper roller is 3.4m / s. The copper roller is usually fed with cooling water, and the temperature of the cooling water is 25°C. The quick-setting alloy flakes were annealed and heat-treated at 750°C for 8 hours under the protection of vacuum or inert gas.

Embodiment 24

[0024] M1 in Example 24 is a lanthanum-rich mixed rare earth metal, which contains about 64% of La, about 25% of Ce, about 3% of Pr, and about 8% of Nd.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to rare earth system hydrogen storage alloy with the general formula of RExYyNiz-a-b-cMnaAlbMcZrATiB. The peak capacity of an alloy electrode is higher than that of LaNi5 type hydrogen storage alloy, and the manufacturing method is simple and safe. The hydrogen storage alloy has the good activation property, the rate discharge capability, and charging and discharging or hydrogen absorption and desorption circular stability, can be used in the wider temperature range, and is small in self discharging. The method can be used for manufacturing a cathode of an alkaline rechargeable battery and a rechargeable battery with the hydrogen storage alloy.

Description

technical field [0001] The invention relates to a kind of A containing zirconium and titanium elements 5 B 19 type rare earth-yttrium-nickel hydrogen storage alloy. Background technique [0002] Hydrogen storage alloys are a class of functional materials with high hydrogen storage density discovered in the late 1960s. The existing hydrogen storage alloys can be roughly divided into six categories in terms of composition: rare earth series AB 5 type like LaNi 5 ; Magnesium series such as Mg 2 Ni, MgNi, La 2 Mg 17 ;Rare earth-magnesium-nickel system AB 3-3.5 type like La 2 MgNi 9 , La 5 Mg 2 Ni 23 , La 3 MgNi 14 ;Titanium-based AB type such as TiNi, TiFe; zirconium, titanium-based Laves phase AB 2 Type such as ZrNi 2 ; Vanadium series solid solution type such as (V 0.9 Ti 0.1 ) 1-x Fe x . [0003] The widely used hydrogen storage material is LaNi 5 type hydrogen storage alloy. The alloy is mainly used as the negative electrode material of metal hydride-ni...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C19/03H01M4/38
CPCY02E60/10
Inventor 李宝犬闫慧忠王利熊玮李金
Owner BAOTOU RES INST OF RARE EARTHS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap