Anti-static polyvinyl chloride sole material and manufacturing method thereof

Abstract

The invention provides an anti-static polyvinyl chloride sole material, and the anti-static polyvinyl chloride sole material comprises the components in parts by weight as follows; 35-50 parts of polyvinyl chloride, 1-5 parts of anionic antistatic agent, 20-30 parts of plasticizer, 1-5 parts of antioxygen, 2-5 parts of reinforcing agent, 3-8 parts of polyethylene wax, 5-15 parts of chlorinated polyethylene and 3-10 parts of calcium carbonate. The manufacturing method for anti-static polyvinyl chloride sole material is also provided. The anti-static polyvinyl chloride sole material has good anti-static performance applied to the anti-static situation.

Description

Technical field:

[0001] The invention relates to a sole material, in particular to an antistatic polyvinyl chloride sole material and a manufacturing method thereof. Background technique:

[0002] Polyvinyl chloride is a thermoplastic resin polymerized by vinyl chloride under the action of an initiator. It is a homopolymer of vinyl chloride and has a wide range of uses. It can be used in plates, pipes, shoe soles, toys, doors and windows, wire sheaths, stationery, packaging boxes, etc. , of which polyvinyl chloride has a great share in the field of shoe materials. Ordinary PVC shoe materials have a high surface resistivity and are prone to static electricity, which can cause explosions of flammable materials in chemical depots, oil depots, coal mines, and other accidents, as well as failure of electronic components. Invention content:

[0003] The technical problem to be solved by the present invention is to provide an antistatic polyvinyl chloride sole material, which ha...

Examples

Embodiment 1

[0023] A kind of antistatic polyvinyl chloride shoe sole material, its weight part consists of:

[0024]

[0025] Its manufacturing method comprises the following steps:

[0026] (1) drying: select the anionic antistatic agent according to the formula, and dry it;

[0027] (2) Mixing: According to the formula, the dried quaternary ammonium salt type cationic surfactant and other components in the formula are mixed to obtain a uniformly mixed material;

[0028] (3) extrude: the material that step (2) obtains is added extruder, extrudes and obtains antistatic polyvinyl chloride pellet;

[0029] (4) Injection molding: adding the antistatic polyvinyl chloride pellets obtained in step (3) into an injection molding machine, and injection molding to obtain an antistatic polyvinyl chloride sole material.

Embodiment 2

[0031] A kind of antistatic polyvinyl chloride shoe sole material, its weight part consists of:

[0032]

[0033] Its manufacturing method comprises the following steps:

[0034] (1) drying: select the anionic antistatic agent according to the formula, and dry it;

[0035] (2) Mixing: According to the formula, the dried quaternary ammonium salt type cationic surfactant and other components in the formula are mixed to obtain a uniformly mixed material;

[0036] (3) extrude: the material that step (2) obtains is added extruder, extrudes and obtains antistatic polyvinyl chloride pellet;

[0037] (4) Injection molding: adding the antistatic polyvinyl chloride pellets obtained in step (3) into an injection molding machine, and injection molding to obtain an antistatic polyvinyl chloride sole material.

Embodiment 3

[0039] A kind of antistatic polyvinyl chloride shoe sole material, its weight part consists of:

[0040]

[0041]

[0042] Its manufacturing method comprises the following steps:

[0043] (1) drying: select the anionic antistatic agent according to the formula, and dry it;

[0044] (2) Mixing: According to the formula, the dried quaternary ammonium salt type cationic surfactant and other components in the formula are mixed to obtain a uniformly mixed material;

[0045] (3) extrude: the material that step (2) obtains is added extruder, extrudes and obtains antistatic polyvinyl chloride pellet;

[0046] (4) Injection molding: adding the antistatic polyvinyl chloride pellets obtained in step (3) into an injection molding machine, and injection molding to obtain an antistatic polyvinyl chloride sole material.

Technical field:

[0001] The invention relates to a sole material, in particular to an antistatic polyvinyl chloride sole material and a manufacturing method thereof. Background technique:

[0002] Polyvinyl chloride is a thermoplastic resin polymerized by vinyl chloride under the action of an initiator. It is a homopolymer of vinyl chloride and has a wide range of uses. It can be used in plates, pipes, shoe soles, toys, doors and windows, wire sheaths, stationery, packaging boxes, etc. , of which polyvinyl chloride has a great share in the field of shoe materials. Ordinary PVC shoe materials have a high surface resistivity and are prone to static electricity, which can cause explosions of flammable materials in chemical depots, oil depots, coal mines, and other accidents, as well as failure of electronic components. Invention content:

[0003] The technical problem to be solved by the present invention is to provide an antistatic polyvinyl chloride sole material, which ha...

Examples

Embodiment 1

[0023] A kind of antistatic polyvinyl chloride shoe sole material, its weight part consists of:

[0024]

[0025] Its manufacturing method comprises the following steps:

[0026] (1) drying: select the anionic antistatic agent according to the formula, and dry it;

[0027] (2) Mixing: According to the formula, the dried quaternary ammonium salt type cationic surfactant and other components in the formula are mixed to obtain a uniformly mixed material;

[0028] (3) extrude: the material that step (2) obtains is added extruder, extrudes and obtains antistatic polyvinyl chloride pellet;

[0029] (4) Injection molding: adding the antistatic polyvinyl chloride pellets obtained in step (3) into an injection molding machine, and injection molding to obtain an antistatic polyvinyl chloride sole material.

Embodiment 2

[0031] A kind of antistatic polyvinyl chloride shoe sole material, its weight part consists of:

[0032]

[0033] Its manufacturing method comprises the following steps:

[0034] (1) drying: select the anionic antistatic agent according to the formula, and dry it;

[0035] (2) Mixing: According to the formula, the dried quaternary ammonium salt type cationic surfactant and other components in the formula are mixed to obtain a uniformly mixed material;

[0036] (3) extrude: the material that step (2) obtains is added extruder, extrudes and obtains antistatic polyvinyl chloride pellet;

[0037] (4) Injection molding: adding the antistatic polyvinyl chloride pellets obtained in step (3) into an injection molding machine, and injection molding to obtain an antistatic polyvinyl chloride sole material.

Embodiment 3

[0039] A kind of antistatic polyvinyl chloride shoe sole material, its weight part consists of:

[0040]

[0041]

[0042] Its manufacturing method comprises the following steps:

[0043] (1) drying: select the anionic antistatic agent according to the formula, and dry it;

[0044] (2) Mixing: According to the formula, the dried quaternary ammonium salt type cationic surfactant and other components in the formula are mixed to obtain a uniformly mixed material;

[0045] (3) extrude: the material that step (2) obtains is added extruder, extrudes and obtains antistatic polyvinyl chloride pellet;

[0046] (4) Injection molding: adding the antistatic polyvinyl chloride pellets obtained in step (3) into an injection molding machine, and injection molding to obtain an antistatic polyvinyl chloride sole material.