Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A kind of activated carbon fiber paper and preparation method thereof

A technology of activated carbon fiber and precipitated fiber, which is applied in the direction of synthetic cellulose/non-cellulose material pulp/paper, fiber raw material treatment, papermaking, etc. Insufficient strength and other problems, to achieve the effect of good paper-forming property, excellent adsorption performance and high strength

Active Publication Date: 2017-02-15
南通大学技术转移中心有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in practical applications, when the amount of activated carbon powder is large, there is usually the problem that the strength of the filter paper is not enough and it is easy to lose powder. However, reducing the amount of activated carbon powder and increasing the amount of fiber pulp will lead to a decrease in the adsorption and filtration efficiency of the filter paper and cannot meet the use requirements. difficult to balance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Preparation of meta-aramid fibrids: isophthaloyl chloride (IPC) and meta-phenylenediamine (MPD) were used as monomers to synthesize meta-aramid fiber solution in dimethylacetamide (DMAc) system. The meta-aramid fiber was prepared by using the synthetic meta-aramid fiber solution. Among them, the concentration of meta-aramid fiber solution is 3%, and the coagulation bath H 2 The O / DMAc mixing weight ratio was 70:30, and the rotor speed was 2000 r / min.

[0023] Fiber paper preparation: The weighed meta-aramid fibrid was decomposed with a beater at a beating concentration of 3% for 25 min to obtain a fibrid slurry with a beating degree of 55°SR. The weighed chopped viscose-based activated carbon fiber with a length of 3 mm was decomposed with a beating machine at a beating concentration of 2% for 15 min to obtain an activated carbon fiber slurry with a beating degree of 15°SR. According to the ratio of meta-aramid fibrillar fiber accounting for 30% (based on the absolute...

Embodiment 2

[0025] Preparation of meta-aramid fibrids: isophthaloyl chloride (IPC) and meta-phenylenediamine (MPD) were used as monomers to synthesize meta-aramid fiber solution in dimethylacetamide (DMAc) system. The meta-aramid fiber was prepared by using the synthetic meta-aramid fiber solution. Among them, the concentration of meta-aramid fiber solution is 5%, and the coagulation bath H 2 The O / DMAc mixing weight ratio was 60:40, and the rotor speed was 2500 r / min.

[0026] Preparation of fiber paper: The weighed meta-aramid fibrid was decomposed with a beater at a beating concentration of 1% for 10 min to obtain a fibrid slurry with a beating degree of 40°SR. The weighed chopped viscose-based activated carbon fiber with a length of 1 mm was decomposed with a beating machine at a beating concentration of 5% for 20 min to obtain an activated carbon fiber slurry with a beating degree of 20°SR. According to the ratio of meta-aramid fibrillar fiber accounting for 10% (based on the absol...

Embodiment 3

[0028] Preparation of para-aramid fibrids: Using terephthaloyl chloride (IPC) and para-phenylenediamine (MPD) as monomers, para-aramid fiber solution was synthesized in dimethylacetamide (DMAc) system. Using the synthetic para-aramid fiber solution, the para-aramid fiber is prepared. Among them, the concentration of para-aramid fiber solution is 7%, and the coagulation bath H 2 The O / DMAc mixing weight ratio was 70:30, and the rotor speed was 3000 r / min.

[0029] Preparation of fiber paper: The weighed para-aramid fibrid was decomposed with a beater at a beating concentration of 5% for 30 min to obtain a fibrid slurry with a beating degree of 70°SR. The weighed chopped viscose-based activated carbon fiber with a length of 8 mm was decomposed with a beating machine at a beating concentration of 1% for 10 min to obtain an activated carbon fiber slurry with a beating degree of 10 °SR. According to the ratio of the para-aramid fibrillar fiber to 50% (the ratio of the absolute dr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses activated carbon fiber paper and a preparation method thereof. The activated carbon fiber paper adopts aramid fibrids as carriers, and the carriers are loaded with activated carbon fibers, wherein the lengths of the activated carbon fibers are within 1-8mm, and the aramid fibrids account for 10-50% of the activated carbon fiber paper in oven-dry mass. Compared with traditional activated carbon fiber paper, the prepared activated carbon fiber paper has the high adsorptive property and high strength.

Description

technical field [0001] The invention relates to a filter paper, in particular to a filter paper using activated carbon fiber as a filter material. Background technique [0002] Activated carbon (AC) is a porous functional material with developed pore structure. Activated carbon filter paper prepared by using the characteristics of activated carbon is a functional filter material, which can be used for air and water purification and military chemical protection. field with broad market prospects. At present, most of the common activated carbon filter papers on the market are made of plant fiber pulp as a carrier, and activated carbon powder is added to the pulp and made by a paper machine. The filtration mechanism is that the activated carbon particles in the paper have a porous structure and a very large specific surface area. It has a strong adsorption capacity for certain components in the gas, and can selectively adsorb and separate toxic and harmful gases from the air. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D21H15/12D21H13/50D21H13/26
Inventor 刘其霞季涛高强倪朝辉姚理荣王飞艳余进
Owner 南通大学技术转移中心有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com