Preparation method of plant fiber/glass fiber-based special thin-sheet substrate

A plant fiber, glass fiber-based technology, applied in the directions of synthetic cellulose/non-cellulose material pulp/paper, non-fiber pulp addition, fiber raw material processing, etc., can solve the problems of poor softness, high brittleness, easy moisture absorption, etc. Achieve the effect of avoiding uneven fiber dispersion, uniform appearance and performance

Active Publication Date: 2019-04-16
SHAANXI UNIV OF SCI & TECH
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Since domestic research on plant fiber/glass fiber-based sound-absorbing and flame-retardant thin sheet materials started relatively late, although some basic research has been carried out and some progress has been made, there are still many problems in the production practice process, especially with Compared wi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A method for preparing a plant fiber / glass fiber-based special sheet substrate, comprising the following steps:

[0029] Step 1, pre-treatment of commercial chemical pulp board: after soaking an appropriate amount of pulp board in water for a certain period of time, disperse the fiber into a uniform fiber suspension with a disintegrator, filter the pulp, wring it out, and balance the water for later use; commercial chemical pulp The board is one of coniferous wood pulp board, hardwood pulp board or bamboo pulp board;

[0030] Step 2, fiber dispersion: put a certain quality of glass fiber and water in a deflagging machine, add a dispersant, and after decomposing for 2w, add the slurry obtained in step 1, and then decompose for 1w to obtain a mixture of glass fibers and plant fibers mixed pulp;

[0031] Step 3, base paper making: copying the mixed pulp with evenly dispersed fibers in step 2 on a paper sample machine;

[0032] Step 4, preparation of dipping solution: tak...

Embodiment 2

[0037] A method for preparing a plant fiber / glass fiber-based special sheet substrate, comprising the following steps:

[0038] Step 1, pre-treatment of commercial chemical pulp board: after soaking an appropriate amount of pulp board in water for a certain period of time, disperse the fiber into a uniform fiber suspension with a disintegrator, filter the pulp, wring it out, and balance the water for later use; commercial chemical pulp The board is one of coniferous wood pulp board, hardwood pulp board or bamboo pulp board;

[0039] Step 2, fiber dispersion: put a certain quality of glass fiber and water in a deflagging machine, add a dispersant, and after decomposing for 2w, add the slurry obtained in step 1, and then decompose for 1w to obtain a mixture of glass fibers and plant fibers mixed pulp;

[0040] Step 3, base paper making: copying the mixed pulp with evenly dispersed fibers in step 2 on a paper sample machine;

[0041] Step 4, preparation of impregnating solution...

Embodiment 3

[0046] A method for preparing a plant fiber / glass fiber-based special sheet substrate, comprising the following steps:

[0047] Step 1, pre-treatment of commercial chemical pulp board: after soaking an appropriate amount of pulp board in water for a certain period of time, disperse the fiber into a uniform fiber suspension with a decomposer, filter the pulp, wring it out, and balance the water for later use; commercial chemical pulp The board is one of coniferous wood pulp board, hardwood pulp board or bamboo pulp board;

[0048] Step 2, fiber dispersion: put a certain quality of glass fiber and water in a deflagging machine, add a dispersant, and after decomposing for 2w, add the slurry obtained in step 1, and then decompose for 1w to obtain a mixture of glass fibers and plant fibers mixed pulp;

[0049]Step 3, base paper making: copying the mixed pulp with evenly dispersed fibers in step 2 on a paper sample machine;

[0050] Step 4, preparation of impregnating liquid: take...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tightnessaaaaaaaaaa
Bulkaaaaaaaaaa
Tightnessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a plant fiber/glass fiber-based special thin-sheet substrate. The method comprises the steps that a commercial chemical pulp board is pretreated, fiberis dispersed, base paper is manufactured with pulp, a maceration extract is prepared, and the base paper is macerated and dried. The plant fiber/glass fiber-based special thin-sheet substrate preparedby combining various measures has the advantages that through maceration with different plasticizers, the compactness of the plant fiber/glass fiber-based special thin-sheet substrate is reduced, thebulk of the material is improved, the absorbing quality is better, and the brittleness of the material is ameliorated, so that the plant fiber/glass fiber-based special thin-sheet substrate is difficult to break during construction and better meets the needs for production and life.

Description

technical field [0001] The invention belongs to the technical field of special paper preparation, and relates to a method for preparing a plant fiber / glass fiber-based special sheet substrate. Background technique [0002] Plant fiber / glass fiber-based special thin sheet substrate is the raw material for preparing plant fiber / glass fiber-based sound-absorbing and flame-retardant thin sheet materials. It is made of plant fiber and glass fiber in a certain proportion by wet papermaking. After being impregnated with binder, it can endow the substrate with certain strength, which is convenient for production and use. Plant fiber / glass fiber-based sound-absorbing and flame-retardant sheet material is a building decoration material with sound-absorbing and flame-retardant functions. It is made of plant fiber / glass fiber-based special sheet substrate, impregnated with flame retardant, color paste and other impregnating liquids, endowing it with good flame retardancy and decoration...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D21H15/12D21H13/40D21H21/08D21H21/14D21H23/32D21H25/06
CPCD21H13/40D21H15/12D21H21/08D21H21/14D21H23/32D21H25/06
Inventor 徐永建王敏李伟岳小鹏
Owner SHAANXI UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap