Aluminum alloy radiator before-paint-spraying passivating solution

A passivation solution and radiator technology, applied in the direction of metal material coating process, etc., can solve the problems of poor corrosion resistance of film formation, and achieve the effects of fast passivation, cost reduction and process saving.

Inactive Publication Date: 2015-02-04
无锡永发电镀有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The conversion coating on the surface of aluminum or aluminum alloy treated in this way does not contain chromiu

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A passivation solution before painting an aluminum alloy radiator, the passivation solution is composed of: sodium molybdate 6g / L, potassium fluoroborate 6g / L, magnesium titanate 3g / L, sodium zirconate 10g / L, water-based polyurethane 16g / L, boric acid 14g / L, acetic acid 4g / L, thiourea 2g / L, and the balance is water.

Embodiment 2

[0016] A passivation solution before painting an aluminum alloy radiator, the passivation solution is composed of: sodium molybdate 8g / L, potassium fluoroborate 4g / L, magnesium titanate 5g / L, sodium zirconate 8g / L, water-based polyurethane 18g / L, boric acid 12g / L, acetic acid 6g / L, thiourea 1g / L, and the balance is water.

Embodiment 3

[0018] A passivation solution before painting an aluminum alloy radiator, the passivation solution is composed of: sodium molybdate 7g / L, potassium fluoroborate 5g / L, magnesium titanate 4g / L, sodium zirconate 9g / L, water-based polyurethane 17g / L, boric acid 13g / L, acetic acid 5g / L, thiourea 1.5g / L, and the balance is water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an aluminum alloy radiator before-paint-spraying passivating solution comprising the following components: 6-8g / L of sodium molybdate, 4-6G / L of potassium fluoborate, 3-5g / L of magnesium titanate, 8-10G / L of sodium zirconate, 16-18G / L of waterborne polyurethane, 12-14g / L of boric acid, 4 6G / L of acetic acid, 1-2g / L of thiourea, and the balance of water.

Description

technical field [0001] The invention relates to the technical field of surface treatment, in particular to a passivation solution before painting an aluminum alloy radiator. Background technique [0002] With the improvement of people's living standards, people are increasingly pursuing the practicality and beauty of home decoration. Among them, the exterior of the aluminum alloy radiator can be painted with various colors of paint to match other colors of home decoration, and because of the good thermal conductivity of aluminum , high heat dissipation efficiency, therefore, colorful radiators made of aluminum alloys are more and more popular. [0003] Various pretreatments are required before aluminum alloy painting, among which chemical conversion coating is the most commonly used technical means in aluminum surface treatment. The chemical conversion coating has a certain corrosion resistance and good physical adsorption capacity, which can greatly improve the bonding for...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C22/44
CPCC23C22/44
Inventor 石明
Owner 无锡永发电镀有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap