High strength steel bar for pre-stressed concrete and production technology thereof

A production process and prestressing technology, applied in the field of smelting, can solve problems such as poor steel bar performance, high process cost, and hidden quality problems, and achieve good upsetting performance, ensure product qualification rate, and strong hysteresis fracture resistance

Active Publication Date: 2015-03-11
溧阳市万兴特种建材有限公司
View PDF3 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the production process of steel rods for general prestressed concrete is setting-off—peeling and derusting—shape and groove—straightening—induction heating—quenching—tempering—cooling—transmission—shearing and splitting—rewinding, and the process cost is high. , a waste of steel, the process is complicated and inconvenient to operate, and the manuf

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] This embodiment provides a steel bar for high-strength prestressed concrete, the chemical composition of which is: C: 0.25%, Si: 1.65%, Mn: 0.20%, Cr: 0.08%, Mo: 0.35%, V: 0.25 %, Nb: 0.08%, Ti: 0.50%, Ni: 0.25%, Ca: 0.30%, S: 0.025%, P: 0.010%, Cu: 0.15%, composite rare earth: 0.20%, and the balance is Fe;

[0041] The composition of compound rare earth is calculated by mass percentage: holmium: 5%, gadolinium: 8%, yttrium: 9%, cerium: 20%, praseodymium: 23%, neodymium: 12%, dysprosium: 14%, and the rest is lanthanum, The sum of the above components is 100%.

[0042] The production process of the above-mentioned high-strength prestressed concrete steel rod, the specific production process is as follows:

[0043] (1) The above components are used as raw materials through converter smelting, refining treatment, and continuous casting to obtain billets, and then the billets are heated to 1000°C through a walking heating furnace, and the heated billets are taken out of th...

Embodiment 2

[0057] This embodiment provides a steel bar for high-strength prestressed concrete, and its weight percentage chemical composition is: C: 0.20%, Si: 1.50%, Mn: 0.50%, Cr: 0.07%, Mo: 0.30%, V: 0.35 %, Nb: 0.05%, Ti: 0.42%, Ni: 0.15%, Ca: 0.25%, S: 0.015%, P: 0.015%, Cu: 0.20%, composite rare earth: 0.15%, and the balance is Fe;

[0058] The composition of compound rare earth is calculated by mass percentage: holmium: 8%, gadolinium: 9%, yttrium: 8%, cerium: 18%, praseodymium: 25%, neodymium: 15%, dysprosium: 11%, and the rest is lanthanum, The sum of the above components is 100%.

[0059] The production process of the above-mentioned high-strength prestressed concrete steel rod, the specific production process is as follows:

[0060] (1) The above components are used as raw materials through converter smelting, refining treatment, and continuous casting to obtain billets, and then the billets are heated to 1250°C through a walking heating furnace, and the heated billets are ta...

Embodiment 3

[0074] This embodiment provides a steel rod for high-strength prestressed concrete, the chemical composition of which is: C: 0.22%, Si: 1.85%, Mn: 0.35%, Cr: 0.09%, Mo: 0.33%, V: 0.30 %, Nb: 0.07%, Ti: 0.61%, Ni: 0.18%, Ca: 0.40%, S: 0.020%, P: 0.025%, Cu: 0.15%, composite rare earth: 0.30%, and the balance is Fe;

[0075] The composition of compound rare earth is calculated by mass percentage: holmium: 7%, gadolinium: 10%, yttrium: 10%, cerium: 15%, praseodymium: 24%, neodymium: 13%, dysprosium: 13%, and the rest is lanthanum, The sum of the above components is 100%.

[0076] The production process of the above-mentioned high-strength prestressed concrete steel rod, the specific production process is as follows:

[0077](1) The above-mentioned components are used as raw materials through converter smelting, refining treatment, and continuous casting to obtain billets, and then the billets are heated to 1500°C through a walking heating furnace, and the heated billets are take...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high strength steel bar for pre-stressed concrete. The steel bar is composed of the following chemical components in percentage by weight: 0.20 to 0.25% of C, 1.50 to 1.85% of Si, 0.20 to 0.50% of Mn, 0.07 to 0.09% of Cr, 0.30 to 0.35% of Mo, 0.25 to 0.35% of V, 0.05 to 0.08% of Nb, 0.42 to 0.61% of Ti, 0.15 to 0.25% of Ni, 0.25 to 0.40% of Ca, not more than 0.025% of S, not more than 0.025% of P, not more than 0.20% of Cu, 0.15 to 0.30% of composite rare earth, and the balance being Fe. The invention further discloses a production technology of the steel bar. The production technology comprises the following steps: smelting to obtain a steel blank, rolling the steel blank, cooling the rolled steel blank, rolling the steel blank for a second time, carrying out a thermal treatment and a stabilizing treatment, performing a gas nitrogenation treatment, spinning, winding, bundling, and storing the bundles in a warehouse.

Description

technical field [0001] The invention belongs to the technical field of smelting, and relates to a steel bar and a production process thereof, in particular to a high-strength prestressed concrete steel bar and a production process thereof. Background technique [0002] The production of prestressed steel in my country started in the early 1960s. Due to the influence of the planned economy, the technology was not developed and introduced until the late 1980s. At that time, the automation of domestic production equipment was relatively low and the process was discontinuous. The production efficiency of the prestressed steel bar products developed at the initial stage is very low, the cost is high, and it is difficult to form large-scale production. With the continuous deepening of my country's economic construction and reform and opening up, during the "Eighth Five-Year Plan" period, several domestic enterprises and research institutes jointly developed a continuous prestressed...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/50C21D8/08
CPCC22C38/02C21D8/08C22C38/002C22C38/005C22C38/04C22C38/44C22C38/46C22C38/48C22C38/50
Inventor 姚圣法吴海洋
Owner 溧阳市万兴特种建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap