Weathering steel surface rust layer stabilization treating agent
A stabilized treatment agent and weather-resistant steel technology, which is applied in the coating process of metal materials, etc., to achieve the effects of simple implementation process, reduced pollution, and short drying time
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0018] Example 1
[0019] The embodiment of the present invention is verified by performing a periodic infiltration accelerated corrosion experiment after coating a rust layer stabilizer on the surface of the weathering steel, which specifically includes the following steps:
[0020] Step 1: Process the weathering steel into a 40mm×60mm×4mm sample, degrease with acetone, clean with alcohol, and blow dry for later use.
[0021] Step 2: Prepare 100g rust layer stabilizer solution, 45g water-soluble acrylic resin + 0.5g chromium sulfate + 2g Fe 2 O 3 +1gFe 3 O 4 +0.05g polyethylene glycol +0.25g defoamer +0.25g wetting agent. Brush the rust layer stabilizer on the surface of the weathering steel sample with a brush, and dry for 20 minutes.
[0022] Step 3: Perform 72h weekly immersion corrosion test on the coated rust stabilizer sample and bare steel sample (the test medium is 0.01mol / L NaHSO 3 Solution, the experimental temperature is 45±2℃, the humidity is 70±5%, each cycle is 60min, i...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap