Polyimide precursor solution

A technology of polyimide precursor and polyamic acid, applied in the direction of coating, etc., can solve the problem that it is difficult to obtain polyimide precursor with high degree of polymerization, and achieve easy process control, excellent environmental suitability, flow good flat effect

Active Publication Date: 2016-01-06
UNITIKA LTD
View PDF14 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, if an alcohol mixed with a strong basic compound such as triethylamine or triethylenediamine is used as a polymerization solvent, it is difficult to obtain a polyimide precursor with a high degree of polymerization, and there are also problems in storage stability.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyimide precursor solution
  • Polyimide precursor solution

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0064] Put the mixture of polyamic acid powder A and 1,2-dimethylimidazole (pKa7.7) (2.5 moles of 1,2-dimethylimidazole relative to 1 mole of structural units of polyamic acid) at 25°C It was dissolved in ethylene glycol to obtain a polyimide precursor solution A-1 having a concentration of 15% by mass as a polyimide precursor. Table 1 shows the evaluation results of the properties of the precursor solution.

Embodiment 2

[0066] The mixture of polyamic acid powder B and 1,2-dimethylimidazole (pKa7.7) (1,2-dimethylimidazole relative to the structural unit of polyamic acid 1 mole, use 2.5 moles) at 25 ° C It was dissolved in ethylene glycol to obtain a polyimide precursor solution B-1 having a concentration of 15% by mass as a polyimide precursor. Table 1 shows the evaluation results of the properties of the precursor solution.

Embodiment 3

[0068] Except having used 2-ethyl-4-methylimidazole (pKa8.3) as a basic compound, it carried out similarly to Example 2, and obtained polyimide precursor solution B-2. Table 1 shows the evaluation results of the properties of the precursor solution.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The purpose of the invention is to provide a polyimide precursor solution having excellent environmental compatibility and good storage stability and leveling properties, the polyimide precursor solution making it possible to produce a polyimide molded article having excellent mechanical strength. The invention provides a polyimide precursor solution obtained by dissolving polyamic acid and a salt of a weakly basic compound having an acid dissociation constant (pKa) of 4.5-8.5 in a solvent containing a polyhydric alcohol.

Description

technical field [0001] The present invention relates to polyimide precursor solutions. A polyimide molded article obtained from this polyimide precursor solution has excellent mechanical strength and high heat resistance. Background technique [0002] Molded products composed of aromatic polyimide obtained from aromatic tetracarboxylic dianhydride and aromatic diamine have excellent properties such as heat resistance, mechanical strength, electrical properties, and solvent resistance, so they can be used in the electronics industry. , Copier field, aviation field and so on are widely used. Due to the lack of solubility of the aromatic polyimide, the polyamic acid as a polyimide precursor is usually dissolved in NMP (N-methyl-2-pyrrolidone), DMF (N,N-dimethyl Formamide), DMAc (N,N-dimethylacetamide) and other amide solvents, the resulting solution is coated on the surface of the substrate, and then cured at high temperature (imidization) to obtain a film , belts and other ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L79/08C08G73/10
CPCC08G73/105C08G73/1067C08G73/1071C08K5/3432C08K5/3445C09D179/08
Inventor 繁田朗吉田猛山田祐己森北达弥细田雅弘越后良彰
Owner UNITIKA LTD
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com