Special nano-modified impregnating compound for basalt continuous fiber and preparation method of special nano-modified impregnating compound

A continuous fiber, nano-modified technology, applied in the field of textile materials, can solve the problems of inability to meet the requirements of weaving into fiber cloth, poor textile properties of basalt fibers, etc., to improve spinnability, mechanical properties, mechanical properties and aging resistance. excellent effect

Active Publication Date: 2016-01-27
江门市新会区美亚化工有限公司
View PDF5 Cites 38 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] According to the above-mentioned prior art, there have been researches on special sizing agent for basalt fiber at present, b

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Special nano-modified impregnating compound for basalt continuous fiber and preparation method of special nano-modified impregnating compound

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Components of a nano-modified sizing agent for continuous basalt fibers, in parts by weight, comprising:

[0038] 25 parts of silicone modified acrylate and polyester resin emulsion;

[0039] 15 parts of fatty acid amide acetate and fatty acid ester sulfate;

[0040] 5 parts of quaternary ammonium salt cationic antistatic agent;

[0041] 5 parts of nano silicon dioxide and titanium dioxide particles;

[0042] 15 parts of silane coupling agent;

[0043] 20 parts of citric acid;

[0044] 5 parts of sodium lactate;

[0045] 50 parts of deionized water.

[0046] Specifically include the following steps:

[0047] (1) Add citric acid to the deionized aqueous solution, adjust the pH value of the citric acid aqueous solution to 3, stir at a high speed of 2000rpm / min for 5min, and add 40 parts of citric acid aqueous solution at 15 drops / min Slowly add 1 part of silane coupling agent dropwise, and continue to stir for 2 hours until the hydrolysis is complete to obtain a cl...

Embodiment 2

[0051] Components of a nano-modified sizing agent for continuous basalt fibers, in parts by weight, comprising:

[0052] 35 parts of silicone modified acrylate and polyester resin emulsion;

[0053] 20 parts of fatty acid amide acetate and fatty acid ester sulfate;

[0054] 10 parts of quaternary ammonium salt cationic antistatic agent;

[0055] 15 parts of nano silicon dioxide and titanium dioxide particles;

[0056] 25 parts of silane coupling agent;

[0057] 30 parts of citric acid;

[0058] 10 parts of sodium lactate;

[0059] 100 parts of deionized water.

[0060] Specifically include the following steps:

[0061] (1) Add citric acid to the deionized aqueous solution, adjust the pH value of the citric acid aqueous solution to 4, stir at a high speed of 2000rpm / min for 10min, and add 50 parts of citric acid aqueous solution at 20 drops / min Slowly add 1 part of silane coupling agent dropwise, and continue to stir for 3 hours until the hydrolysis is complete to obtain...

Embodiment 3

[0065] Components of a nano-modified sizing agent for continuous basalt fibers, in parts by weight, comprising:

[0066] 30 parts of silicone modified acrylate and polyester resin emulsion;

[0067] 17 parts of fatty acid amide acetate and fatty acid ester sulfate;

[0068] 8 parts of quaternary ammonium salt cationic antistatic agent;

[0069] 10 parts of nano silicon dioxide and titanium dioxide particles;

[0070] 20 parts of silane coupling agent;

[0071] 25 parts of citric acid;

[0072] 7 parts of sodium lactate;

[0073] 80 parts of deionized water.

[0074] Specifically include the following steps:

[0075] (1) Add citric acid to the deionized aqueous solution, adjust the pH value of the citric acid aqueous solution to 3.5, stir at a high speed of 2000rpm / min for 8min, and add 45 parts of citric acid aqueous solution at 17 drops / min Slowly add 1 part of silane coupling agent dropwise, and continue to stir for 2.5 hours until the hydrolysis is complete to obtain...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a special nano-modified impregnating compound for basalt continuous fiber and a preparation method of the special nano-modified impregnating compound. The preparation method comprises specific operation steps as follows: (1), citric acid is added to a deionized aqueous solution, the PH (potential of hydrogen) value of a citric acid aqueous solution is adjusted to range from 3 to 4, the mixture is stirred at a high speed, a silane coupling agent is slowly and dropwise added, the mixture is stirred until the silane coupling agent is completely hydrolyzed, and a clear and transparent hydrolyzed coupling agent is obtained; (2), organosilicone-modified acrylic ester and a polyester resin emulsion are diluted by 10-20 times with deionized water respectively and then are mixed and uniformly stirred, and a diluted film forming agent is obtained, monodispersed nano-silica and titanium dioxide particles are added, the mixture is heated, stirred and cooled at the room temperature, and the film forming agent containing nano particles is obtained; (3), fatty acid amide acetate, aliphatic ester sulfate and a quaternary ammonium salt cationic antistatic agent are added to deionized water, the PH value of the solution is adjusted, the hydrolyzed coupling agent and the film forming agent containing the nano particles are added respectively, the mixture is stirred uniformly and left to stand to be defoamed, and the special nano-modified impregnating compound for the basalt continuous fiber is obtained.

Description

Technical field: [0001] The invention belongs to the technical field of textile materials, and in particular relates to a special sizing agent for nano-modified basalt continuous fibers and a preparation method thereof. Background technique: [0002] Basalt fiber is a new type of inorganic fiber. The unique composition of basalt ore and the combination of fiber structure endow the fiber with high strength, high modulus, high temperature corrosion resistance, and the fiber can be directly returned to nature without causing environmental pollution. It is green and environmentally friendly. At present, my country has mastered the preparation technology of basalt fiber, but the research and development of sizing agent for basalt fiber is still less, and the sizing agent of glass fiber is mostly used for basalt fiber. [0003] However, as we all know, the formulation of the sizing agent should be adjusted according to the type and use of the fiber. The sizing agent for glass fiber...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C25/40
Inventor 董芬芳
Owner 江门市新会区美亚化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap