Novel ageing-resistant and combustion-resistant wood-based panel with immersion film paper veneer and preparation method thereof

An anti-aging, membrane paper technology, applied in chemical instruments and methods, paper/cardboard layered products, wood layered products, etc., can solve the aging problem of decorative boards and poor flame resistance, high formaldehyde emission of decorative boards, Toxic gas pollutes the environment and other problems, achieving the effect of omitting gluing equipment, reducing gluing process links, and increasing environmental pollution

Active Publication Date: 2016-03-09
DYNEA GUANGDONG
View PDF7 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the current man-made decorative panels, the production process involves the process of gluing, and the poisonous gas produced by gluing not only pollutes the environmen

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel ageing-resistant and combustion-resistant wood-based panel with immersion film paper veneer and preparation method thereof
  • Novel ageing-resistant and combustion-resistant wood-based panel with immersion film paper veneer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-3 and comparative example 1-2

[0038] A preparation method of a new impregnated film paper facing anti-aging and flame-resistant decorative board,

[0039] Step 1) Laying adhesive film, medium-density stickers, adhesive film and decorative plates on the substrate layer in sequence to form a blank;

[0040] Step 2) After the blank assembly is completed, put it into a hot press machine for hot pressing. The conditions for hot pressing are: the hot pressing temperature is 130-150°C, the hot pressing time is 5 minutes to 7 minutes, and the hot pressing pressure is 12- 15 kg / cm2;

[0041] The adhesive film is made of kraft paper with a gram weight of 40-60 g / dm2 after being impregnated with phenolic resin, and then dried and formed. The amount of kraft paper impregnated with glue is 180%-250%;

[0042] The medium-density sticker is made of kraft paper with a gram weight of 210-240 grams per square decimeter, which is impregnated with phenolic resin and dried to form a membrane paper. The amount of kraft paper i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention provides a novel ageing-resistant and combustion-resistant wood-based panel with an immersion film paper veneer and a preparation method thereof. The method comprises the following steps: (1) sequentially paving an adhesive film, a medium density decal, an adhesive film and a decorative sheet on a substrate layer and assembling; 2) after assembling is completed, placing in a thermocompressor for hot pressing, wherein the adhesive film is film paper which is obtained by soaking kraft paper with gram weight of 40-60 grams/square decimeter by using phenolic resin and then drying and molding, the adhesive dipping amount of the kraft paper is 180%-250%, the medium density decal is film paper which is obtained by soaking kraft paper with gram weight of 210-2400 grams/square decimeter by using phenolic resin, and the adhesive dipping amount of the kraft paper is 30%-35%; and 3) cropping and trimming an ageing-resistant and combustion-resistant decorative panel. The decorative panel provided by the present invention has low formaldehyde emission and good ageing-resistant and combustion-resistant properties.

Description

technical field [0001] The invention relates to a wood-based panel decorative building material, in particular to an anti-aging and flame-resistant decorative panel with low formaldehyde emission and a preparation method thereof. Background technique [0002] Wood-based panels are made of wood, wood chips, scraps, shavings and their processing residues as raw materials, including plywood, medium density fiberboard, particleboard, hard fiberboard, etc. With the development of wood-based panel secondary processing technology and the continuous improvement of people's quality of life, the demand for high-quality decorative wood-based panels is also increasing. Wood-based panels are widely used in the furniture industry. For example, the cabinet industry mainly uses medium-density fiberboard and particleboard as the base material. After simple finishing or surface paint treatment, decorative and practical values ​​are realized. With the improvement of decoration engineering tec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B15/12B32B29/00B32B29/06B32B27/04B32B27/42B32B21/02B32B21/06B32B38/18B32B37/06B32B37/10B32B38/00C08G14/08
CPCB32B15/12B32B21/02B32B21/06B32B29/005B32B29/06B32B37/06B32B37/10B32B38/0004B32B38/1808B32B2260/028B32B2260/046C08G14/08
Inventor 边国民杨晓燕汪启鸿邱辉
Owner DYNEA GUANGDONG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap