A technology of anti-blue light and blue light absorption, applied in optics, optical components, instruments, etc., can solve the problem of less attention on computer film, and achieve the effect of improving the effect of absorbing blue light and filtering blue light well

Inactive Publication Date: 2016-03-30
NINGBO XIAYUAN TECH
View PDF6 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

General computer film needs to be scratch-resistant and good see-through, but less attention is paid to eye-protecting computer film

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Blue-light-proof film
  • Blue-light-proof film
  • Blue-light-proof film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0062] The raw material formula of the release protective film is as follows:

[0063]

[0064] The preparation process of release protective film comprises the following steps:

[0065] 1. Carry out corresponding parts by weight of trifluoropropylmethylcyclotrisiloxane, polytrimethylene terephthalate, hydroxyethyl cellulose, nano silicon dioxide, methacryloxypropyltrimethoxysilane Mix and mix thoroughly with a mixer;

[0066] 2. In step (1), add vinyl silicone oil, dioctyl adipate, and antioxidant, stir at 500-1000 rpm, and heat to 120-160°C at the same time to obtain a coating material;

[0067] 3. Co-extrude the coating material on the PET paper through the coating agent film head, the co-extrusion temperature is 230-280 ℃, the back pressure is 600pa-1000pa, and the co-extrusion speed is 100-150m / min.

[0068] The raw material formula of the anti-blue light adhesive layer includes the following materials by weight:

[0069]

[0070] The anti-blue light adhesive lay...

Embodiment 2

[0084] The raw material formula of the release protective film is as follows:

[0085]

[0086] The preparation process of release protective film comprises the following steps:

[0087] 1. Carry out corresponding parts by weight of trifluoropropylmethylcyclotrisiloxane, polytrimethylene terephthalate, hydroxyethyl cellulose, methacryloxypropyltrimethoxysilane, and nano silicon dioxide Mix and mix thoroughly with a mixer;

[0088] 2. In step (1), add vinyl silicone oil, dioctyl adipate, and antioxidant 1010, stir at 500-1000 rpm, and heat to 120-160°C at the same time to obtain a coating material;

[0089] 3. Co-extrude the coating material on the PET paper through the coating agent film head, the co-extrusion temperature is 230-280 ℃, the back pressure is 600pa-1000pa, and the co-extrusion speed is 100-150m / min.

[0090] The raw material formula of the anti-blue light adhesive layer is as follows:

[0091]

[0092]

[0093] The anti-blue light adhesive layer is pr...

Embodiment 3

[0107] The raw material formula of the release protective film is as follows:

[0108]

[0109] The preparation process of release protective film comprises the following steps:

[0110] 1. Carry out corresponding parts by weight of trifluoropropylmethylcyclotrisiloxane, polytrimethylene terephthalate, hydroxyethyl cellulose, methacryloxypropyltrimethoxysilane, and nano silicon dioxide Mix and mix thoroughly with a mixer;

[0111] 2. In step (1), add vinyl silicone oil, dioctyl adipate, and antioxidant 1010, stir at 500-1000 rpm, and heat to 120-160°C at the same time to obtain a coating material;

[0112] 3. Co-extrude the coating material on the PET paper through the coating agent film head, the co-extrusion temperature is 230-280 ℃, the back pressure is 600pa-1000pa, and the co-extrusion speed is 100-150m / min.

[0113] The raw material formula of the anti-blue light adhesive layer is as follows:

[0114]

[0115] The anti-blue light adhesive layer is prepared accor...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a blue-light-proof film. The blue-light-proof film includes a release protection film, a mounting adhesive, a PET layer, a blue-light-proof adhesive sticky layer, a blue light absorbing layer and a wear resistant layer which are arranged sequentially; the blue-light-proof adhesive sticky layer is made of raw materials of an organosilicone adhesive, methyl acrylate, nanometer cobalt oxide, phthalic dimethylamine, benzoyl peroxide, hexamethylphosphoric triamide and isocyanate curing agent. Compared with the prior art, the nanometer cobalt oxide in the blue-light-proof adhesive sticky layer of the blue-light-proof film of the invention can well absorb blue light, and the phthalic dimethylamine and the hexamethylphosphoric triamide act cooperatively so as to further improve a blue light absorbing effect, and thus, the blue-light-proof film can assuredly have an excellent blue light filtering effect. As indicated by experiment results, the blue-light-proof film can filter out about 90% of blue light, and the light transmittance of the blue-light-proof film is more than 90%.

Description

technical field [0001] The invention relates to the field of thin film technology, in particular to an anti-blue light film. Background technique [0002] Solar radiation is a type of electromagnetic radiation, which can be divided into several bands. The wavelengths shorter than 0.4 microns are called ultraviolet bands, those from 0.4 microns to 0.78 microns are called visible light bands, and electromagnetic waves with wavelengths in the range of 0.78-1000 μm are called infrared rays. In visible light, there is a kind of high-energy visible light-blue light. Blue light is the part of visible light closest to ultraviolet light with the highest energy. It accounts for 60% of white light. Its wavelength is between 380-500nm. Chronically exposed to blue light, the pigments in the cells will promote the reaction of phototoxins, and the retinal cells are more likely to be damaged. Blue light will pass through the cornea and lens and touch the retina. Blue light will accelerate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): G02B5/22C09J4/02C09J4/06C09J11/06C09J11/04
CPCG02B5/223C09J4/06C09J11/04C09J11/06
Inventor 张佳斌
Owner NINGBO XIAYUAN TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap