A kind of high carbon steel slab continuous casting method

A slab continuous casting, high-carbon steel technology, applied in the field of iron and steel smelting, can solve the problems of corner crack center segregation level, surface depression of high carbon steel, etc., to improve the center segregation level, reduce stress, and enhance solidification uniformity. Effect

Active Publication Date: 2018-06-26
SHOUGANG CORPORATION
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention solves the technical problems of high carbon steel surface depression, corner cracks and low center segregation level in the prior art by providing a high carbon steel slab continuous casting method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] In order to solve the technical problems of high carbon steel surface depression, corner cracks and low center segregation level in the prior art, the invention provides a high carbon steel slab continuous casting method.

[0019] In order to make the purpose, technical solutions and advantages of the embodiments of the present invention clearer, the technical solutions in the embodiments of the present invention are clearly and completely described. Obviously, the described embodiments are part of the embodiments of the present invention, not all of them. example. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without creative efforts fall within the protection scope of the present invention.

[0020] An embodiment of the present invention provides a high carbon steel slab continuous casting method, the method comprising:

[0021] Step 101: The superheat degree of high carbon steel slab casting...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of steel and iron smelting, in particular to a continuous casting method of a high-carbon steel plate blank. The method comprises the following steps: the casting superheat degree of the high-carbon steel plate blank is controlled within 10-20 DEG C by low superheat degree; the low-pulling-speed continuous casting is performed for the high-carbon steel plate blank, and the pulling speed is controlled within 0.9-1.1 m / min; the aerial fog cooling is performed for the high-carbon steel plate blank; the taper of a crystallizer is controlled according to variable taper, wherein the alkalinity of covering slag in the crystallizer is controlled within 0.93-0.99; the melting point of the covering slag is not higher than 1050 DEG C; and the viscosity of the covering slag is not higher than 0.140 pa.s. The method reduces the large surface and angle stress, enhances the solidification uniformity of a blank shell, reduces the surface crack generation rate of the plate blank, and improves the center segregation level.

Description

technical field [0001] The invention relates to the technical field of iron and steel smelting, in particular to a high-carbon steel slab continuous casting method. Background technique [0002] High-carbon steel is often used to manufacture mechanical equipment such as gears, springs, and saw blades. The banded structure in high-carbon steel is different from the deformation of the steel matrix, and forms a source of fatigue damage under the action of alternating stress, and the banded structure is usually related to the The slab center segregation is closely related. The high carbon steel slab center segregation level in the prior art is often low. Therefore, the workpiece is subjected to periodic alternating stress during service, which is prone to fatigue damage, which leads to the failure of the workpiece, and , Surface depressions and corner cracks appear in high carbon steel slabs. [0003] In addition, due to the relatively high carbon content and relatively low liq...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22D11/16B22D11/18B22D11/22
Inventor 刘国梁马文俊罗衍昭刘阳春陈斌包春林李海波崔阳倪有金马威
Owner SHOUGANG CORPORATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com