Low hysteresis compound composition for axle box rubber spring and preparation method thereof

The technology of rubber spring and hysteresis glue is applied in the field of low hysteresis rubber compound composition for axle box rubber spring and its preparation field. Low structure and the effect of reducing hysteresis

Active Publication Date: 2018-01-30
CRRC QINGDAO SIFANG ROLLING STOCK RES INST +1
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, ordinary furnace carbon black has small particle size and large structure, and when added to rubber, it will form unstable physical cross-linking, resulting in "pany effect" and increasing the hysteresis performance of the rubber compound.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low hysteresis compound composition for axle box rubber spring and preparation method thereof
  • Low hysteresis compound composition for axle box rubber spring and preparation method thereof
  • Low hysteresis compound composition for axle box rubber spring and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A low-hysteresis compound for an axle box rubber spring, the composition of its main raw materials and the ratio of parts by mass are as follows: 100 parts of deproteinized natural rubber (DPNR); 80 parts of medium particle thermal cracking carbon black N990; 3 parts of anti-aging agent RD; 1.5 parts of anti-aging agent BLE; 5 parts of zinc oxide; 2 parts of stearic acid; 2.5 parts of sulfur; 1.5 parts of accelerator CBS; 1.5 parts of accelerator NOBS.

[0034] Among them, the particle size of medium particle thermal carbon black is 280nm, the specific surface area of ​​CTAB method is 9m2 / g, and the oil absorption value of DBP is 0.40cm3 / g.

[0035] The rubber material for traditional axle box rubber springs, its main raw material composition and mass ratio are: 100 parts of natural rubber; 35 parts of carbon black N550; 3-5 parts of aromatic oil; 6-10 parts of anti-aging agent RD; 3-5 parts of anti-aging agent BLE 3-10 parts of zinc oxide; 1-5 parts of stearic acid; 1-...

Embodiment 2

[0050] A low-hysteresis rubber compound for axle box rubber springs, the composition and mass ratio of its main raw materials are: 100 parts of deproteinized natural rubber (DPNR); 60 parts of medium-sized thermal cracking carbon black; 2 parts of anti-aging agent RD; anti-aging agent BLE 1 part; 3 parts of zinc oxide; 1.2 parts of stearic acid; 1 part of sulfur; 2.3 parts of accelerator CBS; 2.3 parts of accelerator NOBS.

[0051] Among them, the particle size of medium particle thermal carbon black is 280nm, and the specific surface area of ​​CTAB method is 9m 2 / g, DBP oil absorption value is 0.40cm 3 / g.

[0052] The preparation method is as described in Example 1

[0053] Traditional axle box rubber spring compound, its main raw material composition and mass ratio are: 100 parts of natural rubber; 27 parts of carbon black N550; 3-5 parts of aromatic oil; 6-10 parts of anti-aging agent RD; 3-5 parts of anti-aging agent BLE 3-10 parts of zinc oxide; 1-5 parts of stearic ...

Embodiment 3

[0061] A low-hysteresis rubber compound for axle box rubber springs, the main raw material composition and mass ratio are: 100 parts of deproteinized natural rubber (DPNR); 100 parts of medium particle thermal black; 4 parts of anti-aging agent RD; anti-aging agent BLE 2 parts; 10 parts of zinc oxide; 4 parts of stearic acid; 5 parts of sulfur; 0.5 parts of accelerator CBS; 0.5 parts of accelerator NOBS.

[0062] The preparation method is as described in Example 1

[0063] Traditional axle box rubber spring compound, its main raw material composition and mass ratio are: 100 parts of natural rubber; 45 parts of carbon black N550; 3-5 parts of aromatic oil; 6-10 parts of anti-aging agent RD; 3-5 parts of anti-aging agent BLE 3-10 parts of zinc oxide; 1-5 parts of stearic acid; 1-10 parts of sulfur; 0.5-3 parts of accelerator TMTD; 1-4.5 parts of accelerator NOBS.

[0064] The basic properties of the rubber material of the present invention and the traditional rubber material ar...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention relates to journal box rubber, in particular to a low-hysteresis rubber composition for journal box rubber springs and a preparation method of the low-hysteresis rubber composition. The rubber composition comprises, by weight, 100 parts of deproteinized natural rubber (DPNR), 60-100 parts of intermediate-particle heat cracked carbon black N990, 3-6 parts of antiager, 4.2-14 parts of activator, 1-5 parts of sulfur and 1-4.6 parts of accelerant. According to the formula, high-purity DPNR is taken as raw rubber, and the intermediate-particle heat cracked carbon black N990 with large particle size, low structure degree and high purity is taken as a reinforcing filler; thus, on the basis of the reasonable optimized matching, hysteresis property of the rubber composition and product is reduced effectively on the premise of maintaining property of the rubber composition for making the journal box rubber springs.

Description

technical field [0001] The invention relates to an axle box rubber spring, in particular to a low-hysteresis compound composition for an axle box rubber spring and a preparation method thereof. Background technique [0002] Axlebox springs are the main axlebox positioning method adopted by urban rail transit vehicles in my country. The axlebox springs are respectively installed between the axlebox and the frame. Each axlebox has two conical laminated rubber springs, which are respectively installed on both sides of the axlebox. . Axlebox rubber springs (also known as "primary springs") are important components on subway vehicle bogies, used to damp vibration and guide wheelsets safely and reliably. This structure provides flexible support and positioning for the bogie frame, and transmits the lateral, longitudinal and vertical forces from the wheel set to the bogie frame, so that the axle box can achieve no gap and no wear in the three directions elastic positioning. Since...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L7/00C08K13/02C08K3/04C08K3/22C08K3/06C08K5/09
CPCC08K3/04C08K3/06C08K3/22C08K5/09C08K13/02C08K2003/2296C08K2201/003C08K2201/006C08L7/00
Inventor 张波高新文王付胜
Owner CRRC QINGDAO SIFANG ROLLING STOCK RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap