A technology of acrylic resin and resin emulsion, applied in the direction of coating, etc., can solve the problems of reducing the viscosity of the system, reducing the solid content of the coating, and reducing the gloss

Active Publication Date: 2016-08-10
LANGFANG JINHUILI INDAL PAINT
View PDF5 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The anti-sagging performance of water-based coatings is a very important performance in the process of construction and film formation. If this performance is poor, it will lead to the aesthetics and continuity of the coating on the surface of the object, resulting in the failure of coating protection and aesthetic performance.
At present, the main way to improve the sag resistance of water-based paints is to add various types of thickeners to change the rheologic

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Microgel aqueous acrylic acid shell-core resin emulsion and preparation method thereof
  • Microgel aqueous acrylic acid shell-core resin emulsion and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] The material ratio is as follows

[0023]

[0024] The experimental equipment used in the present invention is a constant temperature water bath, a four-necked bottle, a dropping funnel, and a spherical condenser. Pure water (1) and acrylic acid aqueous dispersion (1) are put into the four-necked bottle, and the stirring is started and the temperature is raised; at the same time Pure water (2), acrylic acid aqueous dispersion (2) and all acrylic acid monomers and vinyl monomers are uniformly stirred and mixed as emulsified monomer mixture components; initiator and solvent are stirred and mixed uniformly as initiator components for later use. Raise the temperature to 80°C±2°C and keep it. At this temperature, use two dropping funnels to add the emulsified monomer mixture component and the initiator component dropwise to the four-necked bottle at the same time, and drop them simultaneously for 4-6hr Complete, heat preservation 1hr cooling discharge. The technical indi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the field of aqueous coatings, and relates to a microgel aqueous acrylic acid shell-core resin emulsion. The resin emulsion is prepared through a reaction of 13-16 parts of an acrylic acid resin water dispersion (with the solid content of 28-34%), 18-21 parts of a vinyl monomer, 20.5-27.6 parts of an acrylic acid and acrylate monomer, 0.3-0.6 parts of an initiator, 5-6 parts of an organic solvent and 49-53 parts of water. The microgel resin emulsion is added to an aqueous coating, so the sagging property of a paint film is obviously improved, a good anti-sagging effect is reached, the thickness of the paint film in closed angles or edges and other difficult coating positions of a coated member is obviously increased, and the corrosion resistance of the surface of the coated member is improved. The nanometer-level aqueous acrylic acid emulsion with the particle size being smaller than 150nm is produced through the method, can be added to the aqueous coating without thickening the coating, and facilitates maintenance of high construction solid content.

Description

technical field [0001] The invention relates to a microgel water-based acrylic shell-core resin emulsion and a preparation method thereof, belonging to the field of water-based paints. Background technique [0002] Water-based coatings use water instead of solvents, which can greatly reduce VOC emissions from about 70% of solvent-based paints to less than 15%. Its environmental acceptability is much higher than that of solvent-based paints, and it saves oil. resources, reduce fire hazards, and improve the operating environment. [0003] The anti-sagging performance of water-based coatings is a very important performance in the process of construction and film formation. If this performance is poor, it will lead to the aesthetics and continuity of the coating on the surface of the object, resulting in the failure of coating protection and aesthetic performance. . At present, the main way to improve the sag resistance of water-based paints is to add various types of thickene...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F265/06C08F220/14C08F220/18C08F212/08C08F222/14C08F220/32C09D7/12
CPCC08F265/06C09D7/65C09D7/67C09D7/68C08F220/14
Inventor 秦文方秀莲王英
Owner LANGFANG JINHUILI INDAL PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap