Highly anticorrosive epoxy coating and preparation method thereof

A technology of epoxy coatings and water-based epoxy resins, applied in anti-corrosion coatings, epoxy resin coatings, coatings, etc., can solve problems such as obvious odor, flammability and explosion, and high VOC content

Inactive Publication Date: 2018-12-11
牛宝芬
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, our container epoxy interior paint is a solvent-based two-component coating, which has high VOC content, obvious odor during construction, flammability and explosion, etc. The development of strong anti-corrosion epoxy coatings can solve many of the above problems Easy to solve

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A kind of strong anticorrosion paint, is made up of following raw materials in parts by weight:

[0032] 30 parts of water-based epoxy resin;

[0033] 0.5 part of 2,4-dihydroxybenzophenone;

[0034] 0.5 part of pH regulator;

[0035] 0.5 parts of sodium dioctylsulfosuccinate;

[0036] 60 parts of deionized water;

[0037] 5 parts of propylene glycol butyl ether;

[0038] 10 parts of water-based fatty amine curing agent.

[0039] A kind of preparation method of described strong anticorrosion paint is characterized in that, described preparation method is:

[0040] (1) Weigh the corresponding raw materials according to the formula;

[0041] (2) Add water-based epoxy resin to the mixer, then add deionized water to dilute, stir for 10~20min, and add wetting and dispersing agent;

[0042] (3) Add glass beads to the mixture, perform high-dispersion grinding for 60-90 minutes, and filter with a 200-mesh filter;

[0043] (4) Add UV absorber, light stabilizer, film-formi...

Embodiment 2

[0045] A kind of strong anticorrosion paint, is made up of following raw materials in parts by weight:

[0046] 40 parts of water-based epoxy resin;

[0047] 5 parts of titanium dioxide, 5 parts of superfine talcum powder;

[0048] 1 part of 2,4-dihydroxybenzophenone;

[0049] 1 part of pH regulator;

[0050] 0.1 part of sodium dioctyl sulfosuccinate;

[0051] 40 parts of deionized water;

[0052] 5 parts of propylene glycol methyl ether acetate;

[0053] 15 parts of water-based fatty amine curing agent.

[0054] A kind of preparation method of described strong anticorrosion paint is characterized in that, described preparation method is:

[0055] (1) Weigh the corresponding raw materials according to the formula;

[0056] (2) Add water-based epoxy resin to the mixer, then add deionized water to dilute, stir for 10~20min, and add wetting and dispersing agent;

[0057] (3) Add glass beads to the mixture, perform high-dispersion grinding for 60-90 minutes, and filter wit...

Embodiment 3

[0060] A kind of strong anticorrosion coating, described strong anticorrosion coating is made up of following raw materials in parts by weight:

[0061] 38 parts of water-based epoxy resin;

[0062] 0.8 parts of 2,4-dihydroxybenzophenone;

[0063] 0.4 parts of pH regulator;

[0064] 0.4 parts of sodium dioctylsulfosuccinate;

[0065] 50 parts of deionized water;

[0066] 3 parts of propylene glycol butyl ether, 4 parts of propylene glycol methyl ether acetate;

[0067] 6 parts of water-based fatty amine curing agent.

[0068] A kind of preparation method of described strong anticorrosion paint is characterized in that, described preparation method is:

[0069] (1) Weigh the corresponding raw materials according to the formula;

[0070] (2) Add water-based epoxy resin to the mixer, then add deionized water to dilute, stir for 10~20min, and add wetting and dispersing agent;

[0071] (3) Add glass beads to the mixture, perform high-dispersion grinding for 60-90 minutes, an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of coatings and in particular discloses a highly anticorrosive epoxy coating. The highly anticorrosive epoxy coating is composed of the following raw materials: aqueous epoxy resin, a UV (Ultraviolet) absorbent, a light stabilizer, a pH adjuster, wetting dispersant 0.1-0.5 part, deionized water, a coalescing agent and an aqueous fatty amine curing agent. The highly anticorrosive paint has good construction performance, strong adhesion to metal, extremely low irritation and no emission of VOC (Volatile Organic Compounds), and is environment-friendly.

Description

technical field [0001] The invention relates to the field of heavy-duty anti-corrosion coatings, in particular to a strong anti-corrosion epoxy coating and a preparation method thereof. Background technique [0002] With the development of modern society, the improvement of human living standards, the gradual awakening of energy conservation and environmental protection awareness, and the rapid development of polymer science, the requirements for environmental protection are becoming more and more stringent. [0003] With the formulation of the local standard of Guangdong Province "Volatile Organic Compound Emission Standards for Container Manufacturing Industry", and the national taxation department levying consumption tax on paint products with high VOC content; the comprehensive water-based coating of containers is becoming more and more urgent. [0004] It can be foreseen that for a long time in the future, the development of environmentally friendly water-based coatings...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D163/00C09D5/08C09D7/63
CPCC09D163/00C09D5/08C09D7/63C08K5/132
Inventor 牛宝芬
Owner 牛宝芬
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap