Self-cleaning antibacterial spread-type sisal hemp fabric

A technology of sisal and fabrics, applied in textiles and papermaking, etc., to achieve good self-cleaning and antibacterial properties and improve the quality of use

Inactive Publication Date: 2016-08-10
JIANGYIN HARVEST KNITTING & GARMENTS
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The world's sisal import and export trade is constantly growing, but China's current self-produced sisal fiber cannot meet domestic needs, and with the continuous increase in the use of sisal fiber, China is increasing its imports of sisal fiber every year

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] The self-cleaning antibacterial sisal fabric fabric is to decorate a layer of functional coating on the outer surface of the sisal base cloth by scraping. The preparation of the coating slurry involved in the functional coating is to mix coating glue, silane, Add nano-silver and cross-linking agent to the pulping tank, stir evenly, adjust the pH to 8 with ammonia water, let it stand for 2-4 hours, then apply it to the surface of the sisal base cloth by scraping, and dry it at 80°C 0.5 hours, cured at 120°C for 1.5 hours, and finally balanced under natural conditions for more than 8 hours.

[0011] The weave structure of the sisal base cloth in this embodiment is a 1 / 2 twill weave structure.

[0012] The sisal fabric fabric obtained in this embodiment has good self-cleaning and antibacterial properties.

Embodiment 2

[0014] The self-cleaning antibacterial sisal fabric fabric is to decorate a layer of functional coating on the outer surface of the sisal base cloth by scraping. The preparation of the coating slurry involved in the functional coating is to mix coating glue, silane, Add nano-silver and cross-linking agent to the pulping tank, stir evenly, adjust the pH to 7.5 with ammonia water, let it stand for 2-4 hours, then apply it to the surface of sisal base cloth by scraping, and bake it at 80°C Dry for 0.5 hours, cure at 130°C for 1 hour, and finally balance under natural conditions for more than 8 hours.

[0015] The structure of the sisal base cloth in this embodiment is a broken twill structure.

[0016] The sisal fabric fabric obtained in this embodiment has good self-cleaning and antibacterial properties.

Embodiment 3

[0018] The self-cleaning antibacterial sisal fabric fabric is to decorate a layer of functional coating on the outer surface of the sisal base cloth by scraping. The preparation of the coating slurry involved in the functional coating is to mix coating glue, silane, Add nano-silver and cross-linking agent to the pulping tank, stir evenly, adjust the pH to 8.5 with ammonia water, let it stand for 2-4 hours, then apply it to the surface of the sisal base cloth by scraping, and bake it at 80°C Dry for 0.5 hours, cure at 120°C for 1 hour, and finally balance under natural conditions for more than 8 hours.

[0019] The tissue structure of the sisal base cloth in this embodiment is five pieces of satin weave structure.

[0020] The sisal fabric fabric obtained in this embodiment has good self-cleaning and antibacterial properties.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a self-cleaning and antibacterial scraping-coated sisal fabric fabric, which is to decorate a layer of functional coating on the outer surface of the sisal base cloth by scraping coating, and the coating slurry involved in the functional coating is The preparation is to add the coating glue, silane, nano-silver and cross-linking agent into the pulping tank, stir evenly, adjust the pH to 7.5-8.5 with ammonia water, let it stand for 2-4 hours, and then apply it to the sword by scraping On the surface of the linen base cloth, dry at 80°C for 0.5 hours, cure at 120-135°C for 1-1.5 hours, and finally balance under natural conditions for more than 8 hours. After the surface of the sisal fabric is protected by the coating material, the fabric has better self-cleaning and antibacterial properties, which improves the quality of the fabric.

Description

technical field [0001] The invention belongs to the technical field of sisal fabric fabrics, in particular to a self-cleaning and antibacterial scratch-coated sisal fabric fabric. Background technique [0002] Sisal fiber is tough, wear-resistant, salt-alkali-resistant, and corrosion-resistant. It is widely used in various industries such as transportation, fishery, petroleum, and metallurgy, and has important economic value. The world's sisal import and export trade is constantly growing, but China's current self-produced sisal fiber cannot meet domestic needs, and with the continuous increase in the use of sisal fiber, China is increasing its imports of sisal fiber every year. At the same time, sisal also has important medicinal value, and the application of sisal in fabrics has gradually attracted the attention of the market. It is the development trend of sisal fabrics to continuously develop new functions of sisal fabrics. Contents of the invention [0003] The purpo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06N3/00
CPCD06N3/0006D06N3/0015D06N3/0061D06N3/0063D06N3/0088D06N2201/045D06N2209/1671
Inventor 展平
Owner JIANGYIN HARVEST KNITTING & GARMENTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com