A kind of concrete with c220 strength grade for steel-concrete composite structure
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of strength grade and combined structure, applied in the field of building materials, can solve problems such as poor natural bonding performance, and achieve the effect of improving construction efficiency, significant economic benefits, and reducing construction procedures
Inactive Publication Date: 2017-11-10
XI'AN UNIVERSITY OF ARCHITECTURE AND TECHNOLOGY
View PDF5 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0005] The strength grades of concrete used for steel-concrete composite structures in the prior art include low-strength high-performance concrete of C30, C35, C40, C45, C50 and C55, high-strength high-performance concrete of C60, C70, C80, C90 and C100, and C110, C120, C130, C140, and C150 ultra-high-strength high-performance concrete, as well as the preparation technology of C160, C170, C180, C190, and C200 ultra-high-strength high-performance concrete. ) between the high-strength concrete, and improve the durability of the structure; however, there are still ultra-high-strength high-performance concrete that cannot be extended to higher strength, and when it is used in steel-concrete composite structures, it cannot solve the problem of steel The problem of poor natural bonding performance with ultra-high-strength and high-performance concrete, so it cannot meet the requirements of civil engineering buildings extending to the air, underground and water, that is, super / ultra-high buildings, super / ultra-large spans, underground, sea or Underwater, ultra-durable and heavy, giant and novel structural engineering and other applications and development trends
In addition, in the prior art, there are also some preparation technologies for super / ultra-high strengthening and super / ultra-durability of concrete, but none of them involve or solve the natural relationship between section steel and ultra-high-strength high-performance concrete when used in SRC structures. The problem of poor bonding performance
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment
[0069] (1) Raw materials
[0070] 1. Cement
[0071] Select Qinling brand P·Ⅰ62.5R cement with stable quality and good performance, and conduct an adaptability test with polycarboxylate concrete high-performance water reducer before use. The test method adopts the current building materials industry standard "Cement and The method in JC / T 1083-2008 Compatibility Test Method of Water Reducer has good compatibility with polycarboxylate concrete high performance water reducer. The performance indicators of the selected cement meet the requirements of current relevant national standards such as "Portland Cement and Ordinary Portland Cement" GB175-2007. It has low alkali content, low heat of hydration, and low water demand.
[0072] 2. Aggregate
[0073] Use sand and quartz sand with a mass ratio of 8:2.
[0074] The sand is medium-to-coarse and Bahe sand with smooth particles, hard texture, and good gradation. The quality of the sand conforms to the current building material in...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
compressive strength
aaaaa
aaaaa
specific surface area
aaaaa
aaaaa
specific surface area
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses concrete of a strength grade C220 for a steel reinforced concrete combined structure. The concrete comprises cement, fine aggregate, coarse aggregate, water, a water reducing agent, a defoaming agent, silicon powder, coal ash, an excitant, an expanding agent and a composite plastic retaining agent in a ratio of 488:742:1262:97.6:19.7:1.2:96:120:10:50:0.50. A preparation method comprises the following steps: firstly, uniformly mixing the water reducing agent, the excitant and the composite plastic retaining agent with water so as to obtain a mixture, sequentially adding the fine aggregate, the coarse aggregate and 1 / 3 of the mixture into a stirrer according to a weight ratio, adding the coarse aggregate and 1 / 3 of the mixture, uniformly mixing, adding the cement, the expanding agent, the silicon ash and the coal ash, uniformly mixing, adding the defoaming agent and the rest mixture, stirring, and discharging, thereby obtaining the concrete. By adopting the concrete, the bonding property of steel and concrete can be remarkably improved in a natural state, respective mechanical properties and mutual synergetic working properties of the steel and the concrete can be effectively taken into play, the bearing property, the use performance and the durability of a structural component can be greatly improved, and good volume stability and economy can be achieved.
Description
technical field [0001] The invention belongs to the technical field of building materials, and relates to an ultra-high-strength and high-performance concrete with a strength grade of C220 for steel-concrete composite structures. Background technique [0002] The invention of Portland cement in 1824 led to the rapid development of concrete technology. Its consumption is large and its scope of application ranks the highest in the world. Although concrete is a traditional man-made building material, because of its irreplaceable advantages (abundant raw materials, simple production process, high cost performance, etc.) and the continuous progress of concrete material science and technology, concrete has become the main body of civil engineering materials. , It will also be one of the indispensable main materials in future civil engineering and national construction. At the same time, with the continuous expansion of the city, the continuous increase of the population, the cont...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.