Ecological environment-friendly putty paste

A putty paste, an environmentally friendly technology, applied in the field of building decoration materials, to achieve strong bonding and bending resistance, good market application prospects, and enhanced cross-linking effect

Inactive Publication Date: 2016-09-07
杭州唯曦科技有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide an eco-friendly putty paste that is green, environment-friendly, easy to construct, high in strength, and does not peel or lose powder, aiming at the problems existing in the current putty.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] 10 parts of desulfurized gypsum, 55 parts of white cement, 8 parts of aluminum silicate fiber with a diameter of 1-4 μm, 5 parts of modified plant fiber, 8 parts of negative ion powder, 20 parts of sodium alginate, 45 parts of water, weighed according to the above ratio Take each component, first add a sufficient amount of water into the putty paste mixing tank, start the mixer, add white cement, desulfurized gypsum, sodium silicate fiber, modified plant fiber, sodium alginate and negative ion powder in turn, at a speed of 1000r Stir at 1 / min for 30 minutes, fully stir evenly, turn off the stirrer and let stand for 10-15 minutes and stir again for 3-5 minutes to obtain the finished product.

Embodiment 2

[0036] 8 parts of desulfurized gypsum, 60 parts of white cement, 6 parts of aluminum silicate fiber with a diameter of 1-4 μm, 4 parts of modified plant fiber, 5 parts of negative ion powder, 15 parts of sodium alginate, 40 parts of water, weighed according to the above ratio Take each component, first add a sufficient amount of water into the putty paste mixing tank, start the mixer, add white cement, desulfurized gypsum, sodium silicate fiber, modified plant fiber, sodium alginate and negative ion powder in turn, at a speed of 1000r Stir at 1 / min for 30 minutes, fully stir evenly, turn off the stirrer and let stand for 10-15 minutes and stir again for 3-5 minutes to obtain the finished product.

Embodiment 3

[0038] 12 parts of desulfurized gypsum, 40 parts of white cement, 10 parts of aluminum silicate fiber with a diameter of 1-4 μm, 8 parts of modified plant fiber, 10 parts of negative ion powder, 25 parts of sodium alginate, 45 parts of water, weighed according to the above ratio Take each component, first add a sufficient amount of water into the putty paste mixing tank, start the mixer, add white cement, desulfurized gypsum, sodium silicate fiber, modified plant fiber, sodium alginate and negative ion powder in turn, at a speed of 1000r Stir at 1 / min for 30 minutes, fully stir evenly, turn off the stirrer and let stand for 10-15 minutes and stir again for 3-5 minutes to obtain the finished product.

[0039] Before construction, oil stains, floating ash, dirt and other substances on the surface of the substrate should be removed to ensure that the surface of the substrate is clean. In order to avoid the surface of the substrate being too dry and causing water absorption to the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a building decoration material, in particular to ecological environment-friendly putty paste. The ecological environment-friendly putty paste comprises, by weight, 8-12 parts of desulfurized gypsum, 40-60 parts of white cement, 5-10 parts of aluminum silicate fibers, 3-8 parts of modified plant fibers, 5-10 parts of negative ion powder, 15-25 parts of sodium alginate and 35-45 parts of water. The ecological environment-friendly putty paste has the advantages of environment friendliness, environment optimization, easiness in construction, high strength, avoidance of scaling and powder shedding, simplicity in use method and the like, thereby being promising in market application prospect.

Description

technical field [0001] The invention relates to a building decoration material, in particular to an ecological environment-friendly putty paste. Background technique [0002] As we all know, architectural coatings have become the first choice for indoor and outdoor wall decoration of buildings, and the architectural putty used in conjunction with it has also become an indispensable and important auxiliary material for building wall decoration. In the past, the use of putty used liquid glue On-site deployment and use, so due to the different configuration conditions and deployment personnel, the quality of the prepared putty is quite different, and it is easy to cause instability in the quality of the putty. After coating, poor water resistance, low bonding strength, and poor adhesion are common. , easy peeling, pulverization and other problems. Now, most people use powder putty, which can be used only by mixing the powder putty with water in a certain proportion. This kind ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D5/34
CPCC09D5/34
Inventor 赵小琴
Owner 杭州唯曦科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap