Paint for electric irons, and preparation and application method thereof

A technology for electric irons and coatings, which is applied in the direction of fireproof coatings, epoxy resin coatings, coatings, etc., which can solve the problems of scratch resistance, insufficient hardness, and easy paint peeling, etc., and achieve excellent moisture resistance, smooth surface, and good The effect of hardness

Active Publication Date: 2016-11-09
CHINA PAINT MFG CO SHENZHEN
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The object of the present invention is to provide a coating for electric irons and a preparation method thereof, so as to solve the problem that the existing baking paint for electric irons has insufficient hardness after baking at a temperature lower than 160°C, and cannot meet the requirement of high thermal hardness at 120°C and below, and Easy to drop paint, not resistant to scratches and wear, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Paint for electric irons, and preparation and application method thereof
  • Paint for electric irons, and preparation and application method thereof
  • Paint for electric irons, and preparation and application method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0029] Correspondingly, on the basis of providing the formulation of the paint for electric iron, the embodiment of the present invention also provides a preparation method of the paint for electric iron. In an embodiment, the preparation method of the coating for an electric iron at least includes the following steps: weighing acrylic resin, amino resin, epoxy resin, sealed curing agent, toner, auxiliary agent (auxiliary agent includes Dispersants, anti-settling agents, leveling agents, adhesion promoters) and organic solvents;

[0030] Mixing the weighed organic solvent, acrylic resin, dispersant, anti-sedimentation agent, and toner to obtain the first material;

[0031] Grinding the first material;

[0032] adding the amino resin, closed curing agent, and epoxy resin to the first material in sequence, and performing mixing treatment to obtain a second material;

[0033] Add the leveling agent and the adhesion promoter into the second material, and adjust the viscosity.

...

Embodiment 1～3

[0041] In order to save space, the weight percentages of the raw material formulations of Examples 1 to 3 are listed in Table 1, specifically as follows.

[0042] Table 1 embodiment 1~3 each formula component weight percent (unit: %)

[0043]

[0044]

[0045] The preparation process of above-mentioned each embodiment coating is:

[0046] The first material is obtained by first mixing part of the organic solvent with the acrylic resin, dispersant, anti-sedimentation agent, and toner;

[0047] Grinding the first material so that the particles of the first material are 10 microns or less;

[0048] adding amino resin, closed curing agent, and epoxy resin to the ground first material, and mixing to obtain the second material;

[0049] Add the leveling agent and the adhesion promoter into the second material, and use the remaining organic solvent to adjust the viscosity of the paint to obtain the paint for electric irons in various embodiments.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a paint for electric irons, and a preparation and application method thereof. The paint at least comprises the following components in percentage by weight: 40-60% of acrylic resin, 12-19% of amino resin, 0-5% of epoxy resin, 3-5% of enclosed-type curing agent, 0-28% of toner, 2-5% of aid and 8-20% of organic solvent. The content of the epoxy resin is not 0. The paint is a single-component acrylic amino baking varnish, and has the advantages of favorable spraying effect, smooth surface, high gloss and uniform color. More importantly, the paint film formed by drying at the temperature of lower than 160 DEG C has favorable hardness, and especially can still have higher hot hardness, favorable adhesion to the substrate, excellent damp heat resistance and excellent wear resistance in a 120-DEG C environment.

Description

technical field [0001] The invention relates to the technical field of acrylic amino baking varnish, in particular to a coating for an electric iron and a preparation method and application method thereof. Background technique [0002] There are two main types of existing electric iron coatings: the first type of electric iron coating is suitable for baking varnish coatings of original iron-based materials. Since the paint film needs to meet higher physical property requirements, this type of coating needs to be used in the film-forming process. Baking at a high temperature exceeding 180°C, if the material of modern bakelite or bulk molding compound (also known as unsaturated polyester bulk film plastic; English: Bulk molding compounds; English abbreviation: BMC) is at this temperature for a long time, it will produce As a result, these two materials cannot meet the original process requirements. The second type of paint for electric irons is baking varnish baked at a tempe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D161/32C09D163/00C09D7/00
CPCC08L2201/08C08L2205/03C09D5/18C09D7/20C09D133/00C08L61/32C08L63/00
Inventor 阮志明王烁吴晓斌
Owner CHINA PAINT MFG CO SHENZHEN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com