Wave absorbing coating and preparation method thereof

A technology of wave absorbing paint and wave absorbing material, which is applied in the field of paint, can solve the problems of affecting the aesthetics of the appearance design of cooking utensils, unfavorable user experience, inability to meet the needs of use, etc., and achieves low cost and improved temperature rise effect. , the effect of good temperature rise effect

Inactive Publication Date: 2016-11-16
GUANGDONG MIDEA KITCHEN APPLIANCES MFG CO LTD +1
View PDF5 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] 2. Thick wave-absorbing patches affect the appearance design of cooking utensils and the aesthetics of products
The resulting problem: the thickness of the wave-absorbing sheet is not conducive to the appearance design of the product, nor is it conducive to the user experience
Especially for some baking pans with special shapes or structures, thicker coatings cannot meet the needs of use
If the coating is thicker, problems such as poor adhesion, low strength, and high cost will also occur

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wave absorbing coating and preparation method thereof
  • Wave absorbing coating and preparation method thereof
  • Wave absorbing coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0068] A wave-absorbing paint, the various components of the paint are calculated by mass percentage, the wave-absorbing material binder is 98%, the wave-absorbing material is 1.5%, and the auxiliary agent is 0.5%. The particle diameter of the absorbing material is 15nm.

[0069] The preparation method is as follows:

[0070] 1) Preparation of additives and binder mixing components:

[0071] Mix 98kg liquid ceramic material with 0.5kg additives; additives include 0.3kg dispersion coupling agent BL-20N, 0.1kg defoamer BYK-055 and 0.1kg dispersant Efka Polymer 452, mechanically stir at 400r / min for 10min to Mix evenly to obtain a mixed solution;

[0072] 2) Preparation of absorbing coating:

[0073] Add 1 kg of graphene oxide and 0.5 kg of silicon carbide whisker wave-absorbing powder to the mixed solution prepared in step 1), and mechanically stir at a speed of 800 r / min for 15 minutes until all components are evenly mixed to obtain the wave-absorbing coating of the present ...

Embodiment 2

[0075] A wave-absorbing coating, the various components of the coating are calculated by mass percentage, the wave-absorbing material binder is 98%, the wave-absorbing material is 1%, and the auxiliary agent is 1%. The particle diameter of the absorbing material is 25nm.

[0076] The preparation method is as follows:

[0077] 1) Preparation of additives and binder mixing components:

[0078] Mix 98kg of liquid ceramic material with 1kg of additives, including 0.6kg of dispersion coupling agent BL-20N, 0.1kg of defoamer BYK-055 and 0.3kg of dispersant Efka Polymer 452, and mechanically stir at 400r / min for 10min until mixed homogeneously to obtain a mixture;

[0079] 2) Preparation of absorbing coating:

[0080] Add 1 kg of graphene oxide wave-absorbing powder to the mixed solution prepared in step 1), and mechanically stir at a speed of 900 r / min for 15 minutes until all components are evenly mixed, and then the wave-absorbing coating of the present invention can be obtaine...

Embodiment 3

[0082] A wave-absorbing paint, the various components of the paint are calculated by mass percentage, the wave-absorbing material binder is 95%, the wave-absorbing material is 3.5%, and the auxiliary agent is 1.5%. The particle diameter of the absorbing material is 100nm.

[0083] The preparation method is as follows:

[0084] 1) Preparation of additives and binder mixing components:

[0085] Mix 95kg of liquid ceramic material with 1.5kg of additives, including 0.9kg of dispersion coupling agent BL-20N, 0.2kg of defoamer BYK-055 and 0.4kg of dispersant Efka Polymer 452, and mechanically stir at 600r / min for 10min until evenly mixed to obtain a mixed solution;

[0086] 2) Preparation of absorbing coating:

[0087] Add 0.4kg of graphene oxide, 1.1kg of SiC whiskers and 2kg of TiC wave-absorbing powder to the mixed solution prepared in step 1), and mechanically stir at a speed of 1000r / min for 15min until all components are mixed evenly to obtain this product. Invented absor...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a wave absorbing coating and a preparation method thereof. The wave absorbing coating is prepared from, in percentage by mass, 88%-98% of a wave absorbing material adhesive, 1%-10% of a wave absorbing material and 0.5%-2% of an aid. During preparation, all components are mixed in proportion. The wave absorbing coating has the advantages of thin coating, good adhesion capability, high strength, good heat conducting property, low cost and the like.

Description

technical field [0001] The invention belongs to the technical field of coatings, in particular to a wave-absorbing coating and a preparation method thereof. Background technique [0002] With the gradual change of diet structure, people are more and more inclined to use microwave ovens to cook food. Pizza, barbecue, and baked food are among the more popular foods. If you want to achieve good color, crispness, and taste, etc. Requirements, the absorbing material for cooking utensils is a key factor. [0003] Most of the microwave-absorbing materials used in the baking trays of existing microwave ovens or microwave ovens are to mix and disperse the microwave-absorbing powder in the resin, and solidify it on the surface of the metal or ceramic plate through high temperature to form a layer of microwave-absorbing material of about 2 mm, so as to achieve The baking pan absorbs microwave energy to achieve the purpose of baking and grilling food. However, the microwave baking pan...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/00C09D5/32
CPCC09D1/00C09D5/32
Inventor 赵莉郑文强
Owner GUANGDONG MIDEA KITCHEN APPLIANCES MFG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap