Water-based organic-inorganic hybrid anticorrosive coating and application method thereof

An anti-corrosion coating, organic technology, applied in anti-corrosion coatings, coatings, devices for coating liquids on surfaces, etc., can solve the problems of loss of corrosion inhibition ability, insufficient film strength, insufficient corrosion resistance, etc. Effects of layer longevity requirements, good substrate adhesion, good corrosion resistance

Active Publication Date: 2016-11-16
湖南天氟新材料有限公司
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Hexavalent chromium passivation treatment is subject to more and more restrictions due to environmental pollution and other issues
2) Using pure organic coating without adding anti-rust agent, the corrosion resistance is not enough, especially the corrosion resistance after processing
3) The method of chemical conversion treatment liquid is used for anticorrosion, and the strength of the coating film is insufficient and the adhesion is weak
Therefore, there are the following defects in the related art: due to factors such as insufficient paint film strength, weak adhesion, and insufficient corrosion resistance, etc.
After processing, the coating will be damaged, peeled off, etc., resulting in a decrease in anti-corrosion performance or loss of corrosion inhibition ability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based organic-inorganic hybrid anticorrosive coating and application method thereof
  • Water-based organic-inorganic hybrid anticorrosive coating and application method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A water-based organic-inorganic hybrid anti-corrosion coating, which is composed of the following components in parts by weight: 90 parts of nanomaterial modified acrylate composite emulsion, 10 parts of ammonium fluorozirconate, 15 parts of sodium molybdate, and titanate coupling agent 10 parts, 5 parts of methanol, 32 parts of water, 1 part of defoamer (BYK022), 1.8 parts of PH adjuster, 0.3 part of leveling agent (BYK331), and 7 parts of curing agent.

[0037] The preparation of nanomaterial modified acrylate composite emulsion in the present embodiment is as follows:

[0038] 1) Recipe (parts by weight):

[0039] 1 part of N,N dimethylbisacrylamide, 1 part of polyethylene glycol dimethacrylate, 2 parts of acrylamide, 35 parts of styrene, 35 parts of butyl acrylate, 15 parts of hydroxyethyl methacrylate, methyl methacrylate 5 parts of base acrylic acid, 1.5 parts of allyl glycidyl ether, 25 parts of methyl methacrylate, 15 parts of n-butyl methacrylate, 14 parts of ...

Embodiment 2

[0051] A water-based organic-inorganic hybrid anti-corrosion coating, which is composed of the following components in parts by weight: 90 parts of nanomaterial modified acrylate composite emulsion, 10 parts of ammonium fluorozirconate, 15 parts of sodium molybdate, and titanate coupling agent 10 parts, 5 parts methanol, 32 parts water, 1 part defoamer (BYK022), 2.4 parts PH adjuster, 0.3 part leveling agent (BYK331), 7 parts curing agent.

[0052] The preparation of nanomaterial modified acrylate composite emulsion in the present embodiment is as follows:

[0053] 1) Recipe (parts by weight):

[0054] 1 part of N,N dimethylbisacrylamide, 1 part of polyethylene glycol dimethacrylate, 2 parts of acrylamide, 35 parts of styrene, 35 parts of butyl acrylate, 15 parts of hydroxyethyl methacrylate, methyl methacrylate 5 parts of base acrylic acid, 1.5 parts of allyl glycidyl ether, 25 parts of methyl methacrylate, 15 parts of n-butyl methacrylate, 14 parts of dodecafluoroheptyl met...

Embodiment 3

[0059] A water-based organic-inorganic hybrid anti-corrosion coating, which is composed of the following components in parts by weight: 90 parts of nanomaterial modified acrylate composite emulsion, 10 parts of ammonium fluorozirconate, 15 parts of sodium molybdate, and titanate coupling agent 10 parts, 5 parts methanol, 32 parts water, 1 part defoamer (BYK022), 1.8 parts PH adjuster, 0.3 part leveling agent (BYK331), 5 parts curing agent.

[0060] The preparation of nanomaterial modified acrylate composite emulsion in the present embodiment is as follows:

[0061] 1) Recipe (parts by weight):

[0062] 1 part of N,N dimethylbisacrylamide, 1 part of polyethylene glycol dimethacrylate, 2 parts of acrylamide, 35 parts of styrene, 35 parts of butyl acrylate, 15 parts of hydroxyethyl methacrylate, methyl methacrylate 5 parts of base acrylic acid, 1.5 parts of allyl glycidyl ether, 25 parts of methyl methacrylate, 15 parts of n-butyl methacrylate, 14 parts of dodecafluoroheptyl met...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a water-based organic-inorganic hybrid anticorrosive coating and an application method thereof. The water-based organic-inorganic hybrid anticorrosive coating is prepared from components in parts by weight as follows: 1-50 parts of a nano-material modified acrylic ester composite emulsion, 1-20 parts of a curing agent, 0-30 parts of inorganic salt, 0.001-1.00 part of an auxiliary, 1-20 parts of a solvent and the balance of deionized water. Compared with the prior art, the water-based organic-inorganic hybrid anticorrosive coating has the beneficial effects as follows: 1, functional organic resin is designed and synthesized and is matched with inorganic anticorrosive salt very well, and a good self-repairing function of the coating is realized; 2, excellent adhesion force is provided, and the coating has good recoatability; the organic-inorganic hybrid coating has good base material adhesion force, and a requirement for a long-term effect of the coating is met; 3, under the conditions of deformation, damage and heated baking of the surface of a base material after post-processing, good anticorrosive performance can still be provided.

Description

【Technical field】 [0001] The invention relates to the technical field of anti-corrosion coatings, in particular to a water-based organic-inorganic hybrid anti-corrosion coating and a method for using the same. 【Background technique】 [0002] Corrosion of the metal surface greatly affects its use value, and anti-corrosion treatment is very important. Among them, anti-corrosion paint coating is a widely used measure. There are usually two kinds of anti-corrosion paint: one is inorganic treatment agent, that is, chemical conversion treatment liquid; the other The first type is an organic coating, that is, a primer coating composed of pure organic resins. Hexavalent chromium passivation treatment is subject to more and more constraints due to environmental pollution and other issues. It is very urgent to use an inorganic treatment agent that is non-polluting to the environment to form a conversion coating to provide anti-corrosion properties. In the related art, Patent Publica...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D151/10C09D125/14C09D5/08C09D7/12C08F292/00C08F222/38C08F222/14C08F220/56C08F212/08C08F220/18C08F220/28C08F220/06C08F220/14C08F220/22C08F216/14B05D7/14
CPCB05D7/14C08F212/08C08F220/18C08F220/1804C08F292/00C08K3/08C08K3/24C08K3/28C08K3/36C08K2003/0812C08K2201/011C09D5/08C09D7/61C09D151/10
Inventor 刘天成董其宝樊孝红胡沩
Owner 湖南天氟新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com