Sagger for lithium battery cathode material and preparation method thereof

A technology for positive electrode materials and lithium batteries, which is applied in the field of saggers for lithium battery positive electrode materials and its preparation, can solve the problems of poor corrosion resistance of saggers, easy pollution of battery raw materials, poor thermal shock stability, etc., and achieve saggers Effect of long life, reduction of corrosion channels, and improvement of corrosion resistance

Active Publication Date: 2017-01-04
苏州博立恒新能源科技有限公司
View PDF1 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention is how to overcome the defects of the existing saggers such as weak

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sagger for lithium battery cathode material and preparation method thereof
  • Sagger for lithium battery cathode material and preparation method thereof
  • Sagger for lithium battery cathode material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0035] Example one:

[0036] The present invention provides a sagger for lithium battery cathode material, which is composed of the following components by weight percentage: 55% of tabular corundum, 18.5% of cordierite, 8.3% of aluminum titanate, 10% of pure calcium aluminate cement, and alpha oxidation Aluminum powder 8%, sodium tripolyphosphate 0.15% and explosion-proof fiber 0.05%.

[0037] The tabular corundum includes large-grained tabular corundum and small-sized tabular corundum. The large-granularity tabular corundum has a particle size range of 0.2-1 mm and a weight percentage of 40%. The small-granularity tabular corundum has a particle size range of ≤0.088mm, the weight percentage is 15%.

[0038] The cordierite includes large-size cordierite and small-size cordierite, the size range of the large-size cordierite is 0-0.2mm, and the weight percentage is 10%, and the size range of the small-size cordierite is ≤0.088mm, The weight percentage is 8.5%.

[0039] The aluminum t...

Example Embodiment

[0059] Embodiment two:

[0060] The present invention provides a sagger for lithium battery cathode material, which is composed of the following components in weight percentages: tabular corundum 40.3%, cordierite 33.1%, aluminum titanate 15%, pure calcium aluminate cement 5.2%, alpha oxide Aluminum powder 6.12%, sodium tripolyphosphate 0.2% and explosion-proof fiber 0.08%.

[0061] The tabular corundum includes large-granularity tabular corundum and small-granularity tabular corundum. The large-granularity tabular corundum has a particle size range of 1-1.5 mm and a weight percentage of 20%. The small-granularity tabular corundum has a particle size range It is ≤0.088mm, and the weight percentage is 20.3%.

[0062] The cordierite includes large-size cordierite and small-size cordierite, the size range of the large-size cordierite is 0.2-0.5mm, and the weight percentage is 20%, and the size range of the small-size cordierite is ≤0.088mm, The weight percentage is 13.1%.

[0063] The ...

Example Embodiment

[0072] Embodiment three:

[0073] The present invention provides a sagger for lithium battery cathode material, which is composed of the following components in weight percentage: 20% tabular corundum, 44.3% cordierite, 9.3% aluminum titanate, 20% pure calcium aluminate cement, and alpha oxidation Aluminum powder 6%, sodium tripolyphosphate 0.3% and explosion-proof fiber 0.1%.

[0074] The slab corundum includes large-granularity slab corundum and small-granularity slab corundum. The large-granularity slab corundum has a particle size range of 1.5-2.3 mm and a weight percentage of 10%. The small-granularity slab corundum has a particle size range of It is ≤0.088mm, and the weight percentage is 10%.

[0075] The cordierite includes large-size cordierite and small-size cordierite. The large-size cordierite has a particle size range of 0.5-0.8 mm and a weight percentage of 30%. The small-size cordierite has a particle size range of ≤0.088 mm, The weight percentage is 14.3%.

[0076] Th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Granularityaaaaaaaaaa
Granularityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a sagger for a lithium battery cathode material. The sagger is prepared from, by weight, tabular corundum 20-55%, cordierite 18-45%, aluminum titanate 6-30%, pure calcium aluminate cement 5-20% and alpha alumina micro-powder 6-8%. The invention further discloses a preparation method of the sagger for the lithium battery cathode material. The sagger preparation method adopts a casting molding process, and the defects of poor corrosion resistance, short service life, easy pollution of battery raw materials and the like existing in a traditional mechanical pressing molding process are overcome. Compared with the sagger prepared by adopting the existing mechanical pressing molding process, the sagger has higher bulk density and lower porosity by utilizing the self bonding and good liquidity of the micro-powder, the corrosion channels of the lithium battery cathode material to the fire-resistant sagger at high temperature are decreased, and the corrosion resistance of the sagger is improved.

Description

technical field [0001] The invention relates to the technical field of refractory kiln furniture preparation, in particular to a sagger for lithium battery cathode materials and a preparation method thereof. Background technique [0002] At present, lithium cobaltate and ternary lithium batteries are widely used cathode materials for lithium batteries in China, and most of the cathode materials are produced by high-temperature solid-phase synthesis in refractory kilns. During the synthesis process, bearing Sagger materials for burning are generally cordierite, mullite, quartz and corundum. Among these materials, cordierite composite mullite sagger products are the most widely used. This type of sagger is made of cordierite, mullite, and corundum as raw materials, with some clay and micropowder added as a binder, and pressed into shape under a high-tonnage press. After constant temperature curing, it is fired in a refractory kiln. The product is obtained. Moreover, the aver...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/66C04B35/622
Inventor 刘婷婷陈志达
Owner 苏州博立恒新能源科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap