Ultra-low-temperature-resistant antistatic polypropylene composition and preparation method thereof

A polypropylene composition and antistatic technology, applied in the field of polypropylene composite materials, can solve problems such as static spark discharge, material damage, explosion and fire in chemical product warehouses, and achieve good low-temperature impact toughness, good dimensional stability, and antistatic good effect

Inactive Publication Date: 2017-04-26
TIANJIN KINGFA NEW MATERIAL
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, the polypropylene composites disclosed in the prior art have the disadvantage of not achieving a satisfactory combination of low temperature impact toughness and good rigidity.
Moreover, these technologies use Izod or Charpy notched impact strength to evaluate the low-temperature impact performance, and the notched impact strength can evaluate the low-temperature impact performance to some extent but cannot meet the evaluation of the safety performance of automobiles
[0006] Moreover, because the material is a poor conductor of electricity, it is easy to accumulate static charge during processing and use. When the static charge accumulates to a certain extent, static electricity will cause the material to absorb dust and cause material damage. It may also generate static spark discharge, causing chemical The product warehouse exploded and caught fire, causing major personal accidents

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultra-low-temperature-resistant antistatic polypropylene composition and preparation method thereof
  • Ultra-low-temperature-resistant antistatic polypropylene composition and preparation method thereof
  • Ultra-low-temperature-resistant antistatic polypropylene composition and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] A kind of ultralow temperature resistant antistatic polypropylene composition, this composition is made of the raw material that comprises following parts by weight: 69.4 parts of polypropylene resins, 15 parts of polyolefin elastomers, 4 parts of talc masterbatches (talcum powder and polypropylene resin The mass ratio is 4:1), acrylic acid-polysiloxane rubber-methyl methacrylate multi-polymer copolymer 1 part, permanent antistatic agent 10 parts, phenolic heat stabilizer 0.2 part, hindered amine light stabilizer 0.2 parts, erucamide 0.2 parts.

[0044] The preparation method of the described ultralow temperature resistant antistatic polypropylene composition comprises the steps:

[0045] (1) Add talcum powder and polypropylene resin to a high-temperature mixer, pre-mix at a temperature of 170°C, granulate and cool to obtain a filling enhancer;

[0046] (2) Mix the filling reinforcing agent, polypropylene resin, polyolefin elastomer, low-temperature modifier, antistati...

Embodiment 2

[0049] A kind of ultralow temperature resistant antistatic polypropylene composition, this composition is made of the raw material that comprises following parts by weight: 45.4 parts of polypropylene resins, 27 parts of polyolefin elastomers, 15 parts of talcum masterbatches (talcum powder and polypropylene resin The mass ratio is 4:1), acrylic acid-ethylene propylene rubber-methyl methacrylate multi-polymer copolymer 2 parts, permanent antistatic agent 10 parts, phenolic heat stabilizer 0.2 parts, hindered amine light stabilizer 0.2 parts , 0.2 parts of erucamide.

[0050] The preparation method of the described ultralow temperature resistant antistatic polypropylene composition comprises the steps:

[0051] (1) Add talcum powder and polypropylene resin to a high-temperature mixer, pre-mix at a temperature of 170°C, granulate and cool to obtain a filling enhancer;

[0052] (2) Mix the filling reinforcing agent, polypropylene resin, polyolefin elastomer, low-temperature modi...

Embodiment 3

[0055] A kind of ultralow temperature resistant antistatic polypropylene composition, this composition is made of the raw material that comprises following parts by weight: 39.4 parts of polypropylene resins, 15 parts of polyolefin elastomers, 27 parts of talcum masterbatches (talcum powder and polypropylene resin The mass ratio is 4:1), acrylic acid-ethylene propylene rubber-methyl methacrylate multi-polymer 1.5 parts, acrylic-polysiloxane rubber-methyl methacrylate multi-polymer 1.5 parts, permanent antistatic agent 15 parts, 0.2 part of phenolic heat stabilizer, 0.2 part of hindered amine light stabilizer, 0.2 part of erucamide.

[0056] The preparation method of the described ultralow temperature resistant antistatic polypropylene composition comprises the steps:

[0057] (1) Add talcum powder and polypropylene resin to a high-temperature mixer, pre-mix at a temperature of 170°C, granulate and cool to obtain a filling enhancer;

[0058] (2) Mix the filling reinforcing age...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
densityaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to view more

Abstract

The invention provides an ultra-low-temperature-resistant antistatic polypropylene composition and a preparation method thereof. The composition is prepared from the following raw materials in parts by weight: 39-90 parts of resin A, 10-40 parts of polyolefin elastomer, 1-30 parts of a filling enhancer, 1-5 parts of a low-temperature modifier, 10-15 parts of an antistatic agent and 0.1-4 parts of other auxiliary agents. The ultra-low-temperature-resistant antistatic polypropylene composition provided by the invention has good low-temperature impact toughness (particularly multi-shaft low-temperature impact strength) and good rigidity, and maintains good dimensional stability.

Description

technical field [0001] The invention belongs to the technical field of polypropylene composite materials, and in particular relates to an ultralow temperature-resistant antistatic polypropylene composition. Background technique [0002] Polypropylene is a general-purpose plastic with a wide range of uses. It is polymerized from propylene monomer. The English abbreviation is PP. Its melting point is 165-175 ° C and it is a semi-crystalline plastic. Polypropylene plastic has the characteristics of light weight and easy processing, and has become the largest and fastest-growing variety of automotive plastics. However, polypropylene material has poor low temperature resistance and low rigidity, which cannot meet the requirements and standards of automotive interior parts. Interior parts include instrument panel, auxiliary instrument panel, A, B and C pillars, glove box, door panel, rear tail box panel, etc. [0003] Automobile parts pay more and more attention to safety perfor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/14C08L23/08C08L23/10C08L51/04C08L71/02C08K13/02C08K3/34C08K5/20C08J3/22
CPCC08L23/14C08J3/226C08J2323/14C08J2423/08C08J2423/10C08J2423/14C08J2471/02C08L2201/04C08L2205/02C08L2205/025C08L2205/035C08L2207/53C08L23/0815C08L51/04C08L71/02C08K13/02C08K3/34C08K5/20C08L23/10
Inventor 肖华明王扬利郝垠龙
Owner TIANJIN KINGFA NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap