A kind of method for preparing tackifier copolymerized association

A technology of associates and viscosifiers, which is applied in the field of preparation of polymers for drilling fluids, can solve the problem of no obvious improvement in salt and calcium resistance, and achieve high shear and temperature and salt resistance.

Active Publication Date: 2019-05-17
CHINA PETROLEUM & CHEM CORP +1
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

CN101955564A, CN103113518A, and CN102127401A disclose high-temperature-resistant tackifiers. The high-temperature-resistant performance of the tackifier has been significantly improved, and the temperature resistance can reach above 200°C; the salt-resistant and calcium-resistant properties are not mentioned, but from the monomers used and the preparation method It is speculated that there is no significant improvement in salt and calcium resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of method for preparing tackifier copolymerized association
  • A kind of method for preparing tackifier copolymerized association
  • A kind of method for preparing tackifier copolymerized association

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0065] Add 2.5g of OP15 and 22.5g of Span 80 into 150g of white oil, pass N under stirring condition 2 Deoxygenate for half an hour, prepare the oil phase for later use; add 37.5g NaCl to 140g water and fully dissolve it to prepare an aqueous NaCl solution, then add 18g MAPS and 63gDMAM to the NaCl aqueous solution, stir to fully dissolve it; transfer the oil phase to the reactor Add the water phase dropwise to the oil phase while stirring, and stir for half an hour to obtain an emulsification system; add 0.24g potassium persulfate to the emulsification system, and pass N 2 Deoxygenation for half an hour, while raising the temperature to 60 ° C, and reacting for 1 hour to obtain an intermediate product; then dissolving 2 g of cationic polyamine 1 in 10 g of deionized water to prepare a cationic polyamine solution, and then adding the cationic polyamine solution to the intermediate product, Mix evenly, and at the same time raise the temperature to 70°C, and continue the reactio...

Embodiment 2

[0067] Add 1.5g of OP15 and 13.5g of Span 80 into 75g of white oil, pass N under stirring condition 2 Deoxygenation for half an hour, the oil phase was prepared for use; 20gCaCl 2 Add to 140g water and fully dissolve to make CaCl 2 aqueous solution, then 47gMAPS and 46gDMAM were added to the CaCl 2 In the aqueous solution, stir to fully dissolve it; transfer the oil phase to the reactor, add the water phase to the oil phase dropwise while stirring, and stir for half an hour to obtain an emulsification system; add 0.32g of sodium persulfate to the emulsification system, wait After fully dissolved, pass N 2 Deoxygenation for half an hour, while raising the temperature to 55 ° C for 1.5 hours to obtain an intermediate product; then dissolving 4 g of cationic polyamine 2 in 10 g of deionized water to prepare a cationic polyamine solution, and then adding the cationic polyamine solution to the intermediate product, Mix evenly, and at the same time raise the temperature to 65°C, ...

Embodiment 3

[0069] Add 1.4g of Tween 80 and 13.6g of Span 80 into 90g of white oil, pass N under stirring condition 2 Deoxygenation for half an hour, the oil phase was prepared for use; 10gAlCl 3 Add to 130g water and fully dissolve to make AlCl 3 aqueous solution, then add 28gMAPS and 28gDMAM to AlCl 3 In the aqueous solution, stir to fully dissolve it; transfer the oil phase to the reactor, add the water phase to the oil phase dropwise while stirring, and stir for half an hour to obtain an emulsification system; add 0.2g potassium persulfate to the emulsification system, wait After fully dissolved, pass N 2 Deoxygenation for half an hour, while raising the temperature to 50 ° C, and reacting for 2 hours to obtain an intermediate product; then dissolving 6 g of cationic polyamine 3 in 20 g of deionized water to prepare a cationic polyamine solution, and then adding the cationic polyamine solution to the intermediate product, Mix evenly, and at the same time raise the temperature to 60...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
shear viscosityaaaaaaaaaa
thermal resistanceaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing a tackifier copolymerization associate. The copolymerization associate comprises a constitutional unit A, a constitutional unit B and a constitutional unit C. The constitutional unit A is N, N-dimethylacrylamide, the constitutional unit B is N-methyl diallyl propylsulfonate (MAPS) which is an amphoteric ionic monomer, and the constitutional unit C is an ionic associate of the constitutional unit B and cationic polyamine. Based on the total amount of the copolymerization associate, the copolymerization associate comprises 10-75% by weight of the constitutional unit A, 8-55% by weight of the amphoteric ionic monomer, and 1-50% by weight of the cationic polyamine. A tackifier obtained through the preparation method can resist temperature as high as 200 DEG C, can resist a saturated NaCl solution, and resist a CaCl2 solution with the concentration being 20%. The tackifier is excellent shale inhibition and filtrate reduction.

Description

technical field [0001] The invention relates to a preparation method of a polymer used in drilling fluid during petroleum drilling, in particular to a high-temperature-resistant viscosifier used in drilling fluid and a preparation method thereof. Background technique [0002] During the drilling process, in order to ensure that the drilling fluid has a high viscosity and good rheology under low solid phase, it is usually necessary to add a viscosifier to increase the viscosity of the drilling fluid. Drilling fluid viscosifiers are all water-soluble high molecular polymers with long molecular chains. In addition to the viscosifying effect, viscosifiers often also serve as shale inhibitors (coating agents), fluid loss reducers and flow control agents. type improver, etc. Therefore, the use of viscosifiers is often beneficial to improving the rheological properties of drilling fluids, and is also beneficial to the stability of wellbore walls. [0003] Drilling fluid viscosifi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G81/02C08F220/54C08F226/02C09K8/035
Inventor 杨超张志智孙潇磊鲁娇尹泽群刘全杰
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com