Low-melting-point packing film

A low melting point, packaging film technology, applied in the field of packaging materials, can solve the problems of large vertical and horizontal strength differences, affect applications, and low sealing strength, achieve consistent vertical and horizontal physical properties, improve bag making methods, and high sealing strength Effect

Inactive Publication Date: 2017-05-10
仲铂新材料有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] (1) The appearance of the packaging bag has obvious defects, wrinkles, low transparency, poor dimensional stability of the packaging bag, low sealing strength, and easy damage;
[0004] (2) The physical property index is low, and the vertical and horizontal differences in strength are large, resulting in frequent damage in the direction of low strength (especially for small-sized bags), and due to anisotropic anisotropy, the elongation of the package changes greatly , it is very easy to deform after loading the material, resulting in broken leaks;
[0005] (3) The distribution of melting point is uneven and the temperature difference is large, which affects subsequent applications and directly affects the product quality of downstream customers;
[0006] (4) Due to the limitation of current domestic equipment, the production process plan of the low-melting point packaging bag is unreasonable, resulting in the quality of the packaging bag not meeting the requirements for use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-melting-point packing film
  • Low-melting-point packing film
  • Low-melting-point packing film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A method for making a low-melting point packaging bag, the method comprising the following steps:

[0035] (1) Mixing granules: According to the preset mass percentage, mix the following raw materials evenly to obtain the mixed material:

[0036]

[0037] (2) Film blowing: Use a film blowing machine to heat and melt the mixture and process it into a raw film with an inflation ratio of 3:1;

[0038] Then, the raw material film is cooled at 20°C by using the internal and external cooling method of the film bubble to obtain a low-melting point packaging film;

[0039] (3) bag making (such as figure 1 shown):

[0040] 1) Cutting the low-melting-point packaging film according to the preset bag width W (400 mm) along the length extension direction of the low-melting-point packaging film to obtain multiple small-sized low-melting-point packaging films;

[0041] 2) Carry out double-sided heat-sealing on each small-size low-melting-point packaging film, and cut the small-s...

Embodiment 2

[0043] A method for making a low-melting point packaging bag, the method comprising the following steps:

[0044] (1) Mixing granules: According to the preset mass percentage, mix the following raw materials evenly to obtain the mixed material:

[0045]

[0046] (2) Film blowing: Use a film blowing machine to heat and melt the mixture and process it into a raw film with an inflation ratio of 5:1;

[0047] Then, the raw material film is cooled at 15°C by using the internal and external cooling method of the film bubble to obtain a low-melting point packaging film;

[0048] (3) bag making (such as figure 1 shown):

[0049] 1) Cut the low-melting-point packaging film according to the preset bag width W (300mm) along the length extension direction of the low-melting-point packaging film to obtain a plurality of small-sized low-melting-point packaging films;

[0050] 2) Carry out double-sided heat-sealing on each small-size low-melting-point packaging film, and cut the small-...

Embodiment 3

[0052] A method for making a low-melting point packaging bag, the method comprising the following steps:

[0053] (1) Mixing granules: According to the preset mass percentage, mix the following raw materials evenly to obtain the mixed material:

[0054]

[0055] (2) Film blowing: Use a film blowing machine to heat and melt the mixture and process it into a raw film with an inflation ratio of 4:1;

[0056] Then, the raw material film is cooled at 10°C by using the internal and external cooling method of the film bubble to obtain a low-melting point packaging film;

[0057] (3) bag making (such as figure 1 shown):

[0058] 1) Cut the low-melting-point packaging film according to the preset bag width W (250mm) along the length extension direction of the low-melting-point packaging film to obtain a plurality of small-sized low-melting-point packaging films;

[0059] 2) Carry out double-sided heat-sealing on each small-size low-melting-point packaging film, and cut the small-...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a low-melting-point packing film. The low-melting-point packing film is prepared from, by mass, 65% of vinyl acetate copolymer, 2% of silicon dioxide, 2% of barium sulphate (precipitating method), 23% of low-density polyethylene and 8% of compound open master batch. The nucleating agent silicon dioxide is added in the formula, so that the packing film has good transparency. In addition, a melting point is controlled to be 90 + / -1 DEG C and is stable, and the packing film does not easily break. The low-melting-point packing film is especially suitable for a low-melting-point packing bag with the production bag width smaller than or equal to 400 mm, the obtained packing bag is stable in size, convenient in vertical and horizontal physical property and high in sealing strength, does not easily deform, does not easily break and is high in transparency, free of wrinkles and excellent in appearance.

Description

technical field [0001] The invention relates to a packaging material, in particular to a low melting point packaging film. Background technique [0002] With the improvement of environmental protection requirements, all walks of life are working hard to meet environmental protection standards. The rubber industry has changed from the original open feeding to closed feeding to reduce the pollution of materials to the environment, thus producing industry-specific low-melting point plastic packaging bags. At present, although my country has started on low-melting point packaging bags, there are still many problems, mainly manifested in the following aspects: [0003] (1) The appearance of the packaging bag has obvious defects, wrinkles, low transparency, poor dimensional stability of the packaging bag, low sealing strength, and easy damage; [0004] (2) The physical property index is low, and the vertical and horizontal strength differences are large, resulting in frequent da...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/08C08L23/06C08K3/36C08K3/30
CPCC08L23/0853C08J5/18C08J2323/08C08J2423/06C08L2201/10C08L2203/16C08L2205/02C08L2205/24C08L2207/066C08L23/06C08K3/36C08K2003/3045
Inventor 周中华
Owner 仲铂新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com