A water cup containing filter material

A technology of water cup and filter material, which is applied in the field of daily life, can solve the problems of water pollution, inability to filter bacteria or harmful elements, and the water cup does not have filtering effect, etc., and achieve the effect of good purification effect and convenient use

Active Publication Date: 2017-11-24
邳州市玖寇商贸有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The water cup is a tool commonly used by people in daily life, but the general water cup does not have a filtering effect. Most of the existing tea cups are equipped with a filter screen at the mouth of the cup. The filtering effect of this filter screen is almost negligible, and it can only filter some large impurities. It is impossible to filter bacteria or harmful elements in the water. The current water pollution is serious, and a water cup with a good purification effect is needed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A water cup containing filter material
  • A water cup containing filter material
  • A water cup containing filter material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Prepare palladium nitrate and methyltrimethoxysilane (MTMOS) samples with a mass ratio of 1:1. 0.5g palladium nitrate, 0.5g methyltrimethoxysilane (MTMOS), 10ml ethanol, 5ml tetraethyl orthosilicate, 8g n-hexadecylamine (HDA), 6g isopropanol, 200ml deionized water.

[0020] Step 1. First, 8 g of n-hexadecylamine (HDA) and 10 ml of ethanol are ultrasonically shaken in an oil bath at 100° C. for 3 hours to remove impurities;

[0021] Step 2. Add 8g of n-hexadecylamine (HDA) into a solution consisting of 200ml of deionized water and 10ml of ethanol to form solution A, and stir magnetically for 3h in an oil bath at 100°C;

[0022] Step 3. Remove impurities from methyltrimethoxysilane (MTMOS), palladium nitrate, isopropanol, and tetraethyl orthosilicate (TEOS) in an ultrasonic vibration oil bath at 100°C for 2 hours;

[0023] Step 4. Add 0.5g methyltrimethoxysilane (MTMOS) and 0.5g palladium nitrate to a mixed solution consisting of 6g isopropanol and 5ml tetraethyl orthosi...

Embodiment 2

[0028] Example 2 Prepare palladium nitrate and methyltrimethoxysilane (MTMOS) samples with a mass ratio of 1:2. 0.5g palladium nitrate, 1g methyltrimethoxysilane (MTMOS), 10ml ethanol, 5ml tetraethyl orthosilicate, 8g n-hexadecylamine (HDA), 6g isopropanol, 200ml deionized water.

[0029] Step 1. First, 8 g of n-hexadecylamine (HDA) and 10 ml of ethanol are ultrasonically shaken in an oil bath at 100° C. for 3 hours to remove impurities;

[0030] Step 2. Add 8g of n-hexadecylamine (HDA) into a solution consisting of 200ml of deionized water and 10ml of ethanol to form solution A, and stir magnetically for 3h in an oil bath at 100°C;

[0031] Step 3. Remove impurities from methyltrimethoxysilane (MTMOS), palladium nitrate, isopropanol, and tetraethyl orthosilicate (TEOS) in an ultrasonic vibration oil bath at 100°C for 2 hours;

[0032] Step 4. Add 1g of methyltrimethoxysilane (MTMOS) and 0.5g of palladium nitrate to a mixed solution consisting of 6g of isopropanol and 5ml of ...

Embodiment 3

[0037] Example 3 Prepare palladium nitrate and methyltrimethoxysilane (MTMOS) with a mass ratio of 1:3. 0.5g of palladium nitrate, 1.5g of methyltrimethoxysilane (MTMOS), 10ml of ethanol, 5ml of ethyl orthosilicate, 8g of n-hexadecylamine (HDA), 6g of isopropanol, and 200ml of deionized water.

[0038] Step 1. First, 8 g of n-hexadecylamine (HDA) and 10 ml of ethanol are ultrasonically shaken in an oil bath at 100° C. for 3 hours to remove impurities;

[0039] Step 2. Add 8g of n-hexadecylamine (HDA) into a solution consisting of 200ml of deionized water and 10ml of ethanol to form solution A, and stir magnetically for 3h in an oil bath at 100°C;

[0040] Step 3. Remove impurities from methyltrimethoxysilane (MTMOS), palladium nitrate, isopropanol, and tetraethyl orthosilicate (TEOS) in an ultrasonic vibration oil bath at 100°C for 2 hours;

[0041] Step 4. Add 1.5g of methyltrimethoxysilane (MTMOS) and 0.5g of palladium nitrate to a mixed solution consisting of 6g of isoprop...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a water cup containing a filtering material. The water cup containing the filtering material comprises a water cup body, wherein the inner part of the water cup body is provided with a filtering device, the filtering device comprises a filtering box, a filtering box lid and the filtering material, the filtering material is installed in the filtering box, the outer side of the filtering box lid is provided with an external thread, the inner side of the filtering box is provided with an inner thread, and the filtering box is in screw-thread fit connection with the filtering box lid. According to the water cup contained with the filtering material, the inner part of the water cup is provided with the filtering box, the filtering box can be disassembled and replaced, and thus the water cup is convenient to use; in addition, the filtering box is in screw-thread fit connection with the filtering box lid, new filtering material can be directly replaced, the filtering material is a novel Pd-HMS molecular sieve filtering material which is prepared from a special technology, and the purifying effect is good.

Description

technical field [0001] The invention relates to a water cup containing a filter material, which belongs to the field of daily life. Background technique [0002] The water cup is a tool commonly used by people in daily life, but the general water cup does not have a filtering effect. Most of the existing tea cups are equipped with a filter screen at the mouth of the cup. The filtering effect of this filter screen is almost negligible, and it can only filter some large impurities. Bacteria or harmful elements in the water cannot be filtered. The current water pollution is serious, and a water cup with a good purification effect is needed. Contents of the invention [0003] Aiming at the above-mentioned problems in the prior art, the present invention provides a water cup containing a filter material, which has a good water purification effect. [0004] In order to achieve the above object, the technical solution adopted by the present invention is: a water cup containing f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A47G19/22B01D24/12
CPCA47G19/2205B01D24/12
Inventor 卓懋百
Owner 邳州市玖寇商贸有限公司