High-strength and high flame-retardant cable sheath tube prepared from tanning chromium-containing sludge

A sheath tube, high-strength technology, applied in the field of sheath tube, can solve problems such as unsatisfactory

Active Publication Date: 2017-06-13
ZHEJIANG XINYUANHONG MACROMOLECULE MATERIAL
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these current cable sheathing tubes are still not ideal in terms of strength, rigidity and flame retardancy, or there is only a certain improvement in the performance of a certain aspect, and there is a lot of room for further improvement.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0043] Environmentally friendly high-strength and high flame-retardant cables are prepared from tannery chrome-containing sludge, which includes wire cores, insulating layers, inner sheaths and sheath tubes from the inside to the outside, and the raw materials for the sheath tubes include:

[0044] Acrylonitrile / ethylene / styrene copolymer 70kg

[0045] Tannery chrome sludge 5kg

[0046] Modified tannin extract granules 2kg

[0047] Bentonite 2kg

[0048] Carbon nanotubes 1.2kg

[0049] Methyltriethoxysilane 0.8kg

[0050] Stearic acid 3kg

[0051] Zinc oxide 2kg

[0052] Sodium alginate 0.2kg

[0053] Bisphenol fluorene 1kg

[0054] Hexaphenoxytriphosphazene 2.2kg

[0055] N,N-Methylenebisacrylamide 0.6kg

[0056] N-methylolacrylamide 0.1kg

[0057] Sodium molybdate 0.2kg

[0058] Sodium bismuthate 0.1kg

[0059] Bisphenol A0.1kg

[0060] Preparation method: comprising the following steps:

[0061] (1) Melt blending: Mix the above ingredients according to the pro...

example 2

[0067] Environmentally friendly high-strength and high flame-retardant cables are prepared from tannery chrome-containing sludge, which includes wire cores, insulating layers, inner sheaths and sheath tubes from the inside to the outside, and the raw materials for the sheath tubes include:

[0068] Acrylonitrile / ethylene / styrene copolymer 80kg

[0069] Tannery chrome sludge 9kg

[0070] Modified tannin extract particles 3kg

[0071] Bentonite 3kg

[0072] Carbon nanotubes 1.6kg

[0073] Methyltriethoxysilane 1.2kg

[0074] Stearic acid 3kg

[0075] Zinc oxide 5kg

[0076] Sodium alginate 0.8kg

[0077] Bisphenol fluorene 3.2kg

[0078] Hexaphenoxytriphosphazene 3.6kg

[0079] N,N-Methylenebisacrylamide 2.2kg

[0080] N-methylolacrylamide 0.5kg

[0081] Sodium molybdate 0.5kg

[0082] Sodium bismuthate 0.2kg

[0083] Bisphenol A0.3kg

[0084] Preparation method: comprising the following steps:

[0085] (1) Melt blending: Mix the above ingredients according to the ...

example 3

[0091] Environmentally friendly high-strength and high flame-retardant cables are prepared from tannery chrome-containing sludge, which includes wire cores, insulating layers, inner sheaths and sheath tubes from the inside to the outside, and the raw materials for the sheath tubes include:

[0092] Acrylonitrile / ethylene / styrene copolymer 75kg

[0093] Tannery chrome sludge 7kg

[0094] Modified tannin extract particles 2.5kg

[0095] Bentonite 2.5kg

[0096] Carbon nanotubes 1.4kg

[0097] Methyltriethoxysilane 1kg

[0098] Stearic acid 3kg

[0099] Zinc oxide 3.5kg

[0100] Sodium alginate 0.5kg

[0101] Bisphenol fluorene 2.1kg

[0102] Hexaphenoxytriphosphazene 2.9kg

[0103] N,N-Methylenebisacrylamide 1.4kg

[0104] N-methylolacrylamide 0.3kg

[0105] Sodium molybdate 0.35kg

[0106] Sodium bismuthate 0.15kg

[0107] Bisphenol A0.2kg

[0108] Preparation method: comprising the following steps:

[0109] (1) Melt blending: Mix the above ingredients according t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an environment-friendly high-strength and high flame-retardant cable sheath tube prepared from tanning chromium-containing sludge. The sheath tube is prepared from the following raw materials of polyacrylonitrile / ethylene / styrene copolymer, the tanning chromium-containing sludge, bentonite, methyl triethoxysilane, zinc oxide, sodium alginate, fluorene-9-bisphenol, and hexaphenoxy cyclotriphosphazene. The prepared cable has the advantages that the flame-retardant property and the strength are high, and the effect of low smoke release is realized.

Description

[0001] This application is a divisional application of the Chinese invention patent application filed on April 6, 2016 with the application number 201610209039.3 and the title of the invention is the use of tannery chromium-containing sludge to prepare environmentally friendly high-strength and high flame-retardant cables. technical field [0002] The invention relates to a high-strength cable, in particular to a sheath tube of an environment-friendly high-strength and high-flame-resistance cable prepared by utilizing chrome-containing sludge from leather making. [0003] technical background [0004] With the gradual acceleration of the urbanization process, urban planning is becoming more and more modern. In the process of urban construction, cable entry into the ground has become the minimum construction requirement. At the same time, in the process of urban transformation, it is also necessary to put various cables erected in the air into the ground. At present, the cons...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01B7/18H01B7/28H01B7/295H01B13/24
CPCH01B7/18H01B7/187H01B7/28H01B7/295H01B13/24
Inventor 段宝荣李成
Owner ZHEJIANG XINYUANHONG MACROMOLECULE MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More