A kind of inorganic thermal insulation mortar based on hydrophobic airgel and preparation method thereof

A technology of inorganic thermal insulation mortar and airgel, which is applied in the field of building thermal insulation materials and its preparation, and the preparation of inorganic thermal insulation mortar, which can solve the problems of airgel easy to absorb moisture, overcome technical difficulties, invest in large equipment, and reduce thermal conductivity Effect

Active Publication Date: 2019-06-25
SHANGHAI RES INST OF BUILDING SCI CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, because ordinary aerogels are easy to absorb moisture, aerogels generally need to be treated with water-repellent when used as thermal insulation materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of inorganic thermal insulation mortar based on hydrophobic airgel and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] Weigh the following substances by weight:

[0042] 170 parts of cement, 54 parts of lightweight aggregate (vitrified bead fine powder with a bulk density of 60g / L), 5 parts of hydrophobic airgel (density of 50kg / m3), 2.0 parts of cellulose ether (viscosity of 100000cps), 2.0 parts of air-entraining agent, 0.3 parts of starch ether, 0.5 parts of wood fiber, 1 part of PVA, 450 parts of water.

[0043] Mix as above.

Embodiment 2

[0045] Get the material of following weight parts:

[0046] 140 parts of cement, 60 parts of lightweight aggregate (vitrified microspheres with a better gradation of bulk density of 120g / L), 20 parts of hydrophobic airgel (density of 40kg / m3), 1.5 parts of cellulose ether (viscosity of 200000cps) 1.5 parts of air-entraining agent, 0.15 parts of starch ether, 0.4 parts of wood fiber, 1 part of PVA, and 400 parts of water.

[0047] Mix as described above.

Embodiment 3

[0049] Get the material of following weight parts:

[0050] 110 parts of cement, 42 parts of lightweight aggregate (vitrified bead fine powder with a bulk density of 60g / L), 15 parts of hydrophobic airgel (density of 50kg / m3), 1.7 parts of cellulose ether (viscosity of 100000cps), 1.7 parts of air-entraining agent, 0 parts of starch ether, 0.3 parts of wood fiber, 1 part of PVA, 330 parts of water.

[0051] Mix as described above.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
water absorptionaaaaaaaaaa
water absorptionaaaaaaaaaa
Login to view more

Abstract

The invention provides inorganic insulation mortar based on hydrophobic aerogel and a preparation method thereof; the inorganic insulation mortar based on hydrophobic aerogel is a mixture of, by weight, 110-170 parts of cement, 30-96 parts of light aggregate, 5-25 parts of hydrophobic aerogel, 0.2-2.0 parts of cellulose ether, 0.2-2.0 parts of an air entraining agent, 0.-0.3 part of starch ether, 0.3-0.6 part of wood fiber, 1-2 parts of PVA (polyvinyl alcohol), and 300-580 parts of water. The preparation method comprises the steps of 1, weighing the raw materials according to the parts by weight; 2, mixing well light aggregate and hydrophobic aerogel in advance; 3, mixing well the raw materials except for the light aggregate, hydrophobic aerogel and water, and stirring well with weighed water to form slurry; 4, adding the mixture of the light aggregate and hydrophobic aerogel in step 2 into the slurry of step 3, stirring slowly, and allowing standing to obtain the inorganic insulation mortar based on hydrophobic aerogel.

Description

technical field [0001] The invention belongs to the technical field of building energy saving and new materials, and relates to a building thermal insulation material and a preparation method thereof; in particular, it relates to an inorganic thermal insulation mortar based on hydrophobic airgel and a preparation method of the inorganic thermal insulation mortar. Background technique [0002] my country's existing construction area is about 40 billion m 2 , most of which are high energy consumption buildings; on the other hand, there are nearly 2 billion m2 of new buildings every year 2 , More than 95% of new buildings are still high energy consumption buildings. Building energy consumption accounts for about 1 / 3 of the total energy consumption of the society, and huge building energy consumption has become a major burden on the national economy. During the "Thirteenth Five-Year Plan" period, building energy conservation has been listed as an important task for national en...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/00C04B14/06C04B111/40
CPCC04B14/064C04B28/00C04B2201/20C04B2201/32C04B2201/50C04B14/24C04B24/383C04B2103/304C04B24/38C04B16/02C04B24/2623
Inventor 王琼钱耀丽叶蓓红管文杨利香仲小亮韩云婷李华良
Owner SHANGHAI RES INST OF BUILDING SCI CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products