Three-layer co-extrusion preparation technology for plastic floor
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A three-layer co-extrusion, preparation process technology, applied in the direction of flat products, applications, household appliances, etc., can solve the problems of low floor quality, heavy tiles, shortening, etc., to achieve good elasticity and comfort, simple production steps, and service life. long effect
Active Publication Date: 2017-09-01
ANHUI HANHUA BUILDING MATERIALS TECH
View PDF4 Cites 4 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] The flame retardancy of wooden floors is poor. At the same time, blisters during the production period are prone to breed bacteria and the practical life will be shortened. Ceramic tiles are relatively heavy. At the same time, heavy and hard objects falling from a high place will easily cause the bottom plate to break. Plastic floors are light, waterproof and Convenience of construction has become people's first choice of decoration materials. Most of the existing technologies are produced by pressing technology, but the connection between layers of the pressed bottom plate is not tight, and the glue will overflow during pressing, which needs to be removed. Glue, so that the production process is more cumbersome, the quality of the floor produced is not high
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0018] In order to strengthen the understanding of the present invention, the present invention will be described in further detail below, and this embodiment is only used to explain the present invention, and does not limit the protection scope of the present invention.
[0019] The invention relates to a three-layer co-extrusion preparation process of a plastic board. The plastic board includes an upper surface layer, a middle layer and a lower surface layer. The middle layer is composed of the following materials in parts by weight: 50-60 parts of polyvinyl chloride, 30 parts of calcium carbonate -40 parts, 0.5 parts of foaming agent, 3-5 parts of stabilizer, 2-3 parts of lubricant, 3-6 parts of polyphenylene particles, 4-8 parts of perlite powder, 10-13 parts of polyurethane, ammonium dihydrogen phosphate 2-5 parts, 2-3 parts of auxiliary materials, the upper surface layer and the lower surface layer are composed of the following materials by weight: 30-40 parts of heat-res...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
thickness
aaaaa
aaaaa
thickness
aaaaa
aaaaa
thickness
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses a three-layer co-extrusion preparation technology for a plastic floor. The plastic floor comprises an upper surface layer, a middle layer and a lower surface layer. The middle layer comprises, by weight, 50-60 parts of polyvinyl chloride, 30-40 parts of calcium carbonate, 0.5 part of a foaming agent, 3-5 parts of a stabilizer, 2-3 parts of a lubricant, 3-6 parts of polyphenyl granules, 4-8 parts of crushed crude pearlite, 10-13 parts of polyurethane, 2-5 parts of ammonium dihydrogen phosphate and 2-3 parts of accessories. The upper surface layer and the lower surface layer comprise, by weight, 30-40 parts of heat-resisting polyethylene, 30-35 parts of calcium carbonate, 5 parts of a stabilizer, 3 parts of a lubricant, 10-13 parts of rock wool powder, 4-6 parts of nano-zinc oxide powder, a silver ion antibacterial agent, 2-3 parts of mica powder and 3-5 parts of accessories. The preparation technology includes the steps of burdening, mixing, heating extrusion, cooling, shaping and floor discharging as well as processing of the plastic floor surface. According to the three-layer co-extrusion preparation technology for the plastic floor, design is reasonable, the production steps are simple, and the plastic floor produced through the technology is tight in connection, long in service life and good in elastic comfortable sensation.
Description
technical field [0001] The invention relates to the production technology of the base plate, in particular to a three-layer co-extrusion preparation process of the plastic plate. Background technique [0002] The flame retardancy of wooden floors is poor. At the same time, blisters during the production period are prone to breed bacteria and the practical life will be shortened. Ceramic tiles are relatively heavy. At the same time, heavy and hard objects falling from a high place will easily cause the bottom plate to break. Plastic floors are light, waterproof and Convenience of construction has become people's first choice of decoration materials. Most of the existing technologies are produced by pressing technology, but the connection between layers of the pressed bottom plate is not tight, and the glue will overflow during pressing, which needs to be removed. High-quality glue makes the production process more cumbersome, and the quality of the floor produced is not high....
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.