Cordierite-doped non-chromate Dacromet coating and preparation method

A cordierite and coating technology, used in anti-corrosion coatings, epoxy resin coatings, coatings, etc., can solve the problems of low strength and poor wear resistance, and achieve increased strength and wear resistance, and the coating is dense and smooth. , the effect of reducing production costs

Inactive Publication Date: 2017-09-15
合肥新意境材料有限责任公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The object of the present invention is to provide a kind of chrome-free dacromet coating and preparation method thereof, overcome the bad wear resistance, the low strength shortcoming of dacromet coating existing at present, the technical scheme that the present invention adopts is as follows:

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0018] A kind of cordierite-doped chrome-free dacromet coating, is characterized in that, is made from the raw material of following weight part:

[0019] Cordierite 5, corundum powder 5, silicon carbide 8, fly ash 3, polytetrafluoroethylene powder 10, epoxy resin E42 15, vinyltriamine 15, diatomaceous earth 2, zinc powder 30, aluminum powder 30, silane Coupling agent KH550 50, ethanol 10, acetone 70, polydimethylsiloxane 0.6;

[0020] The zinc powder and aluminum powder are flake powders.

[0021] A kind of cordierite-doped chrome-free dacromet paint and preparation method thereof, is characterized in that, comprises the following operation steps:

[0022] a. ultrasonically disperse corundum powder with ethanol solution for 1-2 hours, filter and dry;

[0023] b. Grind the corundum powder obtained in step a, cordierite, silicon carbide, fly ash, polytetrafluoroethylene powder and diatomaceous earth in a mortar to make it fully mixed, then transfer it to a crucible, place it ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a cordierite-doped non-chromate Dacromet coating and a preparation method thereof, the non-chromate Dacromet coating is characterized by comprising the following parts by weight of raw materials: 3-5 parts of cordierite, 3-5 parts of corundum powder, 4-8 parts of silicon carbide, 1-3 parts of fly ash, 5-10 parts of polytetrafluoroethylene powder, 10-15 parts of epoxy resin E42, 10-15 parts of vinyl triamine, 1-2 parts of diatomite, 20-30 parts of zinc powder, 20-30 parts of aluminum powder, 40-50 parts of silane coupling agent KH550, 5-10 parts of ethanol, 50-70 parts of acetone and 0.3-0.6 part of polydimethylsiloxane; the non-chromate Dacromet coating has the advantages of high strength and wear resistance and good liquidity and adhesion, a formed coating is dense and smooth, the defects of low strength and poor wear resistance of a Dacromet coating solution can be solved, the non-chromate Dacromet coating is highly competitive in the market; the cordierite,the fly ash and the like are added for cooperation to reduce the production cost in the premise of no influence on the property of the coating.

Description

technical field [0001] The invention relates to a dacromet paint, which belongs to the field of metal anticorrosion, in particular to a cordierite-doped chrome-free dacromet paint and a preparation method thereof. Background technique [0002] Corrosion of steel directly leads to a large number of accidents or hidden dangers of accidents every year, causing huge economic losses and seriously affecting national economic development and security. How to provide durable corrosion resistance has become a research hotspot. Dacromet coating is a metal anti-corrosion coating composed of scaly zinc powder, aluminum powder chromic anhydride and organic reducing agent. It has been widely used due to its strong corrosion resistance, high temperature resistance, and high permeability. However, , because the Dacromet treatment solution contains about 2% of highly carcinogenic and highly toxic Cr 6+ . Therefore, the current Dacromet coating has the disadvantages of being not environmen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D163/00C09D5/10C09D7/12C08G59/50
CPCC09D163/00C08G59/5006C08K2003/2227C08K2201/014C08L2205/03C08L2312/00C09D5/103C09D5/106C08L27/18C08L83/04C08K13/06C08K9/00C08K9/06C08K3/34C08K7/00C08K3/22C08K7/26
Inventor 宋睿王贵东
Owner 合肥新意境材料有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap