Wood preservation carbonizing method

A technology of wood preservation and wood, which is applied in the direction of charcoal burning/combustion, can opening and impregnation, etc. It can solve the problems of lack of anti-corrosion performance of carbonized wood and unsatisfactory mechanical properties of carbonized wood, so as to achieve good carbonization effect, sufficient carbonization, and enhanced anti-corrosion performance effect

Inactive Publication Date: 2017-10-13
芜湖斯塔克智能科技有限公司
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, under some harsh conditions of use, the anti-corrosion performance of carbonized wood is still lacking, and the mechanical properties of carbonized wood are not ideal. Therefore, in order to better improve the anti-corrosion performance of carbonized wood, it is necessary to improve the current Carbonized wood processing technology to improve the comprehensive performance of carbonized wood

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wood preservation carbonizing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0039] The present invention provides a wood anticorrosive carbonization method, which includes: drying treatment, drying the cut wood step by step; carbonization treatment, heating and preheating the wood after the drying treatment, and then carbonizing; cooling and cooling, Water vapor is passed into the carbonization kiln for cooling treatment; anticorrosion treatment, the wood after the cooling treatment is soaked in an antiseptic solution; wherein, the stepwise drying includes first-stage drying, second-stage drying and third-stage drying Drying; the first-stage drying temperature is 90°C and the time is 13h; the second-stage drying temperature is 125°C and the time is 9h; the third-stage drying temperature is 150°C and the time is 9h; The preheating is to increase the temperature to 175°C at a rate of 5°C per hour; the carbonization includes first-stage carbonization, second-stage carbonization, and third-stage carbonization. The conditions of the first-stage carbonization...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a wood preservation carbonizing method. The wood preservation carbonizing method comprises the steps of drying treatment, wherein a cropped wood is subjected to step-by-step drying; carbonizing treatment, wherein the wood subjected to drying treatment is warmed and pre-heated and then carbonized; cooling for temperature reduction, wherein steam is introduced into a carbonizing kiln to carry out temperature reduction treatment; and preservative treatment is carried out, wherein the wood which is subjected to temperature reduction treatment is put into a preservative solution to be soaked. By means of the wood preservation carbonizing method, the plant preservation solution is adopted to carry out secondary preservative treatment on the carbonized wood, the preservative performance of the wood is greatly enhanced, the wood can adapt to the harsh external environment, and meanwhile preservation treatment is environmentally friendly, healthy and free of toxicity; and by arranging primary carbonizing, secondary carbonizing and tertiary carbonizing, cellulose, hemicelluloses and lignin in the wood are sufficiently carbonized, carbonizing is more sufficient, and the carbonizing effect is better.

Description

Technical field [0001] The present invention relates to the field of carbonized wood, and more specifically, to a method for preserving and carbonizing wood. Background technique [0002] Carbonized wood is a homogenous carbonization treatment of wood at high temperature without any chemical agent, so that the wood surface has a dark brown beautiful effect, and has anti-corrosion and anti-biological attack effects. Its water content is low, and it is not easy to absorb water. Stable, non-deformed, completely degreasing and non-fat spilling, good heat insulation performance, simple construction, convenient painting, no special odor, it is an ideal indoor and sauna material, becoming a new popular trend in bathroom decoration; it is anti-corrosive and insect-resistant Moth, deformation and cracking resistance, and high temperature resistance have also become ideal materials for outdoor swimming pool landscapes. However, in some harsh environments, the corrosion resistance of carbo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B27M1/06B27K3/04
CPCB27M1/06B27K3/04
Inventor 蒋忠伟汪永彬李期勇黎泽民许伟明潘瑞福王延宇许伟聪
Owner 芜湖斯塔克智能科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products