Active hydrogel, preparation method and application thereof in operative wound healing

A technology of active water and gel, applied in the field of damaged muscle and skin repair, can solve the problems of high brittleness, insufficient mechanical properties and weak water holding capacity of chitosan, and achieves simple preparation process, improved regeneration effect, and good mechanical properties. the effect of strength

Inactive Publication Date: 2017-10-20
北京恒峰铭成生物科技有限公司
View PDF8 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chitosan has a wide range of sources and is easy to prepare. It is the only hydrophilic poplar ion polymer in nature. It has good film-forming properties and hygroscopicity. It also has the characteristics of good biocompatibility, antibacterial properties and biodegradability. The hydrogel prepared with it has many unique features, but the chitosan gel is more brittle, weaker in viscoelasticity, insufficient in mechanical properties and weaker in water holding capacity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Active hydrogel, preparation method and application thereof in operative wound healing
  • Active hydrogel, preparation method and application thereof in operative wound healing
  • Active hydrogel, preparation method and application thereof in operative wound healing

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0042] The present invention will be described in further detail below in conjunction with the accompanying drawings and embodiments, so that those skilled in the art can implement it with reference to the description.

[0043] It should be understood that terms such as "having", "comprising" and "including" used herein do not exclude the presence or addition of one or more other elements or combinations thereof.

[0044] The invention provides an active hydrogel, which is prepared by adding chitosan-hyaluronic acid composite gel to the conditioned medium of adipose-derived mesenchymal stem cells, mixing evenly and adding type I collagen. The gel is used to repair muscle and skin defects caused by surgical trauma.

[0045] The following will introduce the preparation process of the active hydrogel in detail:

[0046] 1. Preparation of conditioned medium for adipose-derived mesenchymal stem cells: preparing conditioned medium for adipose-derived mesenchymal stem cells by prepa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an active hydrogel and a preparation method thereof. The method comprises the following steps: by taking rat groin adipose tissues without capillary and muscular tissues as raw materials, preparing an adipose tissue-derived stromal cell conditional medium; by taking chitosan and hyaluronic acid as raw materials, performing cross-linking reaction on chitosan and hyaluronic acid under the effect of a cross-linking agent glutaraldehyde, thereby preparing a chitosan-hyaluronic acid compound gel; and fully mixing the adipose tissue-derived stromal cell conditional medium and the chitosan-hyaluronic acid compound gel, adhering the active factors of the adipose tissue-derived stromal cell conditional medium to the chitosan-hyaluronic acid compound gel, adding I type collagen and uniformly mixing, thereby acquiring the active hydrogel. The active hydrogel provided by the invention can be used for repairing the skin and muscle injury in operative wound, the regeneration effect of the skin and muscle can be greatly promoted and the active hydrogel is convenient in a use process, high in safety, simple in preparation method and easy in industrialization.

Description

technical field [0001] The present invention relates to the technical field of damaged muscle and skin repair, more specifically, the present invention relates to a kind of active hydrogel, the present invention also relates to a kind of preparation method of active hydrogel, the present invention also relates to an active hydrogel Application of glue in surgical wound repair. Background technique [0002] Surgical trauma is the destruction of human tissues or organs after surgery. Surgical trauma can result in substantial loss of skeletal muscle and disruption of native tissue architecture. For muscle loss, current therapies mainly include surgical muscle flap transplantation, physical therapy and rehabilitation, but cannot effectively restore function. And the limitation and rejection of donor tissue affect the success rate and prognosis of muscle flap surgery. Infection, necrosis, and difficult-to-heal wounds are also complications easily caused by surgical trauma. Co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61L27/52A61L27/20A61L27/24A61L27/36A61L27/38A61L27/60C12N5/0775
Inventor 郝好杰黄宏李梓源易军周严恒刘刚陈惠华
Owner 北京恒峰铭成生物科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products