Diatomite forming composition with hygroscopic and deodorizing functions and preparation method thereof

A technology of diatomite and composition, which is applied in the field of preparation and application of diatomite-based composite materials, can solve the problem that the diatomite molding composition has weak moisture absorption and deodorization functions and environmental purification functions, and reduces the diatomite molding composition. Purification effect, raw material formulation and manufacturing process limitations, etc., to achieve the effect of good efficiency, reduced dosage, and reduced production cost

Active Publication Date: 2017-11-03
桂林良物造环境科技有限公司
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, there are companies at home and abroad that use diatomite to add composite materials to manufacture various molding composition products, but there are still certain limitations in raw material formulations and manufacturing processes, which affect the application effect.
First of all, the diatomite molding composition must first be hot-pressed at a higher temperature, and then calcined at a high temperature to obtain the diatomite molding composition, so that the temperature has a greater adverse effect on the purifying agent, which not only reduces the diatomite molding The purifying effect of the composition, and make the cost of preparation higher; Secondly, the purifying agent for preparing the deodorizing diatomite composite material is mostly composed of tablet core and coating covering the tablet core, and the coating is mainly composed of nano-titanium dioxide, diatomaceous earth Composed of soil composite catalytic material and redispersible latex powder, the catalytic efficiency is low, which makes the moisture absorption and deodorization function and environmental purification function of the prepared diatomite molding composition weak

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Diatomite forming composition with hygroscopic and deodorizing functions and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Embodiment 1: Preparation of diatomite molding composition

[0029] The formula is: the weight percentage of each component of the diatomite molding composition is composed of: 5% of diatomite with a particle size of 25 μm, 5% of tourmaline powder with a particle size of 25 μm, 1% of an inorganic purifier, and an acrylic resin adhesive 0.1%, and the balance is gypsum powder with a particle size of 25 μm. The preparation method of the inorganic purifying agent is: uniformly mixing the inorganic functional material and the noble metal catalyst to obtain a mixture and cooling the mixture to 0°C, and then adding the mixture to the high-speed airflow impact In the type powder surface treatment machine, react for 15s under the air velocity of 800 m / s, take out the mixture and cool it to room temperature, and the cooling rate is 10°C / s, and the inorganic purifier can be prepared; the inorganic functional material is nano A mixture of alumina powder and nano silica powder, wher...

Embodiment 2

[0035] Embodiment 2: Preparation of diatomite molding composition

[0036] The formula is: the weight percentage of each component of the diatomite molding composition is composed of: 40% of diatomite with a particle size of 35 μm, 20% of tourmaline powder with a particle size of 35 μm, 5% of inorganic purifier, acrylic resin adhesive 1.0%, and the balance is gypsum powder with a particle size of 35 μm. The preparation method of the inorganic purifying agent is: uniformly mixing the inorganic functional material and the noble metal catalyst to obtain a mixture and cooling the mixture to 5° C., and then adding the mixture to the high-speed airflow impact In a type powder surface treatment machine, react for 18s under the condition of an airflow velocity of 850 m / s, take out the mixture and cool it to room temperature, and the cooling rate is 15°C / s, and the inorganic purifier can be prepared; the inorganic functional material is a nano A mixture of alumina powder and nano-silic...

Embodiment 3

[0042] Embodiment 3: Preparation of diatomite molding composition

[0043] The formula is: the weight percentage of each component of the diatomite molding composition is composed of: 10% of diatomite with a particle size of 30 μm, 10% of tourmaline powder with a particle size of 30 μm, 2% of an inorganic purifier, and an acrylic resin adhesive 0.5%, and the balance is gypsum powder with a particle size of 30 μm. The preparation method of the inorganic purifying agent is: uniformly mixing the inorganic functional material and the noble metal catalyst to obtain a mixture and cooling the mixture to 2 ° C, and then adding the mixture to the high-speed air flow impact In the type powder surface treatment machine, react for 16s under the air velocity of 820 m / s, take out the mixture and cool it to room temperature, and the cooling rate is 12°C / s, and the inorganic purifier can be prepared; the inorganic functional material is nano A mixture of alumina powder and nano-silica powder,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a diatomite forming composition with hygroscopic and deodorization functions and a preparation method thereof. The diatomite forming composition is prepared from the following components in percentage by weight: 5% to 40% of diatomite, 5% to 20% of tourmaline powder, 1% to 5% of inorganic cleaning agent, 0.1% to 1.0% of acrylic resin adhesive, and the balance of gypsum powder; the inorganic cleaning agent is composite powder prepared by attaching precious metal catalysts to layered inorganic functional materials. According to the diatomite forming composition with the hygroscopic and deodorizing functions and the preparation method thereof, the diatomite forming composition can effectively eliminate harmful gases when the concentration of harmful aldehydes, ammonia and benzene gases is relatively low, instant effectiveness is good, and the purpose of purification in a short time can be achieved; the diatomite forming composition has a relatively strong adsorption capacity of moisture and a strong hygroscopic effect; the diatomite forming composition has a simple production process and a strong purification effect, and is easy to industrial production.

Description

technical field [0001] The invention relates to the technical field of preparation and application of diatomite-based composite materials, in particular to a diatomite molding composition with moisture absorption and deodorization functions and a preparation method thereof. Background technique [0002] Diatomaceous earth is a kind of porous biological siliceous rock formed after the accumulation and deposition of the remains of diatoms, the remains of ancient single-celled lower plants, through preliminary diagenesis. It is composed of the shell of diatoms, on which there are many levels, a large number of micropores arranged in an orderly manner, and diatomaceous earth has the characteristics of small density, large specific surface area, good adsorption, acid resistance, alkali resistance, insulation, etc. Characteristics, its unique surface structure and excellent adsorption performance are suitable for use as adsorption materials, and China's diatomite mineral resources...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14C04B26/06C04B41/85
CPCC04B26/06C04B28/14C04B41/009C04B41/5012C04B41/5122C04B41/85C04B2111/00025C04B14/08C04B14/041C04B22/04C04B14/303C04B14/06C04B22/12C04B41/4535
Inventor 韦仲华韦冬芳韦宇洪
Owner 桂林良物造环境科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap