Manufacturing and firing method of jun porcelain ancient egg-shaped and holed wind instrument

A technology of porcelain xun and sound hole, which is applied in the field of ceramics, can solve the problems of difficult to control the pitch and timbre of the ceramic xun, and the influence of the pitch and timbre of the ceramic xun is very large, so as to achieve a good surface decoration effect, improve the artistic appreciation, and slow down the shrinkage. Effect

Inactive Publication Date: 2017-11-24
PINGDINGSHAN UNIVERSITY
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention provides a method for making and firing Jun porcelain Xun, which solves the problem that the pitch and timbre of the ceramic Xun in the prior art are greatly affected by the raw material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing and firing method of jun porcelain ancient egg-shaped and holed wind instrument
  • Manufacturing and firing method of jun porcelain ancient egg-shaped and holed wind instrument

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0035] Example 1

[0036] A kind of production and firing method of Jun porcelain Xun, its technological process see figure 1 , The specific implementation is as follows:

[0037] Step 1, mud making

[0038] Step 1.1: Weigh 40 parts of kaolin, 10 parts of soda stone, 15 parts of wood knot clay, 5 parts of quartz sand, 0.5 parts of vermiculite, 1 part of plant ash, 2 parts of sodium alginate, and 0.5 parts of phenolic resin powder according to parts by weight;

[0039] Step 1.2, pulverize the raw materials weighed in step 1.1 and mix to obtain a mixture, put the mixture into a ball mill, and then add water of the same quality as the mixture into the ball mill, and grind until the mixture has a fineness of 250 mesh, and The sieve residue is 0.1%, and the ground mud is obtained, and the ground mud is allowed to stand for 24 hours before use;

[0040] Step 2, billet making

[0041] Put the mud prepared in step 1.2 in a vacuum machine, extract the air from the mud, and then pour the air-exh...

Example Embodiment

[0056] Example 2

[0057] A kind of production and firing method of Jun porcelain Xun, its technological process see figure 1 , The specific implementation is as follows:

[0058] Step 1, mud making

[0059] Step 1.1, weigh out 45 parts of kaolin, 8 parts of soda stone, 12 parts of Knot clay, 10 parts of quartz sand, 1 part of vermiculite, 1 part of plant ash, 1.5 parts of sodium alginate, and 1 part of phenolic resin powder according to parts by weight;

[0060] Step 1.2, pulverize the raw materials weighed in step 1.1 and mix to obtain a mixture, put the mixture into a ball mill, and then add water of the same quality as the mixture into the ball mill, and grind until the mixture has a fineness of 250 mesh, and The residue on the sieve is 0.15% to obtain a ground mud, and the ground mud is allowed to stand for 24 hours before use;

[0061] Step 2, billet making

[0062] Place the slurry prepared in step 1.2 in a vacuum machine, extract the air from the slurry, and then pour the evacu...

Example Embodiment

[0075] Example 3

[0076] A kind of production and firing method of Jun porcelain Xun, its technological process see figure 1 , The specific implementation is as follows:

[0077] Step 1, mud making

[0078] Step 1.1: Weigh 50 parts of kaolin, 5 parts of soda stone, 10 parts of Knot clay, 12 parts of quartz sand, 0.5 part of vermiculite, 2 parts of plant ash, 2 parts of sodium alginate, and 1 part of phenolic resin powder according to parts by weight;

[0079] Step 1.2, pulverize the raw materials weighed in step 1.1 and mix to obtain a mixture, put the mixture into a ball mill, and then add water of the same quality as the mixture into the ball mill, and grind until the mixture has a fineness of 250 mesh, and The sieve residue is 0.2%, and the ground mud is obtained, and the ground mud is allowed to stand for 24 hours before use;

[0080] Step 2, billet making

[0081] Put the mud prepared in step 1.2 in a vacuum machine, extract the air in the mud, and then pour the air-exhausted mud...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a manufacturing and firing method of jun porcelain ancient egg-shaped and holed wind instrument. The method comprises the following steps: preparing clay, preparing a blank, biscuit firing, glazing, sintering, and detecting sound. Raw materials for preparing the clay consist of the following components in parts by weight: 40 to 50 parts of kaolin, 5 to 10 parts of alkaline stone, 10 to 15 parts of knot clay, 5 to 10 parts of quartz sand, 0.5 to 1 part of vermiculite, 1 to 2 parts of plant ash, 1 to 2 parts of sodium alginate, and 0.5 to 1 part of phenolic resin powder. A gradually heating multi-sectional heating way is adopted both in the biscuit firing process and the sintering process, so that the blank is slowly heated, the heating non-uniformity and stress change caused by the sudden change of the temperature can be avoided, so that cracks and crease on the surface of the jun porcelain ancient egg-shaped and holed wind instrument can be avoided, and the artistic ornamental value of the jun porcelain ancient egg-shaped and holed wind instrument can be improved; and moreover, the jun porcelain ancient egg-shaped and holed wind instrument fired by the invention is rigid in structure and unlikely to crack, the sound produced by the instrument is strong and ebb and flow, steady and dense and has penetration powder, and the playing requirement of the porcelain jun ancient egg-shaped and holed wind instrument can be met.

Description

technical field [0001] The invention belongs to the technical field of ceramics, and in particular relates to a method for making and firing a Jun porcelain xun. Background technique [0002] Xun is an ancient wind instrument, invented about 7,000 years ago. Its main development process was in the Shang and Zhou dynasties, so its timbre obviously has the unique spiritual temperament of the Shang and Zhou dynasties: simple, vigorous, deep, vicissitudes, mysterious, and mournful. Therefore, Xun is particularly good at expressing sorrow and making solemn, ancient, The terrible special effects have been loved by people since ancient times. [0003] The traditional pottery xun is drop-shaped or bullet-shaped, and is mostly hand-made by artisans using the casting process. Because its intonation and timbre are greatly affected by the raw materials, production process and firing process, and the clay will shrink to a certain extent after being heated into a pottery xun, making it ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B38/06C04B38/08C04B33/04C04B33/13C04B33/24C04B33/32
CPCC04B33/04C04B33/1305C04B33/131C04B33/24C04B33/32C04B38/067C04B38/08C04B2235/3418C04B2235/3427
Inventor 谭嫄刘松涛
Owner PINGDINGSHAN UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka