Composite board and preparation method thereof

A composite material board and composite material layer technology, which is applied in the field of composite material board and its preparation, can solve the problems of impact resistance, poor wear resistance and anti-aging performance, and the appearance is not beautiful enough to achieve improved peel strength and high mechanical strength. The effect of strength and excellent impact resistance

Pending Publication Date: 2018-01-12
GUANGZHOU KINGFA CARBON FIBER NEW MATERIALS DEV
View PDF8 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the impact resistance, wear resistance, and aging resistance of this product are poor, and the appearance is not beautiful enough, so it is limited in application fields such as refrigerated car wall panels and building wall panels.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite board and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Such as figure 1 As shown, a composite material plate includes a composite material layer 4, and also includes an upper adhesive layer 3 and a lower adhesive layer 5 bonded to the upper and lower surfaces of the composite material layer 4 respectively, and the upper adhesive layer and the upper adhesive layer 3 The functional surface layer 2 that is bonded to the upper surface as one, also includes the protective layer 1 that is bonded to the upper surface of the functional surface layer 2, and the thickness of the composite material board is 1.6mm; the composite material layer consists of 3 layers, according to the / 90° / 0° layered unidirectional prepreg composition; the thickness of the unidirectional prepreg is 0.3mm, and the surface density is 420g / m 2 , is a continuous non-alkali glass fiber reinforced polypropylene composite sheet made of continuous non-alkali glass fiber through a molten resin system, fully pre-impregnated, and cooled, based on the total weight of...

Embodiment 2

[0040] A composite material board, comprising a composite material layer 4, and an upper adhesive layer 3 and a lower adhesive layer 5 bonded to the upper and lower surfaces of the composite material layer 4 respectively, and an upper surface of the upper adhesive layer 3 A functional surface layer 2 that is bonded as one; also includes a protective layer 1 bonded to the upper surface of the functional surface layer 2, and the thickness of the composite material plate is 1.2mm; the composite material layer is composed of 3 layers, according to 0° / Composed of unidirectional prepreg sheets with 90° / 0° layup; the thickness of the unidirectional prepreg sheets is 0.25mm, and the areal density is 375g / m 2 , is a continuous medium-alkali glass fiber reinforced polyethylene composite sheet made of continuous medium-alkali glass fiber through a molten resin system, fully pre-impregnated, and cooled, based on the total weight of the continuous medium-alkali glass fiber-reinforced polye...

Embodiment 3

[0043] A composite material board, comprising a composite material layer 4, and an upper adhesive layer 3 and a lower adhesive layer 5 bonded to the upper and lower surfaces of the composite material layer 4 respectively, and an upper surface of the upper adhesive layer 3 A bonded functional surface layer 2; the thickness of the composite material plate is 1.0mm; the composite material layer is composed of 2 layers of unidirectional prepreg laminated according to 0° / 90°; the unidirectional The prepreg has a thickness of 0.25mm and an areal density of 375 g / m 2 , is a continuous high-alkali glass fiber reinforced polypropylene sheet made of continuous high-alkali glass fiber through a molten resin system, fully pre-impregnated, and cooled, based on the total weight of continuous high-alkali glass fiber-reinforced polypropylene, continuous high-alkali glass fiber The weight percentage is 70wt%; the surface density of the upper adhesive layer 3 is 15g / m 2 The spunlace polybutyle...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a composite board, comprising a composite layer, an upper adhesive layer and a lower adhesive layer respectively bonded with the upper and lower surfaces of the composite layerto form an integral body with the composite layer, and a functional surface layer bonded with the upper surface of the upper adhesive layer to form an integral body with the upper adhesive layer. According to the invention, the upper adhesive layer and the lower adhesive layer respectively cover the upper and lower surfaces of the composite layer, and the functional surface layer is laminated with the upper surface of the upper adhesive layer via a film spraying method, so the prepared composite board has excellent impact resistance and the advantages of high mechanical strength, ageing resistance, scratch resistance, etc.; meanwhile, the functional surface layer endows the composite board with unique appearance and functionality; moreover, since one part of the upper adhesive layer is embedded into the upper surface of the composite layer and another part of the upper adhesive layer is embedded into the lower surface of the functional surface layer, such mechanical bonding can improve peeling strength between the functional surface layer and the composite layer; and the lower adhesive layer may be embedded into the lower surface of the composite layer so as to realize bonding between the composite board and other materials.

Description

technical field [0001] The invention relates to the field of composite material panels, in particular to a composite material panel and a preparation method thereof. Background technique [0002] At present, special transportation facilities such as refrigerated containers, refrigerated trucks, trucks, and RVs generally use steel plates or thermosetting composite material plates as inner linings or wall panels. Repair, high thermal conductivity, poor heat insulation effect. The thermosetting plastic composite lining board has high gloss and smooth appearance, but it has poor impact resistance, is easy to crack and scratch, and has poor cleaning performance. At the same time, food processing factories, breweries, pharmaceutical factories and other processing plants, school cafeterias, hospitals, hotels and other public places are required to have antibacterial and mildew-proof, waterproof and moisture-proof, and easy-to-clean functions, while ordinary walls are prone to foam...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B27/02B32B27/12B32B7/06B32B9/00B32B9/04B32B27/34B32B37/02B32B37/06B32B37/10B32B37/12B32B38/16
CPCB32B5/16B32B7/10B32B17/02B32B27/04B32B27/30B32B33/00
Inventor 黄险波陈大华范欣愉孙雅杰黄有平刘玲陈涛李晓拓熊鑫肖彦孟姗姗雷震徐光磊
Owner GUANGZHOU KINGFA CARBON FIBER NEW MATERIALS DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap