Cobalt carbonate high-temperature purple ceramic glaze and preparation method thereof

A technology of cobalt carbonate and ceramic glaze, applied in the field of ceramics, can solve the problems of unsatisfactory and stable color development effect, and achieve the effects of improving the smoothness of the glaze surface, reducing the firing temperature, and increasing the viscosity of the glaze

Active Publication Date: 2018-01-16
广东嘉联企业陶瓷有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Purple ceramic glaze has always been a color glaze that is very difficult to fire, and the color development effect has not been ideal and stable for a long time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A cobalt carbonate high-temperature purple ceramic glaze is prepared by first preparing a cobalt carbonate high-temperature purple ceramic glaze, and then glazing and high-temperature sintering to obtain a cobalt carbonate high-temperature purple ceramic glaze, wherein the cobalt carbonate high-temperature purple ceramic glaze contains raw materials and various The mass percentage of raw material is:

[0035] Nepheline syenite 33.2%, chalk powder 6.8%, silicon dioxide 14.5%, calcined kaolin 25%, dolomite 15%, zinc oxide 5.8%, cobalt carbonate 2%.

[0036] A method for preparing a cobalt carbonate high-temperature purple ceramic glaze, comprising the following steps: firstly preparing a cobalt carbonate high-temperature purple ceramic glaze, glazing and sintering to obtain a cobalt carbonate high-temperature purple ceramic glaze; wherein, the preparation of the cobalt carbonate high-temperature purple ceramic glaze Methods as below:

[0037] Step 1, preparation of cobal...

Embodiment 2

[0043]A cobalt carbonate high-temperature purple ceramic glaze is prepared by first preparing a cobalt carbonate high-temperature purple ceramic glaze, and then glazing and high-temperature sintering to obtain a cobalt carbonate high-temperature purple ceramic glaze, wherein the cobalt carbonate high-temperature purple ceramic glaze contains raw materials and various The mass percentage of raw material is:

[0044] Nepheline syenite 30%, chalk powder 7%, silica 20%, calcined kaolin 18%, dolomite 15%, zinc oxide 7%, cobalt carbonate 3%.

[0045] A method for preparing a cobalt carbonate high-temperature purple ceramic glaze, comprising the following steps: firstly preparing a cobalt carbonate high-temperature purple ceramic glaze, glazing and sintering to obtain a cobalt carbonate high-temperature purple ceramic glaze; wherein, the preparation of the cobalt carbonate high-temperature purple ceramic glaze Methods as below:

[0046] Step 1, preparation of cobalt carbonate high t...

Embodiment 3

[0051] A cobalt carbonate high-temperature purple ceramic glaze is prepared by first preparing a cobalt carbonate high-temperature purple ceramic glaze, and then glazing and high-temperature sintering to obtain a cobalt carbonate high-temperature purple ceramic glaze, wherein the cobalt carbonate high-temperature purple ceramic glaze contains raw materials and various The mass percentage of raw material is:

[0052] Nepheline syenite 33.2%, chalk powder 6.8%, silicon dioxide 16.5%, calcined kaolin 22%, dolomite 13.7%, zinc oxide 5.8%, cobalt carbonate 2%.

[0053] The cobalt carbonate high-temperature purple ceramic glaze also contains manganese dioxide, and the mass of manganese dioxide accounts for the total of (nepheline syenite+chalk powder+silica+calcined kaolin+dolomite+zinc oxide+cobalt carbonate) The mass percentage of mass is 2%.

[0054] The function of adding manganese dioxide to the cobalt carbonate high-temperature purple ceramic glaze is that it can promote the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a cobalt carbonate high-temperature purple ceramic glaze and a preparation method thereof and belongs to the field of ceramics. The cobalt carbonate high-temperature purple ceramic glaze is prepared by firstly preparing a cobalt carbonate high-temperature purple ceramic glaze material and by further performing glazing and high-temperature sintering. The cobalt carbonate high-temperature purple ceramic glaze material comprises the following raw materials in percentage by mass: 30-35% of nepheline syenite, 6-7% of chalk powder, 14.5-18.5% of silicon dioxide, 18-25% of calcined kaolin, 12-15% of dolomite, 4-7% of zinc oxide and 1-3% of cobalt carbonate. By adopting the method, the ceramic glaze has a color effect of light lavender purple and a surface smooth effect athigh temperature, and meanwhile physical and chemical property stability of the ceramic glaze is achieved. The formula of the glaze is adjusted and tested for multiple times for a long time, long-termtests at minus 30 DEG C show that no glaze cracking or dropping phenomenon is caused, and the glaze is resistant to common acid / alkali corrosion.

Description

technical field [0001] The invention relates to the technical field of ceramics, in particular to a cobalt carbonate high-temperature purple ceramic glaze and a preparation method thereof. Background technique [0002] Ceramic glaze is an important raw material that must be used in the production of ceramics. It has a strong protective effect on the ceramic body. At the same time, the physical properties of silicate make the glass enamel on the ceramic surface effectively resistant to acid and alkali corrosion. Very good antibacterial properties. Ordinary ceramic color glazes are achieved by adding metal colorants to the glass enamel to achieve color development during the firing process. Such glaze colors are often single in color and cannot highlight the artistic beauty of the ceramic color glaze itself and the high-temperature firing process. special artistic effects produced in Cobalt carbonate high-temperature purple ceramic glaze effectively overcomes the shortcoming...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C8/14C04B41/86
Inventor 沈海泳李菲
Owner 广东嘉联企业陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com