Bamboo charcoal adsorption environment-friendly waterborne polyurethane wall cloth

A water-based polyurethane, environmentally friendly technology, used in polyurea/polyurethane coatings, antifouling/underwater coatings, coatings, etc., to achieve the effect of strong operability, good air permeability and cost saving

Inactive Publication Date: 2018-02-09
遂昌玄乐炭复合材料有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] "Nanchang University" 2011 master's thesis "Exploration of Aqueous Polyurethane Acid Bath Coagulation Film Formation" paper discloses the use of acetic acid to foam water-based polyurethane emulsion to prepare synthetic leather, but also discloses that the surface and cross-section of WPU acid bath demulsification method have There are many microporous structures, among which the microporous structure without wood powder is richer than that with added wood powder, but no matter which one, compared with the solvent-based PU wet method, the microporous structure is still quite different. Therefore, WPU acid bath demulsification method needs further research from theory to practice

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bamboo charcoal adsorption environment-friendly waterborne polyurethane wall cloth

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

margin

[0048] A kind of production method of environment-friendly type imitation leather water-based polyurethane wall covering, this method comprises the following steps:

[0049] 1) The base cloth is soaked in bamboo vinegar solution before scraping, and the pH of the bamboo vinegar solution is 3.5, so that the base cloth is soaked in bamboo vinegar solution, and then squeezed dry;

[0050] 2) The base cloth is scraped and coated with the above-mentioned water-based polyurethane coating, solidified on the surface of the base cloth to form a water-based polyurethane layer, and squeezed dry;

[0051] 3) After being squeezed dry, enter the bamboo vinegar solution for foaming. The pH of the bamboo vinegar solution is 3.2, and the foaming time is 2 minutes to form a porous polyurethane coating. The coating amount of the water-based polyurethane layer is 40g / m 2 ;

[0052] 4) After foaming, wash with water and dry to obtain the water-based polyurethane wall covering.

[...

Embodiment 2

margin

[0100] A kind of production method of environment-friendly type imitation leather water-based polyurethane wall covering, this method comprises the following steps:

[0101] 1) The base cloth is soaked in bamboo vinegar solution before scraping, and the pH of the bamboo vinegar solution is 3.5, so that the base cloth is soaked in bamboo vinegar solution, and then squeezed dry;

[0102] 2) The base cloth is scraped and coated with the above-mentioned water-based polyurethane coating, solidified on the surface of the base cloth to form a water-based polyurethane layer, and squeezed dry;

[0103] 3) After being squeezed dry, enter the bamboo vinegar solution for foaming. The pH of the bamboo vinegar solution is 3.2, and the foaming time is 2 minutes to form a porous polyurethane coating. The coating amount of the water-based polyurethane layer is 40g / m 2 ;

[0104] 4) After foaming, wash with water and dry to obtain the water-based polyurethane wall covering.

[...

Embodiment 3

margin

[0115] A kind of production method of environment-friendly type imitation leather water-based polyurethane wall covering, this method comprises the following steps:

[0116] 1) The base cloth is soaked in bamboo vinegar solution before scraping, and the pH of the bamboo vinegar solution is 3.5, so that the base cloth is soaked in bamboo vinegar solution, and then squeezed dry;

[0117] 2) The base cloth is scraped and coated with the above-mentioned water-based polyurethane coating, solidified on the surface of the base cloth to form a water-based polyurethane layer, and squeezed dry;

[0118] 3) After being squeezed dry, enter the bamboo vinegar solution for foaming. The pH of the bamboo vinegar solution is 3.2, and the foaming time is 2 minutes to form a porous polyurethane coating. The coating amount of the water-based polyurethane layer is 40g / m 2 ;

[0119] 4) After foaming, wash with water and dry to obtain the water-based polyurethane wall covering.

[...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the field of wall cloth, and especially relates to a bamboo charcoal adsorption environment-friendly waterborne polyurethane wall cloth. The bamboo charcoal adsorption environment-friendly waterborne polyurethane wall cloth is prepared via foaming with bamboo vinegar; the tensile strength, tear resistance, and wear resistance are improved to achieve that of products obtained via DMF wet foaming; the obtained products are excellent in handfeel, fine in texture, excellent in permeability and sound insulation performance; no DMF is adopted in the whole production process; water is taken as a solvent; flame resistance is achieved; the obtained bamboo charcoal adsorption environment-friendly waterborne polyurethane wall cloth is safe, is friendly to the environment, and is low in cost; no formaldehyde or DMF is detected in the obtained bamboo charcoal adsorption environment-friendly waterborne polyurethane wall cloth; and requirements on ecological waterborne polyurethane wall cloth are achieved. The operationality of the technology is high, production efficiency is high, cost is low, and environment protection and industrialized large scale production are realized.

Description

technical field [0001] The invention relates to the field of wall coverings, in particular to a bamboo charcoal adsorption and environment-friendly water-based polyurethane wall covering. Background technique [0002] There are many kinds of interior wall decoration materials in the domestic market. Among them, the wallpaper wall cloth constructed by pasting technology has gradually replaced the paint because of its strong decoration and convenient construction. Clothed with a layer of PVC material, it is easy to warp and mold, crack and degumming after a long time. Ordinary wall coverings are easy to deform and stain because they are made of fabric, and have a short service life. They are not suitable for places with large traffic such as hotels. Thereby be badly in need of a kind of environmental protection life-span is long, sound insulation effect is good, the wall covering of exquisite appearance. [0003] Polyurethane synthetic leather has soft and natural luster, sof...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C09D197/02C09D5/14C09D5/18C09D7/65C09D7/63C09D7/61C08J9/04D06N3/14D06N3/00
CPCC09D175/04C08J9/04C08J2375/04C08K2003/2241C08K2003/265C08K2201/011C08L2201/02C08L2205/035C09D5/14C09D5/18D06N3/0043D06N3/0063D06N3/0088D06N3/14D06N2211/063C08L97/02C08L83/04C08L91/06C08K13/02C08K3/26C08K5/053C08K3/22
Inventor 管宁章管玄谢永水
Owner 遂昌玄乐炭复合材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka