Carded woolen adhesive agent pigment printing fabric
A technology of pigment printing and printing paste, applied in the field of printing fabrics, can solve the problems of poor printing color fastness and rough cloth surface, and achieve the effect of high printing color fastness and single color pattern change.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0044] A carded wool glue paint printing fabric is prepared by the following method:
[0045] Step 1: Select 66 counts of sheep cashmere as raw material, and spin cashmere and polyester into 13.5 s / 1 for the 750G / M wool-polyester blended fake double-layer fabric developed and produced by Jingwei;
[0046] Step 2: The fabric is pre-treated, dyed and washed in sequence;
[0047] Step 3: Apply the printing paste to the fabric for printing, and use the flat screen printing process for printing, and the mesh of the flat screen printing is 150 mesh;
[0048] Step 4: Control the drying temperature to 120°C, the baking temperature to 170°C, and the baking time to 90s, and then perform drying and baking in sequence;
[0049] The printing paste comprises the following components by weight:
[0050] 5 parts of guar gum, 1 part of urea, 15 parts of sodium carboxymethyl cellulose, 0.5 parts of polycarboxylic acid dispersant, 70 parts of deionized water.
Embodiment 2
[0052] A carded wool glue paint printing fabric is prepared by the following method:
[0053] Step 1: Select 66 counts of sheep cashmere as raw material, and spin cashmere and polyester into 13.5 s / 1 for the 750G / M wool-polyester blended fake double-layer fabric developed and produced by Jingwei;
[0054] Step 2: The fabric is pre-treated, dyed and washed in sequence;
[0055] Step 3: Apply the printing paste to the fabric for printing, and use the flat screen printing process for printing, and the mesh of the flat screen printing is 150 mesh;
[0056] Step 4: Control the drying temperature to 120°C, the baking temperature to 170°C, and the baking time to 90s, and then perform drying and baking in sequence;
[0057] The printing paste comprises the following components by weight:
[0058] 2 parts of tamarind gum, 2 parts of urea, 16 parts of polyvinyl alcohol, 0.7 parts of polycarboxylic acid dispersant, 55 parts of deionized water.
Embodiment 3
[0060] A carded wool glue paint printing fabric is prepared by the following method:
[0061] Step 1: Select 66 counts of sheep cashmere as raw materials, and spin cashmere and polyester into 13.5s / 1 750G / M wool-polyester blended false double-layer fabric developed and produced by warp and weft;
[0062] Step 2: The fabric is pre-treated, dyed and washed in sequence;
[0063] Step 3: Apply the printing paste to the fabric for printing, and use the flat screen printing process for printing, and the mesh of the flat screen printing is 150 mesh;
[0064] Step 4: Control the drying temperature to 120°C, the baking temperature to 170°C, and the baking time to 90s, and then perform drying and baking in sequence;
[0065] The printing paste comprises the following components by weight:
[0066] 3 parts of sodium alginate, 3 parts of urea, 17 parts of sodium carboxymethyl cellulose, 1 part of polycarboxylic acid dispersant, 50 parts of deionized water.