High-strength waterproof building material and preparation method thereof

A waterproof building material and high-strength technology, applied in the field of waterproof building materials, can solve problems affecting building quality, loose texture, insufficient strength, etc., and achieve the effect of simple preparation method, enhanced strength, and favorable market promotion

Inactive Publication Date: 2018-04-24
牛霞光
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing waterproof building materials have the disadvantages of loose texture and insufficient strength, which easily affect the overall building quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A high-strength waterproof building material, comprising the following raw materials in parts by weight: 200 parts of polyethylene resin, 11 parts of zinc oxide, 6 parts of tigelic acid, 5 parts of quartz sand, 4 parts of calcium carbonate, 5 parts of basalt fiber, calcined silicon 3 parts of algae earth, 4 parts of cement, 3 parts of fly ash, 3 parts of steel slag powder, 5 parts of corn starch, 2 parts of expanded vermiculite, 3 parts of river mud, and 5 parts of rosin.

[0017] A method for preparing a high-strength waterproof building material, comprising the following steps: (1) Weighing polyethylene resin, zinc oxide, tigelic acid, quartz sand, calcium carbonate, basalt fiber, calcined diatomite, cement, powder Coal ash, steel slag powder, corn starch, expanded vermiculite, river mud and rosin, for later use; (2) Preparation of calcined diatomite: put diatomite in a muffle furnace, calcinate at 700°C for 1 hour, take it out and cool , and then ground to 200 mesh; ...

Embodiment 2

[0019] A high-strength waterproof building material, comprising the following raw materials in parts by weight: 300 parts of polyethylene resin, 25 parts of zinc oxide, 10 parts of tigelic acid, 10 parts of quartz sand, 8 parts of calcium carbonate, 15 parts of basalt fiber, calcined silicon 8 parts of algae earth, 15 parts of cement, 8 parts of fly ash, 7 parts of steel slag powder, 11 parts of corn starch, 5 parts of expanded vermiculite, 8 parts of river mud, and 10 parts of rosin.

[0020] A method for preparing a high-strength waterproof building material, comprising the following steps: (1) Weighing polyethylene resin, zinc oxide, tigelic acid, quartz sand, calcium carbonate, basalt fiber, calcined diatomite, cement, powder Coal ash, steel slag powder, corn starch, expanded vermiculite, river mud and rosin, for later use; (2) Preparation of calcined diatomite: put diatomite in a muffle furnace, calcinate at 900°C for 2 hours, take it out and cool , and then ground to 300...

Embodiment 3

[0022] A high-strength waterproof building material, comprising the following raw materials in parts by weight: 250 parts of polyethylene resin, 18 parts of zinc oxide, 8 parts of tigelic acid, 7 parts of quartz sand, 6 parts of calcium carbonate, 10 parts of basalt fiber, calcined silicon 5 parts of algae earth, 6 parts of cement, 5 parts of fly ash, 5 parts of steel slag powder, 7 parts of corn starch, 4 parts of expanded vermiculite, 5 parts of river mud, and 7 parts of rosin.

[0023] A method for preparing a high-strength waterproof building material, comprising the following steps: (1) Weighing polyethylene resin, zinc oxide, tigelic acid, quartz sand, calcium carbonate, basalt fiber, calcined diatomite, cement, powder Coal ash, steel slag powder, corn starch, expanded vermiculite, river mud and rosin, for later use; (2) Preparation of calcined diatomite: put the diatomite in a muffle furnace, calcinate at 800°C for 1.5h, take it out Cool, then grind to 250 mesh; (3) Mix...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-strength waterproof building material. The material is prepared from, by weight, 200-300 parts of polyethylene resin, 11-25 parts of zinc oxide, 6-10 parts of tiglic acid, 5-10 parts of quartz sand, 4-8 parts of calcium carbonate, 5-15 parts of basalt fiber, 3-8 parts of calcined diatomite, 4-15 parts of cement, 3-8 parts of coal ash, 3-7 parts of steel slag micropowder, 5-11 parts of corn starch, 2-5 parts of expanded vermiculite, 3-8 parts of river mud and 5-10 parts of rosin. The waterproof building material achieves the synergistic effect through raw materialcompounding, the strength of the material can be effectively enhanced, the phenomenon of bubbling or cracking is avoided, and the preparation method is simple and beneficial to market popularization.

Description

technical field [0001] The invention relates to a waterproof building material, in particular to a high-strength waterproof building material and a preparation method thereof. Background technique [0002] In the prior art, the enclosure structure of the building should prevent the infiltration of rainwater, snowwater and groundwater; it should prevent the erosion of moisture, steam and other harmful gases and liquids in the air; the separation structure should prevent the seepage of water supply and drainage . These anti-penetration, leakage and erosion materials are collectively referred to as waterproof materials. [0003] Building waterproofing is the measures taken from the building materials and structure to prevent water from penetrating certain parts of the building. Waterproofing is mostly used in roofs, underground buildings, underground parts of buildings, inner chambers and water storage structures that need to be waterproofed. According to the different measu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L3/02C08L93/04C08K13/06C08K9/00C08K7/26C08K3/22C08K3/36C08K7/10C08K3/34C08K3/26
Inventor 牛霞光
Owner 牛霞光
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka