LED lampshade and processing process thereof

A technology of LED lampshade and processing technology, applied in the field of lampshade, can solve problems such as difficulty in obtaining cost advantages, and achieve the effect of excellent uniform light effect, good uniform light effect and convenient processing.

Inactive Publication Date: 2018-05-15
曹结宾
View PDF8 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the prior art, in order to improve the atomization effect of the LED lampshade and increase the light transmittance, technicians have proposed many solutions, such as the application number "201010139330.0" and the patent name "A lampshade coating and its preparation method" The Chinese invention patent, which uses a lampshade coating, which can have a good atomization effect on the light after being coated on the inner surface of the lampshade, improve the light transmittance, and increase the luminous intensity; but this kind of molding is carried out after The method of coating is equivalent to the secondary processing of the lampshade, which not only needs to overcome the yield rate of finished products brought about by the secondary processing, but also makes it difficult to obtain cost advantages by secondary coating

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The composition formula of the LED lampshade provided by the present embodiment is:

[0029] Polycarbonate (Bayer 2805, Germany) 100 parts

[0030] PMMA resin (Sumitomo HT25X) 16 parts

[0031] MBS (Formosa Plastics M-41) 2 copies

[0032] Magnesium oxide whiskers (5 μm in diameter, 200 μm in length) 5 parts

[0033] SiO 2 (Lingshou County Hengkai Mineral Products Processing Plant, particle size 10μm) 3 parts

[0034] TiO 2 (purchased from DuPont, particle size 3μm) 6 parts

[0035] Antioxidant 1010 1.2 parts

[0036] The processing technology of the LED lampshade comprises the following steps:

[0037] (1) Take polycarbonate and PMMA resin according to the formula quantity, mix and stir in a high-speed mixer (Zhangjiagang Yongli Machinery SHR-100A) for 4min; then weigh MBS, magnesium oxide whiskers, SiO 2 and TiO 2 , Antioxidant 1010 and add it into a high-speed mixer and stir to mix evenly;

[0038] (2) The above-mentioned mixture is lowered into a twin-scre...

Embodiment 2

[0043] The composition formula of the LED lampshade provided by the present embodiment is:

[0044] Polycarbonate (Bayer 2805, Germany) 90 parts

[0045] PMMA resin (Sumitomo HT25X) 14 parts

[0046] MBS (Formosa Plastics M-41) 1.5 parts

[0047] Zinc oxide whiskers (diameter 3 μm, length 180 μm) 4 parts

[0048] SiO 2 (Lingshou County Hengkai Mineral Products Processing Plant, particle size 10μm) 2 parts

[0049] TiO 2 (purchased from DuPont, particle size 3μm) 4 parts

[0050] Antioxidant 168 1.5 parts

[0051] The processing technology of the LED lampshade comprises the following steps:

[0052] (1) Take polycarbonate and PMMA resin according to the formula amount, mix and stir in a high-speed mixer for 4min; then weigh MBS, zinc oxide whisker, SiO 2 and TiO 2 , Antioxidant 1010 and add it into a high-speed mixer and stir to mix evenly;

[0053] (2) The above-mentioned mixture is lowered into a twin-screw extruder through a feeding device, melted and mixed, drawn,...

Embodiment 3

[0058] The composition formula of the LED lampshade provided by the present embodiment is:

[0059] Polycarbonate (Bayer 2805, Germany) 110 parts

[0060] PMMA resin (Sumitomo HT25X) 18 parts

[0061] MBS (Formosa Plastics M-41) 2.5 parts

[0062] Calcium sulfate whiskers (diameter 8 μm, length 230 μm) 6 parts

[0063] SiO 2 (Lingshou County Hengkai Mineral Products Processing Plant, particle size 15μm) 3 parts

[0064] TiO 2 (purchased from DuPont, particle size 4μm) 6 parts

[0065] Antioxidant 1010 0.8 parts

[0066] The processing technology of the LED lampshade comprises the following steps:

[0067] (1) Take polycarbonate and PMMA resin according to the formula quantity, mix and stir in a high-speed mixer for 5min; then weigh MBS, calcium sulfate whiskers, SiO 2 and TiO 2 , Antioxidant 1010 and add it into a high-speed mixer and stir to mix evenly;

[0068] (2) The above-mentioned mixture is lowered into a twin-screw extruder through a feeding device, melted an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of a lampshade, in particular to an LED lampshade and a processing process thereof. The LED lampshade comprises the following materials in parts by weight:80 to 125 parts of polycarbonate, 12 to 20 parts of PMMA resin, 0.5 to 3 parts of MBS, 3 to 7 parts of reinforced fiber, 5 to 10 parts of mixture and 0.3 to 2 parts of other functional aid, wherein the mixture is obtained by compounding SiO2 and TiO2 according to the weight ratio of 1:(1-2.5). The processing process comprises the following steps: spraying the inner surface of the LED lampshade byusing a hydrofluoric acid solution with the concentration of 40 to 60 percent after the LED lampshade is formed, standing for 3 to 5 minutes, washing with deionized water and drying to obtain an LEDlampshade finished product. According to the LED lampshade provided by the invention and through overall consideration on the composition formula of the lampshade and the final structure of the product, the LED lamp which is convenient to process and has high diffusion property is obtained, has excellent dodging effect and avoids undesirable phenomena of facula, halo and the like on the basis of guaranteeing high light-transmitting performance.

Description

technical field [0001] The invention relates to the technical field of lampshades, in particular to an LED lampshade and a processing technology thereof. Background technique [0002] LED lampshade is a kind of LED accessories. Its function is to better gather light, make the light more concentrated and softer, and avoid direct glare of LED light. In addition to high flame retardancy and high impact strength, LED lampshades also need high light transmission and high diffusion performance, so as to improve the utilization rate of light energy. [0003] In the prior art, in order to improve the atomization effect of the LED lampshade and increase the light transmittance, technicians have proposed many solutions, such as the application number "201010139330.0" and the patent name "A lampshade coating and its preparation method" The Chinese invention patent, which uses a lampshade coating, which can have a good atomization effect on the light after being coated on the inner sur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08J7/14C08L69/00C08L33/12C08L51/04C08K13/04C08K3/36C08K3/22C08K7/08C08K7/10F21V3/06F21Y115/10
CPCC08J7/14C08J2369/00C08J2433/12C08J2451/04C08K3/36C08K7/08C08K7/10C08K13/04C08K2003/2241C08K2201/003C08K2201/004F21Y2115/10
Inventor 曹结宾
Owner 曹结宾
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap