A method for forming a cone at one time

A kind of cone, the same technology, applied in the field of one-time forming of the cone, can solve the problems of increasing the purchase cost of the construction unit, limited specifications and sizes, and many types of work, etc., to achieve high industrial application value, convenient construction, and improve efficiency.

Active Publication Date: 2020-09-01
CHINA NAT CHEM ENG THIRD CONSTR
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

During on-site production, it is usually selected to cut the material in sections, and then use the roller bed to roll in sections, and then combine the tapered surfaces rolled in sections. This method has a long production cycle and is limited by the size and layout of the incoming plates. The loss is large, and the prefabricated cone site of the roller bed is required, and there are many types of work involved, and the mechanical cost is large, which increases the purchase cost of the construction unit.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for forming a cone at one time
  • A method for forming a cone at one time
  • A method for forming a cone at one time

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] The cone made in this embodiment is the bottom cover of the slag bin. The diameter of the small opening section of the bottom cover is 400mm, the diameter of the large opening section is 6000mm, and the height is 4820mm. The material of the fan ring plate is carbon steel Q235-B, and the thickness of the fan ring plate is 8mm.

[0030] figure 1 It is a structural schematic diagram of the fan ring plate 1 in this embodiment. figure 2 It is a schematic diagram of lifting the small mouth section of fan ring plate 1 in this embodiment.

[0031] The cone molding method of the present embodiment comprises the following steps:

[0032] a. The steel plate is blanked at one time and tailor-welded into the fan ring plate 1 required for cone forming;

[0033] b. The fixed bucket 5 that is equal to the small mouth section of the cone is installed at the small mouth section of fan ring plate 1;

[0034] c. 3 rib plates 2 are installed on the fan ring plate 1, and the 3 rib pla...

Embodiment 2

[0039] The cone made in this embodiment is the top cover of the slag bin. The diameter of the small opening section of the top cover is 500mm, the diameter of the large opening section is 5980mm, and the height is 240mm. The material of the fan ring plate is Q235-B, and the thickness of the fan ring plate is 3mm.

[0040] The cone molding method of the present embodiment comprises the following steps:

[0041] a. The steel plate is blanked at one time and tailor-welded into the fan ring plate 1 required for cone forming;

[0042] b. The fixed bucket 5 that is equal to the small mouth section of the cone is installed at the small mouth section of fan ring plate 1;

[0043] c. 3 rib plates 2 are installed on the fan ring plate 1, and the 3 rib plates 2 are welded on the busbar of the fan ring plate 1 and evenly distributed on the fan ring plate 1, and the 3 rib plates 2 connect the fan ring The area of ​​the plate 1 is divided into four equal parts; four lifting lugs 3 are i...

Embodiment 3

[0048] image 3 It is a structural schematic diagram of the fan ring plate in this embodiment. The cone that present embodiment makes is ash bin bottom cover, and the small mouth section diameter of bottom cover is 600mm, and big mouth section diameter is 10100mm, and height 6700mm, and fan ring plate material is stainless steel, and fan ring plate thickness is 18mm.

[0049] The cone molding method of the present embodiment comprises the following steps:

[0050] a. The steel plate is blanked at one time and tailor-welded into the fan ring plate 1 required for cone forming;

[0051] b. The fixed bucket 5 that is equal to the small mouth section of the cone is installed at the small mouth section of fan ring plate 1;

[0052]c. 5 rib plates 2 are installed on the fan ring plate 1, and the 5 rib plates 2 are welded on the busbar of the fan ring plate 1 and evenly distributed on the fan ring plate 1, and the 5 rib plates 2 connect the fan ring The area of ​​the plate 1 is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a cone once-forming method. The method includes the following steps of blanking a steel plate at a time, conducting tailor-welding to form a sector plate required for cone forming, installing a fixing barrel with the diameter the same as the diameter of a small-opening section of a cone at a small-opening section of the sector plate, installing lifting lugs on the sector plate, installing welded junction assembling clamps on the straight sides of the sector plate, starting a hoister to lift the small-opening section of the sector plate, descending the sector plate, conducting the lifting and descending operations 2-3 times, then conducting lifting and assembling the two straight sides of the sector plate through the clamps, and conducting welding to complete cone forming. By means of the method, blanking is conducted at a time, the stress is eliminated in the hoister lifting process by means of the gravity of the sector, no special rolling device is needed, the cone forming efficiency is improved, the large-diameter cone forming difficulty is reduced, and the method has high industrial application value.

Description

technical field [0001] The invention belongs to the field of chemical equipment manufacturing, in particular to a method for one-time forming of a cone. Background technique [0002] Cone parts are widely used in chemical equipment, for example, they can be used as the bottom or top cover of reactors, separators, ash bins, etc. In addition, the cone part can also be used as a variable diameter section of the equipment. For example, the upper and lower parts of some reaction towers have different diameters. At this time, the cone parts can be used to connect the two towers with different diameters. [0003] At present, cones with a diameter greater than 3.5 meters in general design drawings are basically supplied in sections or produced on site due to transportation road reasons and traffic control in various places. When supplying in stages, there will be handover work between the manufacturer and the installation and construction unit, resulting in additional expenses. Du...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K31/00
CPCB23K31/00
Inventor 陈春海
Owner CHINA NAT CHEM ENG THIRD CONSTR