Durable epoxy resin caulking material and preparation method thereof

A technology of epoxy resin and caulking material, applied in the direction of epoxy resin glue, novolac epoxy resin adhesive, adhesive type, etc. Good sealing effect

Active Publication Date: 2021-02-12
广东铁科灌浆科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the above traditional caulking materials generally have the problem of poor durability, therefore, it is very necessary to develop a durable caulking material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Durable epoxy resin caulking material and preparation method thereof
  • Durable epoxy resin caulking material and preparation method thereof
  • Durable epoxy resin caulking material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] This embodiment provides a durable epoxy resin caulking material and its preparation method:

[0044] The raw material formula of this durable type epoxy resin caulking material is shown in Table 1;

[0045] The preparation method of the durable epoxy resin caulking material comprises the following steps:

[0046] Take 100g of bisphenol A epoxy resin E51, 10g of phenol novolac epoxy resin, 5g of hydrogenated bisphenol A epoxy resin, 50g of polyurethane modified epoxy resin, and 20g of butyl glycidyl ether. After mixing evenly, add thixotropic 2g anti-aging agent, 2g anti-oxidant, 2g ultraviolet absorber, 100g micro-silica powder, and mix well to obtain component A;

[0047] Take 25g of diethylenetriamine, 10g of polyamide curing agent, 2g of coupling agent, and 2g of 2-methylimidazole, and mix them uniformly to obtain component B.

[0048] Mix components A and B according to the ratio of parts by mass of 3:1 and then use it for caulking.

Embodiment 2

[0050] This embodiment provides a durable epoxy resin caulking material and its preparation method:

[0051] The raw material formula of this durable type epoxy resin caulking material is shown in Table 1;

[0052] The preparation method of the durable epoxy resin caulking material comprises the following steps:

[0053] Take bisphenol A epoxy resin E51 100g, o-cresol novolac epoxy resin 10g, hydrogenated bisphenol A epoxy resin 5g, polyurethane modified epoxy resin 50g, butyl glycidyl ether 20g, mix well and then add Thixotropic agent 2g, anti-aging agent 2g, antioxidant 2g, ultraviolet absorber 2g, silicon micropowder 100g, mix well to obtain component A;

[0054] Take 30g of triethylenetetramine, 15g of polyamide curing agent, 2g of coupling agent, and 2g of 2-methylimidazole, and mix them uniformly to obtain component B.

[0055] Mix components A and B according to the ratio of parts by mass of 3:1 and then use it for caulking.

Embodiment 3

[0057] This embodiment provides a durable epoxy resin caulking material and its preparation method:

[0058] The raw material formula of this durable type epoxy resin caulking material is shown in Table 1;

[0059] The preparation method of the durable epoxy resin caulking material comprises the following steps:

[0060] Get 100g of bisphenol A epoxy resin E51, 10g of phenol novolac epoxy resin, 5g of hydrogenated bisphenol A epoxy resin, 50g of polyurethane modified epoxy resin, and 20g of butyl glycidyl ether, mix well, then add touch 2g of variable agent, 2g of anti-aging agent, 2g of antioxidant, 2g of ultraviolet absorber, and mix evenly to obtain component A;

[0061] Take 25g of diethylenetriamine, 10g of polyamide curing agent, 2g of coupling agent, and 2g of 2-methylimidazole, and mix them uniformly to obtain component B.

[0062] Mix components A and B evenly in a ratio of 2:1 in parts by mass and it can be used for caulking.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a durable epoxy resin joint filling material and a preparation method thereof. The durable epoxy resin joint filling material comprises a component A and a component B, whereinthe component A is mainly prepared from the following raw materials: 50-100 parts of a bisphenol A epoxy resin, 10-20 parts of a phenolic epoxy resin, 5-10 parts of a hydrogenated bisphenol A epoxy resin, 50-100 parts of a flexible epoxy resin, 5-50 parts of an active diluent, 0-100 parts of an inorganic filler, 0-10 parts of a thixotropic agent, 1-3 parts of an anti-aging agent, 1-3 parts of an antioxidant and 1-3 parts of an ultraviolet absorbent; the component B is mainly prepared from the following raw materials: 10-265 parts of a modified amino curing agent, 0-3 parts of a curing agent and 0-3 parts of a curing accelerator. The component A can be mixed with the component B with the modified amino curing agent to form a solid with particularly good durability, a building joint filled with the solid is good in sealing property, and leakage caused by cracking, deformation and the like of the solid can be avoided.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a durable epoxy resin caulking material and a preparation method thereof. Background technique [0002] The rapid development of high-speed railways in recent years has become China's business card and one of the representatives of China's rapid technological development. Since the implementation of the "Medium and Long-term Railway Network Planning" in 2004, my country's high-speed railway development has achieved remarkable results, playing an important role in promoting economic and social development, ensuring and improving people's livelihood, supporting the implementation of major national strategies, and enhancing my country's comprehensive strength and international influence. Based on "four vertical and four horizontal", form a high-speed railway network with "eight vertical and eight horizontal" main passages as the skeleton, regional connection lines, and int...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J163/00C09J163/04C09J11/04C09J11/06
CPCC08K2201/014C08L2201/08C08L2205/02C08L2205/025C08L2205/035C09J11/04C09J11/06C09J163/00C08L63/04C08K13/02C08K3/36C08K5/3475C08K5/13C08K5/132C08K13/06C08K9/04C08K3/346C08K5/5419C08K5/37C08K13/04C08K3/34C08K5/5435
Inventor 郑祥安王虹贝学鑫
Owner 广东铁科灌浆科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com