High damping Ca and Mg containing aluminum alloy for pressure casting and processing technology thereof

An aluminum alloy and high damping technology, applied in the field of alloys, can solve the problems of damaging the plant, equipment and ecological environment, poisonous gas polluting the environment, reducing service life, etc., and achieves excellent filling performance, excellent flame retardancy, and shrinkage cavity formation Tendency to small effect

Inactive Publication Date: 2018-08-10
GUANGZHOU YUZHI TECH CO LTD
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the use of both methods is limited by the inevitable drawbacks
For example, it is easy to produce toxic gas to pollute the environment and cause flux inclusions to damage the performance of the alloy.
Moreover, flux inclusions are likely to become a source of corrosion during product use, accelerating material corrosion and reducing service life
In addition, the chlorine salt and fluorine salt in the flux are easy to volatilize at high temperature and produce some strong corrosive gases, which will damage the plant, equipment and ecological environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A high-damping Ca and Mg-containing aluminum alloy for die-casting smelted at 750 degrees. In terms of weight percentage, the chemical composition of the alloy is: Ca: 1.2wt.%, Mg: 3.5wt.%; Sn: 4.2wt.%, Y: 0.9wt.%, Mo: 0.5wt.%, Be: 0.3wt .%, the balance is aluminum. The preparation method of the alloy: add the above-mentioned raw materials into the atmosphere-protected induction furnace, and use a silicon carbide crucible; induction heat to 750 degrees to form an alloy solution, and use the electromagnetic stirring effect to fully stir for about 10 minutes; put the alloy liquid in After standing at 750°C for 10 minutes, it is cast into the equipment at the same level as the hot top for semi-continuous casting into the required square and round ingots. The ingot moves down at a speed of 8m / min. The ingot can be used as casting raw material for pressure casting in the subsequent process to prepare aluminum-calcium alloy castings with complex shapes; the final heat treatm...

Embodiment 2

[0019] A high-damping Ca and Mg-containing aluminum alloy for die-casting smelted at 770 degrees. In terms of weight percentage, the chemical composition of the alloy is: Ca: 0.9wt.%, Mg: 6.4wt.%; Sn: 4.5wt.%, Y: 0.9wt.%, Mo: 0.5wt.%, Be: 0.3wt .%, the balance is aluminum. The preparation method of the alloy: add the above-mentioned raw materials into the atmosphere-protected induction furnace, and use a silicon carbide crucible; induction heat to 770 degrees to form an alloy solution, and use the electromagnetic stirring effect to fully stir for about 10 minutes; put the alloy liquid in After standing at 770°C for 10 minutes, it is cast into the equipment at the same level as the hot top for semi-continuous casting into the required square and round ingots. The ingot moves down at a speed of 8m / min. The ingot can be used as casting raw material for pressure casting in the subsequent process to prepare aluminum-calcium alloy castings with complex shapes; the final heat treatm...

Embodiment 3

[0022] A high-damping Ca and Mg-containing aluminum alloy for die-casting smelted at 790 degrees. In terms of weight percentage, the chemical composition of the alloy is: Ca: 1.0wt.%, Mg: 4.3wt.%; Sn: 3.8wt.%, Y: 0.9wt.%, Mo: 0.5wt.%, Be: 0.3wt.% .%, the balance is aluminum. The preparation method of the alloy: add the above-mentioned raw materials into the atmosphere-protected induction furnace, and use a silicon carbide crucible; induction heat to 790 degrees to form an alloy solution, and use the electromagnetic stirring effect to fully stir for about 10 minutes; put the alloy liquid in After standing at 790°C for 10 minutes, it is cast into the equipment at the same level as the hot top for semi-continuous casting into the required square and round ingots. The ingot moves down at a speed of 8m / min. The ingot can be used as casting raw material for pressure casting in the subsequent process to prepare aluminum-calcium alloy castings with complex shapes; the final heat trea...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses high damping Ca and Mg containing aluminum alloy for pressure casting and a processing technology thereof. The alloy is prepared from the following components in percentage byweight: 0.8-1.5wt% of Ca, 2.0-8.0wt% of Mg, 3.0-5.0wt% of Sn, 0.5-1.2wt% of Y, 0.4-0.6wt% of Mo, 0.2-0.5wt% of Be and the balance of aluminum. The aluminum-calcium alloy has excellent pressure castingperform and excellent damping perform and is expected to have positive significance of development and promotion of an aluminum alloy pressure casting technology and even the whole pressure casting industry and a technology thereof.

Description

technical field [0001] The invention relates to the technical field of alloys, in particular to an aluminum-calcium alloy. Background technique [0002] Aluminum alloy is a cheap, energy-saving and high-quality new material that has been widely used at home and abroad in recent decades. It has the advantages of high tensile strength and hardness, good damping, good wear resistance, small friction coefficient, low friction temperature rise, and low material and manufacturing costs. At the same time, it also has good process performance, not only can be used for die casting, but also suitable for sand mold, metal mold, graphite mold, continuous casting, etc. Casting aluminum alloy is to fill the casting mold with molten metal to obtain the aluminum alloy of parts of various shapes. Cast aluminum alloy has good casting performance and can be made into parts with complex shapes; it does not require huge additional equipment; it has the advantages of saving metal, reducing cost...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/00C22C21/06C22C1/02C22F1/04C22F1/047C22F1/02
CPCC22C21/003C22C1/026C22C21/06C22F1/02C22F1/04C22F1/047
Inventor 杨长江
Owner GUANGZHOU YUZHI TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap