Medical hemostasis antibacterial dressing and preparation method thereof
A hemostatic antibacterial and raw material technology, applied in medical science, absorbent pads, bandages, etc., can solve the problems of not being able to keep the wound moist, delay wound healing, and damage granulation tissue, so as to speed up skin healing, promote healing and repair, and promote The effect of tissue repair
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0025] A medical hemostatic antibacterial dressing is prepared from the following raw materials in parts by weight: 70 parts of polyglutamic acid-pullulan polysaccharide crosslinked polymer, 30 parts of collagen, 15 parts of bamboo vinegar powder, 15 parts of glycolic acid, 8 parts of garlic polysaccharide, 10 parts of hyaluronic acid, 55 parts of purified water.
[0026] As mentioned above, the polyglutamic acid-pullulan polysaccharide cross-linked polymer is prepared by the following method: adding the pullulan polysaccharide solution to the polyglutamic acid solution, stirring and reacting at 35°C for 1.2h, without Precipitate the mixed solution with water and ethanol, collect the precipitate by vacuum filtration, dissolve the precipitate with deionized water, place it in a dialysis bag for dialysis for 1 hour, and freeze-dry the dialysis retentate to obtain a polyglutamic acid-pullulan cross-linked polymer.
[0027] Said, the mass ratio of polyglutamic acid solution and pu...
Embodiment 2
[0037] A medical hemostatic and antibacterial dressing is prepared from the following raw materials in parts by weight: 60 parts of polyglutamic acid-pullulan polysaccharide crosslinked polymer, 35 parts of collagen, 13 parts of bamboo vinegar powder, 18 parts of glycolic acid, 6 parts of garlic polysaccharide, 15 parts of hyaluronic acid, 50 parts of purified water.
[0038] As mentioned above, the polyglutamic acid-pullulan polysaccharide cross-linked polymer is prepared by the following method: adding the pullulan polysaccharide solution to the polyglutamic acid solution, stirring and reacting at 40°C for 1.1h, without Precipitate the mixed solution with water and ethanol, collect the precipitate by vacuum filtration, dissolve the precipitate with deionized water, place it in a dialysis bag for dialysis for 1.5 hours, and freeze-dry the dialysis retentate to obtain polyglutamic acid-pullulan cross-linked polymer .
[0039] Said, the mass ratio of polyglutamic acid solution...
Embodiment 3
[0049] A medical hemostatic and antibacterial dressing is prepared from the following raw materials in parts by weight: 80 parts of polyglutamic acid-pullulan polysaccharide crosslinked polymer, 25 parts of collagen, 17 parts of bamboo vinegar powder, 12 parts of glycolic acid, 10 parts of garlic polysaccharide, 5 parts of hyaluronic acid, 60 parts of purified water.
[0050] As mentioned above, the polyglutamic acid-pullulan polysaccharide cross-linked polymer is prepared by the following method: adding the pullulan polysaccharide solution to the polyglutamic acid solution, stirring and reacting at 30°C for 1.4h, without Precipitate the mixed solution with water and ethanol, collect the precipitate by vacuum filtration, dissolve the precipitate with deionized water, place it in a dialysis bag for dialysis for 0.5h, and freeze-dry the dialysis retentate to obtain polyglutamic acid-pullulan cross-linked polymer .
[0051] Said, the mass ratio of polyglutamic acid solution and ...
PUM
Property | Measurement | Unit |
---|---|---|
Concentration | aaaaa | aaaaa |
Concentration | aaaaa | aaaaa |
Average molecular weight | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com